退火对Fe-Cr-Al-Mn双相不锈钢组织及性能的影响

doi:10.13251/j.issn.0254-6051.2021.06.007

金属热处理 ›› 2021, Vol. 46 ›› Issue (6): 31-35.DOI: 10.13251/j.issn.0254-6051.2021.06.007

退火对Fe-Cr-Al-Mn双相不锈钢组织及性能的影响

陈鹏, 张晓明, 潘明明

东北大学材料科学与工程学院轧制技术及连轧自动化国家重点实验室, 辽宁沈阳 110819

收稿日期:2021-01-16 出版日期:2021-06-25 发布日期:2021-07-21
通讯作者: 张晓明,教授,博士,E-mail:zhangxm@ral.neu.edu.cn
作者简介:陈鹏(1994—),男,硕士研究生,主要研究方向为双相不锈钢,E-mail:1500329072@qq.com。
基金资助:
国家重点研发计划(2017YFB0305004)

Effect of annealing on microstructure and properties of a Fe-Cr-Al-Mn duplex stainless steel

Chen Peng, Zhang Xiaoming, Pan Mingming

State Key Laboratory of Rolling and Automation, School of Materials Science and Engineering, Northeastern University, Shenyang Liaoning 110819, China

Received:2021-01-16 Online:2021-06-25 Published:2021-07-21

摘要/Abstract

摘要： 设计制备了一种新型的Fe-Cr-Al-Mn资源节约型双相不锈钢,对其进行高温单相铁素体热轧,研究冷轧后不同退火工艺对其显微组织、力学性能和耐腐蚀性的影响。结果表明,Fe-Cr-Al-Mn钢冷轧后,粗大α相晶粒破碎细化,退火后奥氏体在铁素体晶界形核长大,随退火时间的增加,奥氏体体积分数逐渐增加。随退火温度升高,奥氏体含量减少,伸长率和耐点蚀性能均表现出先增强再减弱的趋势。经800 ℃×4 h退火后,表现出均匀的铁素体和奥氏体相比例和晶粒尺寸,试验钢的强度、伸长率和抗点蚀性能综合性能良好。

关键词: Fe-Cr-Al-Mn双相不锈钢, 退火, 组织, 力学性能, 耐腐蚀性

Abstract: A new type of resource-saving duplex stainless steel Fe-Cr-Al-Mn was designed, prepared, and hot rolled in the high temperature single-phase ferrite (α) region. The effects of different annealing processes on the microstructure, mechanical properties and corrosion resistance after cold-rolling were further studied. The results show that the coarse α-phase grains are broken and refined after the cold rolling. During the annealing process, austenite nucleates and grows at the ferrite grain boundaries. As the annealing time increases, the volume fraction of austenite gradually increases. With the increases of annealing temperature, the volume fraction of austenite decreases, both the elongation and the pitting corrosion resistance show a tendency to increase first and then decrease. After 800 ℃×4 h annealing, the phase ratio and grain size of ferrite and austenite are uniform, which results in excellent combination of strength, elongation and pitting resistance.

Key words: Fe-Cr-Al-Mn duplex stainless steel, annealing, microstructure, mechanical properties, corrosion resistance

中图分类号:

陈鹏, 张晓明, 潘明明. 退火对Fe-Cr-Al-Mn双相不锈钢组织及性能的影响[J]. 金属热处理, 2021, 46(6): 31-35.

Chen Peng, Zhang Xiaoming, Pan Mingming. Effect of annealing on microstructure and properties of a Fe-Cr-Al-Mn duplex stainless steel[J]. Heat Treatment of Metals, 2021, 46(6): 31-35.

参考文献

[1]邢珊珊, 戚浩宇, 郑传波. 固溶处理对2205双相不锈钢组织及钝化膜特性的影响[J]. 金属热处理, 2020, 45(3): 146-150.
Xing Shanshan, Qi Haoyu, Zheng Chuanbo. Effect of solution treatment on microstructure and passivation film properties of 2205 duplex stainless steel[J]. Heat Treatment of Metals, 2020, 45(3): 146-150.
[2]Lo K H, Shek C H, Lai J K L. Recent developments in stainless steels[J]. Materials Science and Engineering R Reports, 2009, 65(4-6): 39-104.
[3]曹静, 安立聪, 杨弋涛. 铸造双相不锈钢时效过程组织演变[J]. 金属热处理, 2016, 41(12): 1-4.
Cao Jing, An Licong, Yang Getao. Microstructure evolution of cast duplex stainless steel during aging[J]. Heat Treatment of Metals, 2016, 41(12): 1-4.
[4]Rys J, Cempura G. Microstructure and deformation behavior of metastable duplex stainless steel at high rolling reductions[J]. Materials Science and Engineering, 2017, 700(17): 656-666.
[5]Yang Y H, Yan B, Wang J, et al. The influence of solution treatment temperature on microstructure and corrosion behavior of high temperature ageing in 25% Cr duplex stainless steel[J]. Journal of Alloys and Compounds, 2011, 509(36): 8870-8879.
[6]Ran Q X, Wang M L, Wu Z Y, et al. Economical Si-bearing, nearly Ni-free 19Cr TRIP-aided duplex stainless steels with better high-temperature oxidation resistance[J]. Journal of Materials Engineering and Performance, 2019, 29(1): 529-540.
[7]Herrera C, Ponge D, Raabe D. Design of a novel Mn-based 1 GPa duplex stainless TRIP steel with 60% ductility by a reduction of austenite stability[J]. Acta Materialia, 2011, 59(11): 4653-4664.
[8]Jiang D W, Ge C S, Zhao X J, et al. 22Cr high-Mn-N low-Ni economical duplex stainless steels[J]. Journal of Iron and Steel Research International, 2012, 19(2): 50-56.
[9]Fang Y L, Liu Z Y, Song H M, et al. Hot deformation behavior of a new austenite-ferrite duplex stainless steel containing high content of nitrogen[J]. Materials Science and Engineering A, 2009, 526(1/2): 128-133.
[10]Wan J Q, Ran Q X, Li J, et al. A new resource-saving, low chromium and low nickel duplex stainless steel 15Cr-xAl-2Ni-yMn[J]. Materials and Design, 2014, 53: 43-50.
[11]Sohn S S, Choi K, Kwak J H, et al. Novel ferrite-austenite duplex lightweight steel with 77% ductility by transformation induced plasticity and twinning induced plasticity mechanisms[J]. Acta Materialia, 2014, 78: 181-189.
[12]Zhao Yan, Zhang Weina, Liu Xin, et al. Development of TRIP-aided lean duplex stainless steel by twin-roll strip casting and its deformation mechanism[J]. Metallurgical and Materials Transactions A, 2016, 47(12): 6292-6303.
[13]Pan M M, Zhang X M, Chen P, et al. The effect of chemical composition and annealing condition on the microstructure and tensile properties of a resource-saving duplex stainless steel[J]. Materials Science and Engineering A, 2020, 788: 139540.
[14]Pan M M, Zhang X M, Chen Y, et al. Effect of cold rolling and annealing on microstructure and properties of a new resource-saving duplex stainless steel Fe-19Cr-0. 6Al-12Mn[J]. Journal of Iron and Steel Research International, 2020, 27(12): 1420-1432.
[15]Simmons J W. Overview: High-nitrogen alloying of stainless steels[J]. Materials Science and Engineering A, 1996, 207(2): 159-169.

退火对Fe-Cr-Al-Mn双相不锈钢组织及性能的影响

Effect of annealing on microstructure and properties of a Fe-Cr-Al-Mn duplex stainless steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[2]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[3]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[4]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[5]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[6]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[7]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[8]	贾昌远, 霍元明, 何涛, 霍存龙, 刘克然. 40CrNiMo钢高温拉伸变形行为和组织演变规律[J]. 金属热处理, 2022, 47(4): 69-74.
[9]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[10]	刘丽艳, 毕文珍, 韦习成. Mn元素对热冲压钢镀锌层组织演变的影响[J]. 金属热处理, 2022, 47(4): 93-99.
[11]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[12]	付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.
[13]	宿鹏吉, 麻永林, 董丽丽, 杨雪峰. 磁场预退火处理对CGO钢组织与织构的影响[J]. 金属热处理, 2022, 47(4): 128-132.
[14]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[15]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.