锯片基材75Cr1钢的热处理工艺及其组织性能

doi:10.13251/j.issn.0254-6051.2021.09.035

金属热处理 ›› 2021, Vol. 46 ›› Issue (9): 193-198.DOI: 10.13251/j.issn.0254-6051.2021.09.035

锯片基材75Cr1钢的热处理工艺及其组织性能

董绍明¹, 胡建文^1,2,3, 梁子玉¹

1.河北科技大学材料科学与工程学院, 河北石家庄 050018;
2.河北省材料近净成形技术重点实验室, 河北石家庄 050018;
3.航空轻质复合材料与加工技术河北省工程实验室, 河北石家庄 050018

收稿日期:2021-04-04 出版日期:2021-09-25 发布日期:2021-12-09
通讯作者: 胡建文,教授,博士,E-mail:hujianwen05@163.com
作者简介:董绍明(1994—),男,硕士研究生,主要研究方向为金属材料及热处理,E-mail:mingming059@qq.com。

Heat treatment process of 75Cr1 steel for saw blade substrate and its microstructure and mechanical properties

Dong Shaoming¹, Hu Jianwen^1,2,3, Liang Ziyu¹

1. School of Materials Science and Engineering, Hebei University of Science and Technology, Shijiazhuang Hebei 050018, China;
2. Hebei Key Laboratory of Materials Near-Net Forming Technology, Shijiazhuang Hebei 050018, China;
3. Hebei Engineering Laboratory of Aviation Lightweight Composite Materials and Processing Technology, Shijiazhuang Hebei 050018, China

Received:2021-04-04 Online:2021-09-25 Published:2021-12-09

摘要/Abstract

摘要： 研究了锯片基材75Cr1钢不同热处理工艺下的组织、晶粒度、碳化物分布以及力学性能。结果表明:780~840 ℃之间淬火,组织为细小的针片马氏体+少量残留奥氏体。随淬火温度升高,硬度略有升高,但均在63 HRC水平附近,晶粒度由10级降至8级,晶粒不均匀程度也更加明显;随回火温度升高,组织由回火屈氏体转变为回火索氏体,细小的颗粒状碳化物增多。800 ℃淬火+540 ℃回火,75Cr1钢组织为回火索氏体,细小碳化物弥散分布,硬度36.5 HRC,具有良好的强度和塑韧性匹配。

关键词: 锯片用75Cr1钢, 热处理工艺, 组织, 力学性能, 晶粒度

Abstract: Microstructure, grain sizes, carbide distribution and mechanical properties of the 75Cr1 steel for saw blade substrate under different heat treatment processes were studied. The results show that microstructures are fine acicular martensite and a less amount of residual austenite after quenching between 780 ℃ and 840 ℃, and the hardness increases slightly with the increase of quenching temperature around the level of 63 HRC. The grain size decreases from grade 10 to grade 8, and unevenness of grains is greater with the increase of temperature. With the increase of tempering temperature, the microstructure changes from tempered troostite to tempered sorbite, and the amounts of granular carbides increase. Quenched at 800 ℃ and tempered at 540 ℃, the microstructure of tempered sorbite with a dispersed distribution of fine carbides is obtained. The hardness of the 75Cr1 steel is 36.5 HRC, with good matching of strength and toughness.

Key words: saw blade steel 75Cr1, heat treatment process, microstructure, mechanical properties, grain size

中图分类号:

TG142.1

董绍明, 胡建文, 梁子玉. 锯片基材75Cr1钢的热处理工艺及其组织性能[J]. 金属热处理, 2021, 46(9): 193-198.

Dong Shaoming, Hu Jianwen, Liang Ziyu. Heat treatment process of 75Cr1 steel for saw blade substrate and its microstructure and mechanical properties[J]. Heat Treatment of Metals, 2021, 46(9): 193-198.

参考文献

[1]郭继富. 金属冷切圆锯片在轧钢生产中的应用[J]. 冶金设备, 2005(1): 43-48.
Guo Jifu. Application of metal cold-cutting circular saw blade in steel rolling[J]. Metallurgical Equipment, 2005(1): 43-48.
[2]金欣, 周健. Mo-W-Co系高热强性热锻模具钢的组织与性能[J]. 金属热处理, 2018, 43(2): 8-14.
Jin Xin, Zhou Jian. Microstructure and mechanical properties of Mo-W-Co high hot-strength hot-work die steels[J]. Heat Treatment of Metals, 2018, 43(2): 8-14.
[3]王孟, 宝志坚. 汽车轴类热锻模具的失效形式与分析[J]. 中国工程机械学报, 2008, 6(3): 364-369.
Wang Meng, Bao Zhijian. Deficiency formation and analysis on automotive axle heat-forged mould[J]. Chinese Journal of Mechanical Engineering, 2008, 6(3): 364-369.
[4]Buyuksagis I S. Effect of cutting mode on the sawability of granites using segmented circular diamond sawblade[J]. Journal of Materials Processing Technology, 2007, 183(2-3): 399-406.
[5]苑少强, 郭继富. 回火温度对冶金锯片用钢75Cr1回火组织及性能的影响[J]. 河北冶金, 2009, 38(5): 17-18.
Yuan Shaoqing, Guo Jifu. Influence of tempering temperature on structure and property of 75Crl steel for metallurgical saw shade[J]. Hebei Metallurgy, 2009, 38(5): 17-18.
[6]张新明, 朱永伟. 金刚石锯片在锯切过程中的受力与失效分析[J]. 摩擦学学报, 2001, 21(6): 464-468.
Zhang Xinming, Zhu Yongwei. Force and failure analysis of diamond saw-blade in cutting of granite[J]. Tribology, 2001, 21(6): 464-468.
[7]张文, 朱百智, 黄振建, 等. 淬火介质对 42CrMo 钢棒淬火组织及硬度影响的数值模拟及试验验证[J]. 金属热处理, 2020, 45(1): 56-60.
Zhang Wen, Zhu Baizhi, Huang Zhenjian, et al. Numerical simulation and experimental verification of effect of quenching medium on quenching microstructure and hardness of 42CrMo steel rod[J]. Heat Treatment of Metals, 2020, 45(1): 56-60.
[8]Jerro H D, Pang S S, Yang C, et al. Kinematics analysis of the chipping process using the circular diamond saw blade[J]. Journal of Manufacturing Science & Engineering, 1999, 121(2): 257-264.
[9]宋城, 樊雪琴. 高效耐磨金刚石锯片的研制[J]. 金刚石与磨料磨具工程, 2006(6): 32-35.
Song Cheng, Fan Xueqin. Preparation of high-efficient and wear-resisting diamond saw[J]. Diamond & Abrasives Engineering, 2006(6): 32-35.
[10]何浪. 75Cr1薄板坯高温力学性能研究及配水工艺优化[D]. 长沙: 中南大学, 2013.
He Lang. Study on high temperature thermoplastic property and optimization water-cooling technology of 75Cr1 sheet billet[D]. Changsha: Central South University, 2013.
[11]张阳, 王福明, 唐郑磊, 等. SXQ500/550D 钢奥氏体晶粒长大行为及其影响因素[J]. 金属热处理, 2019, 44(8): 110-118.
Zhang Yang, Wang Fuming, Tang Zhenglei, et al. Austenite grain growth behavior and its influencing factors of SXQ500/550D steel[J]. Heat Treatment of Metals, 2019, 44(8): 110-118.
[12]孙宜强, 甘晓龙, 汪水泽, 等. 金刚石锯片基体用钢75Cr1的连续冷却转变曲线研究[J]. 热加工工艺, 2019, 48(4): 92-95.
Sun Yiqiang, Gan Xiaolong, Wang Shuize, et al. Study on continuous cooling transformation curves of 75Cr1 steel for diamond saw blades matrix[J]. Hot Working Technology, 2019, 48(4): 92-95.
[13]陈明昕, 杨晓江, 冯晓勇. Nb元素添加对75Cr1钢热变形行为的影响[J]. 中国冶金, 2020, 30(6): 71-79.
Chen Mingxin, Yang Xiaojiang, Feng Xiaoyong. Effect of niobium addition on hot deformation behavior of 75Cr1 steel [J]. China Metallurgy, 2020, 30(6): 71-79.
[14]戚正风. 金属热处理原理[M]. 北京: 机械工业出版社, 1987.

[1]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[2]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[3]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[4]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[5]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[6]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[7]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[8]	贾昌远, 霍元明, 何涛, 霍存龙, 刘克然. 40CrNiMo钢高温拉伸变形行为和组织演变规律[J]. 金属热处理, 2022, 47(4): 69-74.
[9]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[10]	刘丽艳, 毕文珍, 韦习成. Mn元素对热冲压钢镀锌层组织演变的影响[J]. 金属热处理, 2022, 47(4): 93-99.
[11]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[12]	付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.
[13]	宿鹏吉, 麻永林, 董丽丽, 杨雪峰. 磁场预退火处理对CGO钢组织与织构的影响[J]. 金属热处理, 2022, 47(4): 128-132.
[14]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[15]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.

锯片基材75Cr1钢的热处理工艺及其组织性能

Heat treatment process of 75Cr1 steel for saw blade substrate and its microstructure and mechanical properties

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价