不同镍含量奥氏体基低密度热轧钢的组织与力学性能

doi:10.13251/j.issn.0254-6051.2021.12.006

金属热处理 ›› 2021, Vol. 46 ›› Issue (12): 31-39.DOI: 10.13251/j.issn.0254-6051.2021.12.006

不同镍含量奥氏体基低密度热轧钢的组织与力学性能

王凤权^1,2, 孙挺², 王毛球², 尉文超², 周晓龙¹

1.昆明理工大学材料科学与工程学院, 云南昆明 650093;
2.钢铁研究总院特殊钢研究所, 北京 100081

收稿日期:2021-08-04 出版日期:2021-12-25 发布日期:2022-02-18
通讯作者: 孙挺,高级工程师,博士,E-mail:suntingsj@163.com
作者简介:王凤权(1995—),男,硕士研究生,主要研究方向为低密度钢的研发与应用,E-mail:1710488879@qq.com。
基金资助:
国家重点研发计划(2016YFB0300100)

Microstructure and mechanical properties of low density austenitic matrix hot rolling steel with different Ni contents

Wang Fengquan^1,2, Sun Ting², Wang Maoqiu², Yu Wenchao², Zhou Xiaolong¹

1. Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming Yunnan 650093, China;
2. Research Institute of Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China

Received:2021-08-04 Online:2021-12-25 Published:2022-02-18

摘要/Abstract

摘要： 研究了3种Fe-18Mn-10Al-1C-(0, 3, 5)Ni-0.08V-0.03Nb(wt%)奥氏体基低密度双相钢在热轧后的组织和力学性能。结果表明,热轧后,试验钢的组织由拉长的奥氏体、条带状B2相及沿再结晶奥氏体晶粒晶界处的块状B2颗粒组成。此外,在奥氏体晶粒和B2颗粒中分别形成了纳米级κ-碳化物和DO₃相。5Ni钢屈服强度高达1352 MPa,这主要是由于奥氏体晶界存在大量纳米级别的B2颗粒以及VC相产生析出强化效果。随着Ni含量的增加,钢的强度与硬度均增加,5Ni钢屈服强度比0Ni钢高116 MPa,归因于5Ni钢中更多的B2相含量(16.9%)。但含Ni钢在强度增加的同时,极大损失了塑性,导致钢的伸长率极低,分析其原因为条带状B2相主要分布在奥氏体晶界处,试样在变形过程中裂纹更易沿晶界断裂,断口有分层现象。

关键词: 奥氏体基, 低密度钢, Ni含量, B2相, 热轧, 力学性能

Abstract: The microstructure and mechanical properties of three kinds of Fe-18Mn-10Al-1C-(0, 3, 5)Ni-0.08V-0.03Nb (wt%) austenitic matrix low density dual phase steels after hot rolling were studied. The results show that the microstructure of the steel after hot rolling is composed of elongated austenite, band B2 and massive B2 particles along the grain boundaries of recrystallized austenite grains. In addition, nano-sized κ-carbide and DO₃ phase are formed in austenite grains and B2 grains, respectively. The yield strength of the tested 5Ni steel reaches 1352 MPa, which is mainly due to the precipitation strengthening effect of a large number of nano-sized B2 particles and VC phase in the austenite grain boundary. With the increase of Ni content, the strength and hardness of the steel increase, and the yield strength of 5Ni steel is 116 MPa higher than that of 0Ni steel, which is attributed to more B2 phase content (16.9%) in the 5Ni steel. However, while the strength of the Ni-containing steel increases, the plasticity of the steel is greatly lost, resulting in a very low elongation. The reason is that the banded B2 phase is mainly distributed at the austenite grain boundary, and the crack is easier to break along the grain boundary in the process of deformation. In the meantime, delamination can be observed on the fracture surface.

Key words: austenite matrix, low density steel, Ni content, B2 phase, hot rolling, mechanical properties

中图分类号:

TG142.1

王凤权, 孙挺, 王毛球, 尉文超, 周晓龙. 不同镍含量奥氏体基低密度热轧钢的组织与力学性能[J]. 金属热处理, 2021, 46(12): 31-39.

Wang Fengquan, Sun Ting, Wang Maoqiu, Yu Wenchao, Zhou Xiaolong. Microstructure and mechanical properties of low density austenitic matrix hot rolling steel with different Ni contents[J]. Heat Treatment of Metals, 2021, 46(12): 31-39.

参考文献

[1]Frommeyer G, Bruex U. Microstructures and mechanical properties of high-strength Fe-Mn-Al-C light-weight TRIPLEX steels[J]. Steel Research, 2006, 77(9/10): 627-633.
[2]杨富强, 宋仁伯, 李亚萍, 等. 退火温度对冷轧Fe-Mn-Al-C低密度钢性能的影响[J]. 材料研究学报, 2015, 29(2): 108-114.
Yang Fuqiang, Song Renbo, Li Yaping, et al. Effect of annealing temperature on properties of cold rolled Fe-Mn-Al-C low density steel[J]. Chinese Journal of Materials Research, 2015, 29(2): 108-114.
[3]刘少尊, 厉勇, 王春旭, 等. 固溶处理对Fe-Mn-Al-C系低密度钢组织与性能的影响[J]. 金属热处理, 2015, 40(9): 120-124.
Liu Shaozun, Li Yong, Wang Chunxu, et al. Effect of solution treatment on microstructure and properties of Fe-Mn-Al-C low density steel[J]. Heart Treatment of Metals, 2015, 40(9): 120-124.
[4]Zhao C, Song R, Zhang L, et al. Effect of annealing temperature on the microstructure and tensile properties of Fe-10Mn-10Al-0.7C low-density steel[J]. Materials and Design, 2016, 91(2): 348-360.
[5]Yang M X, Yuan F P, Xie Q G, et al. Strain hardening in Fe-16Mn-10Al-0.86C-5Ni high specific strength steel[J]. Acta Materialia, 2016, 109: 213-222.
[6]Hwang S W, Ji J H, Lee E G, et al. Tensile deformation of a duplex Fe-20Mn-9Al-0.6C steel having the reduced specific weight[J]. Materials Science and Engineering A, 2011, 528(15): 5196-5203.
[7]Yang F Q, Song R B, Li Y P, et al. Tensile deformation of low density duplex Fe-Mn-Al-C steel[J]. Materials and Design, 2015, 76(7): 32-39.
[8]Ha M C, Koo J M, Lee J K, et al. Tensile deformation of a low density Fe-27Mn-12Al-0.8C duplex steel in association with ordered phases at ambient temperature[J]. Materials Science and Engineering A, 2013, 586: 276-283.
[9]Liu D, Cai M, Ding H, et al. Control of inter/intra-granular κ-carbides and its influence on overall mechanical properties of a Fe-11Mn-10Al-1.25C low density steel[J]. Materials Science and Engineering A, 2017, 715: 25-32.
[10]Ding H, Li H Y, Devesh K, et al. Strengthening mechanisms in low density Fe-26Mn-xAl-1C steels[J]. Steel Research International, 2017, 89(9): 1700381.
[11]Hwang J H, Trang T T T, Lee O, et al. Improvement of strength-ductility balance of B2-strengthened lightweight steel[J]. Acta Materialia, 2020, 191: 1-12.
[12]Ding H, Han D, Cai Z, et al. Microstructures and mechanical behavior of Fe-18Mn-10Al-(0.8-1.2)C steels[J]. JOM, 2014, 66(9): 1821-1827.
[13]Zhang J L, Raabe D. Designing duplex, ultrafine-grained Fe-Mn-Al-C steels by tuning phase transformation and recrystallization kinetics[J]. Acta Materialia, 2017, 141: 374-387.
[14]Huang H, Yang G, Zhao G, et al. Effect of Nb on the microstructure and properties of Ti-Mo microalloyed high-strength ferritic steel[J]. Materials Science and Engineering A, 2018, 736(24): 148-155.
[15]Zargaran A, Kim H S, Kwak J H. Effects of Nb and C additions on the microstructure and tensile properties of lightweight ferritic Fe-8Al-5Mn alloy[J]. Scripta Materialia, 2014, 89: 37-40.
[16]Li Z, Wang Y C, Cheng X W, et al. The effect of Ti-Mo-Nb on the microstructures and tensile properties of a Fe-Mn-Al-C austenitic steel[J]. Acta Materialia, 2020, 780: 139-146.
[17]Kim S H, Kim H, Kim N J. Brittle intermetallic compound makes ultrastrong low-density steel with large ductility[J]. Nature, 2015, 518: 77-82.
[18]Cheng Weichun. Phase transformations of an Fe-0.85C-17.9Mn-7.1Al austenitic steel after quenching and annealing[J]. JOM, 2014, 66(9): 1809-1820.
[19]Kim H, Suh D W, Kim N J. Fe-Al-Mn-C lightweight structural alloys: A review on the microstructures and mechanical properties[J]. Science and Technology of Advanced Materials, 2013, 14(1): 014205.
[20]Rahnama A, Kotadia H, Sridhar S. Effect of Ni alloying on the microstructural evolution and mechanical properties of two duplex light-weight steels during different annealing temperatures: Experiment and phase-field simulation[J]. Acta Materialia, 2017, 132: 627-643.
[21]雍岐龙. 钢铁材料中的第二相[M]. 北京: 冶金工业出版社, 2006.
Yong Qilong. The second phase in iron and steel[M]. Beijing: Metallurgical Industry Press, 2006.

不同镍含量奥氏体基低密度热轧钢的组织与力学性能

Microstructure and mechanical properties of low density austenitic matrix hot rolling steel with different Ni contents

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[2]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[3]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[4]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[5]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[6]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[7]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[8]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[9]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[10]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[11]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[12]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[13]	陈强, 陈林芳, 杨明华. 18CrNiMo7-6钢的可控气氛高温渗碳工艺[J]. 金属热处理, 2022, 47(4): 231-239.
[14]	刘乃瑜, 曹磊, 郑少梅. 不同沉积温度下CrCN涂层的力学性能[J]. 金属热处理, 2022, 47(4): 240-244.
[15]	刘志桥, 冯庆晓, 李化龙, 李腾飞. 退火工艺对低碳贝氏体钢组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 53-56.