V-N微合金化CrSiMn系低合金铸钢中的析出行为

doi:10.13251/j.issn.0254-6051.2021.08.003

金属热处理 ›› 2021, Vol. 46 ›› Issue (8): 15-19.DOI: 10.13251/j.issn.0254-6051.2021.08.003

V-N微合金化CrSiMn系低合金铸钢中的析出行为

王晓东^1,2, 陈蕴博¹, 左玲立¹, 游龙², 陈冲², 毛丰², 张峻嘉³

1.机械科学研究总院, 北京 100083;
2.河南科技大学金属材料磨损控制与成型技术国家地方联合工程研究中心, 河南洛阳 471000;
3.东北大学材料科学与工程学院辽宁省轻量化用关键金属结构材料重点实验室, 辽宁沈阳 110819

收稿日期:2021-03-25 出版日期:2021-08-25 发布日期:2021-12-09
通讯作者: 陈蕴博,中国工程院院士,教授,E-mail:webmaster@ht.org.cn
作者简介:王晓东(1979—),男,工程师,硕士,主要研究方向为先进耐磨材料,E-mail:nmxdwang@163.com。

Precipitation behavior in V-N microalloyed CrSiMn low alloy cast steel

Wang Xiaodong^1,2, Chen Yunbo¹, Zuo Lingli¹, You Long², Chen Chong², Mao Feng², Zhang Junjia³

1. China Academy of Machinery Science and Technology Group Co., Ltd., Beijing 100083, China;
2. National Joint Engineering Research Center for Abrasion Control and Molding of Metal Materials, Henan University of Science and Technology, Luoyang Henan 471000, China;
3. Liaoning Key Laboratory of Lightweight Metal Structural Materials, School of Materials Science and Engineering, Northeastern University, Shenyang Liaoning 110819, China

Received:2021-03-25 Online:2021-08-25 Published:2021-12-09

摘要/Abstract

摘要： 利用JMatPro热力学模拟软件对V-N微合金化CrSiMn系低合金铸钢进行了计算,得到了不同V含量铸钢的平衡相组成,着重研究了平衡状态下各析出相的析出行为。结果表明,在加热过程中,V含量的增加将增大铁素体向奥氏体的转变阻力;V含量对微合金化渗碳体及M₇C₃型碳化物的析出行为影响不大;V含量对氮化物及碳氮化物的析出有较大影响,当V含量由0增加至0.18%(质量分数)时,氮化物及碳氮化物的初始析出温度由734.2 ℃提升至1133.93 ℃,最大析出量(质量分数)由0.07%提升至0.24%。

关键词: 微合金化, JMatPro, 铸钢, 析出行为

Abstract: V-N microalloyed CrSiMn low alloy cast steel was calculated by means of JMatPro software, the equilibrium phase composition of the cast steel with different V contents was obtained. The precipitation behavior of each precipitated phases in the microalloyed steel at equilibrium state was emphatically studied. The results show that during the heating process, the increase of V content promotes the phase transformation resistance of ferritic to austenite. The V content has little influence on precipitation behavior of cementite and M₇C₃. The content of V has a great influence on precipitation of nitrides and carbonides. When V content increases from 0 to 0.18% (mass fraction), the initial precipitation temperature of nitrides and carbonides increases from 734.2 ℃ to 1133.93 ℃, and the mass fraction of the maximum precipitation amount increases from 0.07% to 0.24%.

Key words: microalloying, JMatPro, cast steel, precipitation behavior

中图分类号:

TG142.1

王晓东, 陈蕴博, 左玲立, 游龙, 陈冲, 毛丰, 张峻嘉. V-N微合金化CrSiMn系低合金铸钢中的析出行为[J]. 金属热处理, 2021, 46(8): 15-19.

Wang Xiaodong, Chen Yunbo, Zuo Lingli, You Long, Chen Chong, Mao Feng, Zhang Junjia. Precipitation behavior in V-N microalloyed CrSiMn low alloy cast steel[J]. Heat Treatment of Metals, 2021, 46(8): 15-19.

参考文献

[1]Skobir D A. High-strength low-allow (HSLA) steels[J]. Materials in Technologies, 2011, 45(4): 295-301.
[2]方芳, 雍岐龙, 杨才福, 等. V(C, N)在铁素体中的析出动力学模型研究[J]. 金属学报, 2009, 45(5): 625-629.
Fang Fang, Yong Qilong, Yang Caifu, et al. Precipitating kinetics of V(C,N) in ferrite of V-N microalloying steel[J]. Acta Metallurgica Sinica, 2009, 45(5): 625-629.
[3]包俊成, 赵捷, 宁保群, 等. 低碳铌钒微合金化钢奥氏体连续冷却转变行为[J]. 钢铁研究学报, 2013, 25(8): 28-31.
Bao Juncheng, Zhao Jie, Ning Baoqun, et al. Transformation behavior of austenite continuous cooling for Nb-V micro-alloyed low carbon steel[J]. Journal of Iron and Steel Research, 2013, 25(8): 28-31.
[4]杨才福, 张永权. 钒氮微合金化技术在HSLA钢中的应用[J]. 钢铁, 2002, 37(11): 42-47.
Yang Caifu, Zhang Yongquan. Applications of V-N microalloying technology in HSLA steels[J]. Iron and Steel, 2002, 37(11): 42-47.
[5]Wang H, Li Y, Detemple E, et al. Revealing the two-step nucleation and growth mechanism of vanadium carbonitrides in microalloyed steels[J]. Scripta Materialia, 2020, 187: 350-354.
[6]唐国翌, 郑炀曾, 蔡其巩, 等. V-Ti-N微合金钢的晶粒粗化行为[J]. 金属学报, 1989, 25(6): 414-420.
Tang Guoyi, Zheng Shangceng, Cai Qigong, et al. Grain coarsening temperature of V-Ti-N microalloying steels[J]. Acta Metallurgica Sinica, 1989, 25(6): 414-420.
[7]Najafi H, Rassizadehghani J, Halvaaee A. Mechanical properties of as cast microalloyed steels containing V, Nb and Ti[J]. Materials Science and Technology, 2013, 23(6): 699-705.
[8]Najafi H, Rassizadehghani J, Norouzi S. Mechanical properties of as-cast microalloyed steels produced via investment casting[J]. Materials & Design, 2011, 32(2): 656-663.
[9]张可, 孙新军, 雍岐龙, 等. 回火时间对高Ti微合金化淬火马氏体钢组织及力学性能的影响[J]. 金属学报, 2015(5): 43-50.
Zhang Ke, Sun Xinjun, Yong Qilong, et al. Effect of tempering time on microstructure and mechanical properties of high Ti microalloyed quenched martensitic steel[J]. Acta Metallurgica Sinica, 2015(5): 43-50.
[10]Akbarzadeh H A, Tamizifar M, Mirdamadi S, et al. Mechanical properties and microstructures of Zr-microalloyed cast steel[J]. Transactions of the Iron & Steel Institute of Japan, 2006, 45(8): 1201-1204.
[11]盛伟, 陈天运, 李志, 等. 基于JMatPro软件的超高强度钢强度设计[J]. 金属热处理, 2017, 42(6): 157-160.
Sheng Wei, Chen Tianyun, Li Zhi, et al. Strength design of ultra-high strength steel based on JMatPro software[J]. Heat Treatment of Metals, 2017, 42(6): 157-160.
[12]崔崑. 钢的成分、组织与性能(上册)[M]. 北京: 科学出版社, 2013.
[13]刘庆冬, 褚于良, 王泽民, 等. Nb-V微合金钢中渗碳体周围元素分布的三维原子探针表征[J]. 金属学报, 2008(11): 1281-1285.
Liu Qingdong, Chu Yuliang, Wang Zemin, et al. 3D atom probe characterization of alloying elements partitioning in cementite of Nb-V microalloying steel[J]. Acta Metallurgica Sinica, 2008(11): 1281-1285.

[1]	于洪军, 程福超, 马泽天, 王永金, 陈俊豪, 陈正家, 宋传颂馨. 不同水韧处理工艺下铌微合金化高锰钢的组织演变和力学性能[J]. 金属热处理, 2022, 47(4): 151-154.
[2]	王英虎, 郑淮北, 白青青, 宋令玺, 姚斌, 王利伟. 无磁钻铤用Cr-Mn-Ni-N系高氮钢平衡凝固相变与析出行为[J]. 金属热处理, 2022, 47(3): 173-180.
[3]	郭亚洲, 宋宁宏, 倪雷, 凌华, 毕文珍, 韦习成. B1800HS热成形钢组织转变的JMatPro计算和试验研究[J]. 金属热处理, 2022, 47(3): 239-244.
[4]	张鹏程, 武会宾. Ti微合金化对耐火建筑钢组织和性能的影响[J]. 金属热处理, 2022, 47(2): 9-13.
[5]	王舒镜, 王同浩, 王剑, 李玉平, 韩培德. B-Ce复合微合金化对S31254超级奥氏体不锈钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(2): 14-19.
[6]	郝天赐, 吴雍壕, 阴树标, 曹建春, 罗瀚宇. Zr对Ti-Mo复合微合金化钢形变奥氏体静态再结晶动力学和析出相的影响[J]. 金属热处理, 2022, 47(2): 41-47.
[7]	胡芳忠, 杨少朋, 金国忠, 胡乃悦, 汪开忠, 杨志强, 陈世杰. 淬火温度对Nb微合金化齿轮钢18CrNiMo7-6组织演变及力学性能的影响[J]. 金属热处理, 2022, 47(2): 105-111.
[8]	宋延沛, 陈丹萍, 周汉, 林小丽, 李丽. 热处理工艺对Cr15Ni2MnMoCuNbRE铸钢组织及性能的影响[J]. 金属热处理, 2022, 47(2): 178-182.
[9]	马启林, 刘刚, 郑健, 阴树标, 李拔, 刘清友. Nb-V复合微合金化高钢级管线钢的奥氏体连续冷却转变[J]. 金属热处理, 2022, 47(1): 13-18.
[10]	卓城之, 高丽, 顾炜华, 雍岐龙, 陆忠. Nb-V微合金化高碳钢在弹性盖板针布用钢丝上的运用[J]. 金属热处理, 2022, 47(1): 69-72.
[11]	王自敏, 杨志强, 胡芳忠, 汪开忠, 丁雷. Nb微合金化对18CrNiMo7-6钢奥氏体晶粒长大的影响[J]. 金属热处理, 2021, 46(9): 53-57.
[12]	于洪军, 陈正家, 迟晓明, 裴中正, 程福超, 许洁, 王永金. 淬火温度对中合金马氏体耐磨铸钢组织和性能的影响[J]. 金属热处理, 2021, 46(9): 133-137.
[13]	杨晓伟, 陈焕德, 周云, 张宇. 轧制工艺对V-Nb微合金化HRB600E钢筋组织及性能的影响[J]. 金属热处理, 2021, 46(8): 150-155.
[14]	吕晶, 杨其全, 张倩, 胡杰, 许鑫. 铸钢轮装制动盘螺栓孔裂纹产生原因分析[J]. 金属热处理, 2021, 46(7): 238-241.
[15]	王玉静, 吴光亮. 工程机械用高强钢Q1100热处理参数及热物理性能预测[J]. 金属热处理, 2021, 46(6): 172-176.

V-N微合金化CrSiMn系低合金铸钢中的析出行为

Precipitation behavior in V-N microalloyed CrSiMn low alloy cast steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价