碳含量对SA-508 Gr.3钢大锻件组织和性能的影响

doi:10.13251/j.issn.0254-6051.2021.07.015

金属热处理 ›› 2021, Vol. 46 ›› Issue (7): 79-83.DOI: 10.13251/j.issn.0254-6051.2021.07.015

碳含量对SA-508 Gr.3钢大锻件组织和性能的影响

张明桥, 傅明娇, 赵晓光, 付朝政, 汪洪宇, 李卓林

贵州航天科技有限公司, 贵州遵义 563003

收稿日期:2021-02-17 出版日期:2021-07-25 发布日期:2021-12-10
作者简介:张明桥(1985—),男,工程师,主要研究方向为金属塑性成形及热处理,E-mail: fmjblue@163.com。

Effect of carbon content on microstructure and properties of SA-508 Gr.3 steel heavy forgings

Zhang Mingqiao, Fu Mingjiao, Zhao Xiaoguang, Fu Chaozheng, Wang Hongyu, Li Zhuolin

Guizhou Aerospace Xinli Technology Co., Ltd., Zunyi Guizhou 563003, China

Received:2021-02-17 Online:2021-07-25 Published:2021-12-10

摘要/Abstract

摘要： 研究了碳含量对SA-508 Gr.3钢大锻件的显微组织和力学性能的影响。结果表明:随着碳含量的增加,SA-508 Gr.3钢的贝氏体转变温度降低,M₃C碳化物析出量增加;室温和350 ℃抗拉强度提高,冲击性能先升高后降低,0 ℃冲击断口形貌由混合型断裂转变为韧窝断裂。为使SA-508 Gr.3钢获得较好的综合性能,碳含量应控制在0.19%~0.22%(质量分数)。

关键词: SA-508 Gr.3钢, 大锻件, 碳含量, 组织, 性能

Abstract: Effect of carbon content on microstructure and properties of heavy forgings of SA-508 Gr.3 steel was investigated. The results show that as the carbon content of the steel increases, the bainite transformation temperature decreases and the precipitation amount of M₃C carbides increases. The tensile strength at room temperature and at 350 ℃ are obviously improved, the impact properties first increase and then decrease, and the impact fracture morphologies at 0 ℃ change from mixed fracture to dimple fracture. In order to obtain a better performance, the carbon content of SA-508 Gr.3 steel should be controlled within 0.19%~0.22%(mass fraction).

Key words: SA-508 Gr.3 steel, heavy forgings, carbon content, microstructure, property

中图分类号:

TG142.33

张明桥, 傅明娇, 赵晓光, 付朝政, 汪洪宇, 李卓林. 碳含量对SA-508 Gr.3钢大锻件组织和性能的影响[J]. 金属热处理, 2021, 46(7): 79-83.

Zhang Mingqiao, Fu Mingjiao, Zhao Xiaoguang, Fu Chaozheng, Wang Hongyu, Li Zhuolin. Effect of carbon content on microstructure and properties of SA-508 Gr.3 steel heavy forgings[J]. Heat Treatment of Metals, 2021, 46(7): 79-83.

参考文献

[1] 李承亮, 张明乾. 压水堆核电站反应堆压力容器材料概述[J]. 材料导报, 2008, 22(9): 65-68.
Li Chenliang, Zhang Mingqian. Overview of reactor pressure vessel steel in PWR nuclear power plants[J]. Materials Review, 2008, 22(9): 65-68.
[2] 阮於珍. 核电厂材料[M]. 北京: 原子能出版社, 2010.
[3] 顾军. AP1000设备技术及分析[M]. 北京: 中国原子能出版传媒有限公司, 2011.
[4] 王伟. 核电材料SA508-3钢非均匀热变形实验与数值模拟研究[D]. 上海: 上海交通大学, 2013.
Wang Wei. Research of nuclear power material SA508-3 steel in homogeneous hot deformation experiment and numerical simulation[D]. Shanghai: Shanghai Jiao Tong University, 2013.
[5] 白天. AP1000压力容器法兰接管锻件的组织和性能评价[D]. 昆明: 昆明理工大学, 2013.
[6] 马玉霞, 党淑娥, 秦尚武, 等. SA508-3钢粗大非平衡组织重新加热奥氏体晶核形成与长大行为[J]. 金属热处理, 2018, 43(10): 41-45.
Ma Yuxia, Dang Shu'e, Qin Shangwu, et al. Formation and growth behavior of austenite nuclei in coarse and non-equilibrium structure of SA508-3 steel during reheating[J]. Heat Treatment of Metals, 2018, 43(10): 41-45.
[7] 陈宏宇, 刘正东, 林肇杰, 等. SA508-3钢平衡相转变的热力学计算和分析[J]. 特殊钢, 2007, 28(2): 19-21.
Chen Hongyu, Liu Zhengdong, Liu Zhaojie, et al. Thermodynamic calculation and analysis on equilibrium phases transformation in SA508-3 steel[J]. Special Steel, 2007, 28(2): 19-21.
[8] 胡本芙, 杨兴博, 林岳萌. 核电站压力容器用SA508-3钢厚截面锻件热处理冷却速度[J]. 钢铁, 1998, 33(5): 49-52.
Hu Benfu, Yang Xingbo, Lin Yuemeng. Quenching cooling rate of heavy section SA508-3 steel forging for pressure vessel for nuclear power station[J]. Iron ang Steel, 1998, 33(5): 49-52.
[9] 杨兴博, 孙永立, 程义, 等. 国产SA508-3锻件厚度-平均冷却速度-显微组织-力学性能关系的研究[J]. 锅炉制造, 1995(4): 29-35.
Yang Xingbo, Sun Yongli, Cheng Yi, et al. Research of the relation among the thickness-average cooling rate-microstructure-mechanical properties of forging SA508-3 in China[J]. Boiler Manufacturing, 1995(4): 29-35.
[10] 韩利战, 顾剑锋, 龙智南, 等. 不同冷却条件下核电大锻件用钢显微组织分析[C]//中国核学会2011年学术年会论文集, 2011: 534-541.
[11] Kim S, Im Y R, Lee S, et al. Effects of alloying elements on fracture toughness in the transition temperature region of base metals and simulated heat-affected zones of Mn-Mo-Ni low-alloy steels[J]. Metallurgical and Materials Transactions A, 2004, 35(7): 2027-2037.
[12] Tanaka Y, Sato I. Development of high purity large forgings for nuclear power plants[J]. Journal of Nuclear Materials, 2011, 417(1/3): 854-859.
[13] Lee S G, Kim I S. Effect of pre-charged hydrogen on fatigue crack growth of low alloy steel at 288 ℃[J]. Materials Science and Engineering A, 2006, 420(1/2): 279-283.
[14] Lee S, Kim S, Hwang B, et al. Effect of carbide distribution on the fracture toughness in the transition temperature region of an SA508 steel[J]. Acta Materialia, 2002, 50(19): 4755-4762.
[15] Lee Ki-Hyoung, Kim Min-Chul, Yang Won-Jon, et al. Evaluation of microstructural parameters controlling cleavage fracture toughness in Mn-Mo-Ni low alloy steels[J]. Materials Science and Engineering A, 2013, 565: 158-164.
[16] 王天睿. 厚大断面核电压力容器SA 508-3钢锻件低温冲击韧性研究[D]. 沈阳: 沈阳理工大学, 2017.
Wang Tianrui. Study on low temperature impact toughness of SA 508-3 steel for heavy section forging in reactor pressure vessel[D]. Shenyang: Shenyang Ligong University, 2017.

碳含量对SA-508 Gr.3钢大锻件组织和性能的影响

Effect of carbon content on microstructure and properties of SA-508 Gr.3 steel heavy forgings

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[2]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[3]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[4]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[5]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[6]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[7]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[8]	贾昌远, 霍元明, 何涛, 霍存龙, 刘克然. 40CrNiMo钢高温拉伸变形行为和组织演变规律[J]. 金属热处理, 2022, 47(4): 69-74.
[9]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[10]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[11]	刘丽艳, 毕文珍, 韦习成. Mn元素对热冲压钢镀锌层组织演变的影响[J]. 金属热处理, 2022, 47(4): 93-99.
[12]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[13]	白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.
[14]	陈刚, 罗小兵, 柴锋, 杨才福, 张正延, 杨丽. 轧制加热温度对高强度低合金钢组织及冲击性能的影响[J]. 金属热处理, 2022, 47(4): 116-121.
[15]	付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.