时效处理对7A55铝合金微观组织和性能的影响

doi:10.13251/j.issn.0254-6051.2021.09.020

金属热处理 ›› 2021, Vol. 46 ›› Issue (9): 120-123.DOI: 10.13251/j.issn.0254-6051.2021.09.020

时效处理对7A55铝合金微观组织和性能的影响

丁轩¹, 甘玉荣¹, 蒋爱娟¹, 李辉^1,2, 杨明球³

1.烟台南山学院工学院, 山东烟台 265713;
2.山东南山铝业股份有限公司国家铝合金压力加工工程技术研究中心, 山东烟台 265700;
3.山东南山暖通新材料有限公司技术中心, 山东烟台 265700

收稿日期:2021-03-14 出版日期:2021-09-25 发布日期:2021-12-09
作者简介:丁轩(1985—),男,讲师,硕士,主要研究方向为金属材料的组织性能调控,E-mail:18210297896@163.com
基金资助:
山东省高等学校青创科技计划(2019KJA019)

Influence of aging treatment on microstructure and properties of 7A55 aluminum alloy

Ding Xuan¹, Gan Yurong¹, Jiang Aijuan¹, Li Hui^1,2, Yang Mingqiu³

1. College of Engineering, Yantai Nanshan University, Yantai Shandong 265713, China;
2. National Engineering Research Center for Plastic Working of Aluminum Alloys, Shandong Nanshan Aluminum Co., Ltd., Yantai Shandong 265700, China;
3. Technology Center, Shandong Nanshan Nuantong New Material Co., Ltd., Yantai Shandong 265700, China

Received:2021-03-14 Online:2021-09-25 Published:2021-12-09

摘要/Abstract

摘要： 系统研究了时效处理对7A55铝合金微观组织演变和性能的影响。测试了其显微硬度、力学性能和电化学腐蚀性能,表征了透射组织和腐蚀形貌。试验结果表明:固溶处理后的7A55试验铝合金,具有高的硬化响应速率。经160 ℃×12 h时效处理后,显微硬度达到峰值,由固溶处理后的56 HV0.5提高到87 HV0.5,提高了55.36%,且前期的硬度升高速率极快。预时效(PA)处理抑制了试验7A55铝合金的自然时效(NA)效应,提升了烘烤硬化(BH)响应。经BH处理后,PA+NA态的屈服强度明显提升,达到475 MPa,硬化增量达到190 MPa,提高了66.67%,伸长率降低为12.5%。PA+NA+BH状态下,析出相粒子尺寸更为细小,粒子直径在10~15 nm范围,且分布均匀。PA+NA+BH态的合金腐蚀电位最高,为－1.032 V(vs SCE),腐蚀坑数量最少,平均腐蚀深度约为33 μm,最不易被腐蚀。

关键词: 7A55铝合金, 时效处理, 微观组织, 显微硬度, 电化学腐蚀性能

Abstract: Influence of aging treatment on microstructure evolution and properties of 7A55 aluminum alloy was investigated. The microhardness, mechanical properties and electrochemical corrosion behavior were tested. The TEM microstructure and corrosion morphology were characterized. The results indicate that the experimental 7A55 aluminum alloy after solution treatment has higher hardening rate. After aging at 160 ℃ for 12 h, the hardness reaches the peak (87 HV0.5) from 56 HV0.5 in the solution treated state, i.e., increased by 55.36%, and the hardening rate in early aging stage is very high. Pre-aging (PA) treatment inhibits the natural aging (NA) effect and improves the bake hardening (BH) response. The yield strength under PA+NA state after BH treatment reaches 475 MPa with an increment of 190 MPa, which improves 66.67%, and the elongation reaches 12.5%. The precipitated particles under PA+NA+BH state are finer and uniformly distributed, with the diameter in the range of 10-15 nm. The PA+NA+BH state alloy has the highest corrosion potential (－1.032 V, vs SCE), the least corrosion pits and the best corrosion resistance, with the average corrosion depth being about 33 μm.

Key words: 7A55 aluminum alloy, aging treatment, microstructure, microhardness, electrochemical corrosion property

中图分类号:

TG156

丁轩, 甘玉荣, 蒋爱娟, 李辉, 杨明球. 时效处理对7A55铝合金微观组织和性能的影响[J]. 金属热处理, 2021, 46(9): 120-123.

Ding Xuan, Gan Yurong, Jiang Aijuan, Li Hui, Yang Mingqiu. Influence of aging treatment on microstructure and properties of 7A55 aluminum alloy[J]. Heat Treatment of Metals, 2021, 46(9): 120-123.

参考文献

[1]Miller W S, Zhuang L, Bottema J, et al. Recent development in aluminum alloys for the automotive industry[J]. Materials Science and Engineering A, 2000, 280(1): 37-49.
[2]Hirsch J. Recent development in aluminum for automotive applications[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(7): 1995-2002.
[3]Henriksson F, Johansen K. On material substitution in automotive BIWs-from steel to aluminum body sides[J]. Procedia CIRP, 2016, 50: 683-688.
[4]杨守杰, 戴圣龙. 航空铝合金的发展回顾与展望[J]. 材料导报, 2005(2): 76-80.
Yang Shoujie, Dai Shenglong. A glimpse at the development and application of aluminum alloys in aviation industry[J]. Materials Review, 2005(2): 76-80.
[5]Cao C, Zhang D, Zhuang L Z, et al. Improved age-hardening response and altered precipitation behavior of Al-5.2Mg-0.45Cu-2.0Zn alloy with pre-aging treatment[J]. Journal of Alloys and Compounds, 2017, 691: 40-43.
[6]Yang R X, Liu Z Y, Ying P Y, et al. Multistage-aging process effect on formation of GP zones and mechanical properties in Al-Zn-Mg-Cu alloy[J]. Transactions of Nonferrous Metals Society of China, 2016, 25(5): 1183-1190.
[7]许晓静, 王子路, 陆文俊, 等. 固溶-大变形-时效下7085铝合金的强化机理[J]. 稀有金属材料与工程, 2017(4): 1008-1012.
Xu Xiaojing, Wang Zilu, Lu Wenjun, et al. Strengthening mechanisms of 7085 aluminum alloy by solution-large deformation-aging[J]. Rare Metal Materials and Engineering, 2017(4): 1008-1012.
[8]Chen S Y, Chen K H, Peng G S, et al. Effect of heat treatment on hot deformation behavior and microstructure evolution of 7085 aluminum alloy[J]. Journal of Alloys and Compounds, 2012, 537: 338-345.
[9]Bennett T A, Petrov R H, Kestens L A I. Effect of particles on texture banding in an aluminium alloy[J]. Scripta Materialia, 2010, 62(2): 78-81.
[10]Jiang F L, Zurob H S, Purdy G R, et al. Characterizing precipitate evolution of an Al-Zn-Mg-Cu based commercial alloy during artificial aging and non-isothermal heat treatments by in situ electrical resistivity monitoring[J]. Materials Characterization, 2016, 117: 47-56.

[1]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[2]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[3]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[4]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[5]	胡静, 陶科, 杨庆松, 李刚, 张德汉. 机械抛光后的时效工艺对0Cr25Al5电热合金拉拔性能的影响[J]. 金属热处理, 2022, 47(4): 171-177.
[6]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.
[7]	杨春苗, 王珊, 王淑慧, 李延珍, 刘文文. RRA过程中预时效时间对7A85铝合金组织性能的影响[J]. 金属热处理, 2022, 47(3): 44-47.
[8]	陈善勇, 王快社, 乔柯, 王文. 碱热处理对搅拌摩擦加工AZ31镁合金耐腐蚀性能的影响[J]. 金属热处理, 2022, 47(3): 61-66.
[9]	梅金娜, 姜凤阳, 卫娜, 刘浪浪, 思芳, 刘松涛, 王俊勃, 刘江南. 轧制变形对高熵合金微观组织和力学性能的影响[J]. 金属热处理, 2022, 47(3): 67-71.
[10]	叶拓, 唐明, 刘吉兆, 刘伟, 吴远志, 刘巍, 徐文. 固溶温度对7075铝合金板材组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 119-123.
[11]	周钟平, 张小娟, 白鹭, 余方印, 闵永安. T250钢离子渗氮后的组织和性能[J]. 金属热处理, 2022, 47(3): 210-214.
[12]	叶拓, 何玉兵, 何文鹏, 刘巍, 袁浩登, 吴远志, 刘伟, 刘吉兆. 轧制态6082-T6铝合金的热压缩力学行为及微观组织分析[J]. 金属热处理, 2022, 47(2): 26-30.
[13]	闵旭东, 黄元春, 肖政兵, 刘宇, 任贤魏, 邹倜. 预处理对汽车用Al-Mg-Si合金组织和晶间腐蚀行为的影响[J]. 金属热处理, 2022, 47(2): 78-85.
[14]	刘跃, 韩顺, 厉勇, 王春旭, 严晓红, 李建新. 淬火温度对GE1014超高强度钢组织及性能的影响[J]. 金属热处理, 2022, 47(2): 125-129.
[15]	董瑞, 陈林, 岑耀东, 包喜荣. 不同热处理条件下贝氏体钢的微观组织和疲劳裂纹扩展[J]. 金属热处理, 2022, 47(2): 153-158.

时效处理对7A55铝合金微观组织和性能的影响

Influence of aging treatment on microstructure and properties of 7A55 aluminum alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价