热处理工艺对5Cr钢力学性能和耐蚀性能的影响

doi:10.13251/j.issn.0254-6051.2021.11.032

金属热处理 ›› 2021, Vol. 46 ›› Issue (11): 186-190.DOI: 10.13251/j.issn.0254-6051.2021.11.032

热处理工艺对5Cr钢力学性能和耐蚀性能的影响

刘勇¹, 张志慧², 高燕¹, 赵晋斌¹, 武会宾²

1.南京钢铁股份有限公司科技质量部, 江苏南京 210044;
2.北京科技大学钢铁共性技术协同创新中心, 北京 100083

收稿日期:2021-05-03 出版日期:2021-11-25 发布日期:2021-12-08
作者简介:刘勇(1970—),男,高级工程师,主要研究方向为钢铁产品相关技术、质量、检测等,E-mail:liuyong1@njsteel.com.cn
基金资助:
国家重点研发计划(2017YFB0304900)

Effect of heat treatment process on mechanical properties and corrosion resistance of 5Cr steel

Liu Yong¹, Zhang Zhihui², Gao Yan¹, Zhao Jinbin¹, Wu Huibin²

1. Science and Technology Quality Department of Nanjing Iron and Steel Co., Ltd., Nanjing Jiangsu 210044, China;
2. Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China

Received:2021-05-03 Online:2021-11-25 Published:2021-12-08

摘要/Abstract

摘要： 利用光学显微镜、拉伸及冲击试验机等仪器研究了不同热处理工艺对5Cr钢组织和力学性能的影响,利用高温高压反应釜模拟腐蚀过程,并结合电化学测试对比分析了热轧态和调质态钢的耐腐蚀性能。结果表明:5Cr钢经淬火+回火处理后,组织中碳化物弥散析出,具有较高的强度和良好的塑、韧性。热轧态钢的腐蚀速率为0.188 mm/a,调质态钢为0.158 mm/a。调质态钢中作为阴极的碳化物(Fe₃C)少且均匀弥散分布,组织自腐蚀电位较高,腐蚀电流密度较低,电偶腐蚀程度较浅,耐腐蚀性能较好。

关键词: 5Cr钢, 热处理, 耐腐蚀性, 碳化物, 力学性能

Abstract: Effect of heat treatment process on microstructure and mechanical properties of the 5Cr steel was studied by using optical microscopes, tensile and impact testing machines and other instruments. The corrosion process of 5Cr steel was simulated and the resistance of hot rolled and quenched + tempered steels was compared and analyzed by using high temperature and high pressure reactors and combing with electrochemical tests. The results show that after quenching and tempering treatment, the 5Cr steel has carbides dispersed and precipitated in the structure and has high strength and good plasticity and toughness. The corrosion rate of hot rolled steel is 0.188 mm/a, and that of quenched + tempered steel is 0.158 mm/a. In the quenched + tempered steel, the carbide (Fe₃C) as the cathode is less and uniformly dispersed, the self-corrosion potential is higher and the corrosion current density is lower of the structure, the degree of galvanic corrosion is shallow, and the corrosion resistance is better.

Key words: 5Cr steel, heat treatment, corrosion resistance, carbide, mechanical properties

中图分类号:

TG172.82

刘勇, 张志慧, 高燕, 赵晋斌, 武会宾. 热处理工艺对5Cr钢力学性能和耐蚀性能的影响[J]. 金属热处理, 2021, 46(11): 186-190.

Liu Yong, Zhang Zhihui, Gao Yan, Zhao Jinbin, Wu Huibin. Effect of heat treatment process on mechanical properties and corrosion resistance of 5Cr steel[J]. Heat Treatment of Metals, 2021, 46(11): 186-190.

参考文献

[1]路民旭, 白真权, 赵新伟, 等. 油气采集储运中的腐蚀现状及典型案例[J]. 腐蚀与防护, 2002(3): 105-113.
Lu Minxu, Bai Zhenquan, Zhao Xinwei, et al. Corrosion status and typical cases in oil and gas collection, storage and transportation[J]. Corrosion and Protection, 2002(3): 105-113.
[2]孙建波, 柳伟, 常炜, 等. 低铬X65管线钢CO₂腐蚀产物膜的特征及形成机制[J]. 金属学报, 2009, 45(1): 84-90.
Sun Jianbo, Liu Wei, Chang Wei, et al. Characteristics and formation mechanism of CO₂ corrosion product film on low chromium X65 pipeline steel[J]. Acta Metallurgica Sinica, 2009, 45(1): 84-90.
[3]郭少强, 许立宁, 常炜, 等. 3Cr管线钢CO₂腐蚀实验研究[J]. 金属学报, 2011, 47(8): 1067-1074.
Guo Shaoqiang, Xu Lining, Chang Wei, et al. Experimental study on CO₂ corrosion of 3Cr pipeline steel[J]. Acta Metallurgica Sinica, 2011, 47(8): 1067-1074.
[4]陈长风, 赵国仙, 路民旭, 等. 含Cr油套管钢CO₂腐蚀产物膜特征[J]. 中国腐蚀与防护学报, 2002, 22(6): 335-338.
Chen Changfeng, Zhao Guoxian, Lu Minxu, et al. Characteristics of CO₂ corrosion scales on Cr-containing N80 steel[J]. Chinese Journal of Corrosion and Protection, 2002, 22(6): 335-338.
[5]Wu T, Wu H B, Niu G, et al. Effect of microstructure on the corrosion performance of 5%Cr steel in a CO₂ environment[J]. Corrosion, 2018, 74(7): 757-767.
[6]杜明, 朱世东, 张骁勇, 等. 含Cr低合金钢的CO₂腐蚀产物膜形成及机理研究进展[J]. 腐蚀科学与防护技术, 2019, 31(3): 335-342.
Du Ming, Zhu Shidong, Zhang Xiaoyong, et al. Research progress on formation and mechanism of CO₂ corrosion product film of Cr-containing low alloy steel[J]. Corrosion Science and Protection Technology, 2019, 31(3): 335-342.
[7]许立宁, 王贝, 路民旭. 6.5%Cr钢在高温高压CO₂环境下的腐蚀行为研究[J]. 金属学报, 2016, 52(6): 672-678.
Xu Lining, Wang Bei, Lu Minxu. Study on corrosion behavior of 6.5%Cr steel in high temperature and high pressure CO₂ environment[J]. Acta Metallurgica Sinica, 2016, 52(6): 672-678.
[8]王芬玲, 刘禹炯, 王天剑, 等. 热处理工艺对12Cr钢组织与性能的影响[J]. 金属热处理, 2020, 45(7): 42-45.
Wang Fenling, Liu Yujiong, Wang Tianjian, et al. The effect of heat treatment process on the structure and properties of 12Cr steel[J]. Heat Treatment of Metals, 2020, 45(7): 42-45.
[9]姜雯, 赵昆渝, 苏杰, 等. 热处理工艺对不同Cr含量超级马氏体不锈钢组织与性能的影响[J]. 金属热处理, 2019, 44(10): 135-140.
Jiang Wen, Zhao Kunyu, Su Jie, et al. The effect of heat treatment process on the microstructure and properties of super martensitic stainless steel with different Cr content[J]. Heat Treatment of Metals, 2019, 44(10): 135-140.
[10]Cleary H J, Greene N D. Electrochemical properties of Fe and steel[J]. Corrosion Science, 1969, 9(1): 3-13.
[11]Paolineli L D, Simison S N, Perez T. The influence of Cr on the efficiency of inhibitor of C-Mn steel CO₂ corrosion[C]//International Cowosion Conferenc Series. Houston: NACE, 2006: 369.
[12]López Damián A, Simison S N, Sánchez S R de. The influence of steel microstructur on CO₂ corrosion. EIIS studies on the inhibition efficiency of benzimidazole[J]. Eletrochimica Acta, 2003, 48(7): 845-854.
[13]Lotz U, Sydberger T. CO₂ corrosion of carbon steel and 13Cr steel in particle-laden fluid[J]. Corrosion, 1988, 44(11): 800-809.

[1]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[2]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[3]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[4]	王英虎, 郑淮北, 刘庭耀, 宋令玺, 白青青. 固溶处理对53Cr21Mn9Ni4N耐热钢组织及碳化物的影响[J]. 金属热处理, 2022, 47(4): 39-45.
[5]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[6]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[7]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[8]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[9]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[10]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[11]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[12]	李梦, 武美萍, 陆佩佩, 赵子硕, 缪小进. 选区激光熔化MnSi₂增强316L不锈钢复合材料的表面质量及耐蚀性能[J]. 金属热处理, 2022, 47(4): 165-170.
[13]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[14]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[15]	王方军, 王东哲, 万红, 时瑶, 沈涛. 热处理和冷变形量对定膨胀合金4J32C线膨胀系数的影响[J]. 金属热处理, 2022, 47(4): 199-203.

热处理工艺对5Cr钢力学性能和耐蚀性能的影响

Effect of heat treatment process on mechanical properties and corrosion resistance of 5Cr steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价