21Cr节镍型双相不锈钢高温形变过程的静态软化分析

doi:10.13251/j.issn.0254-6051.2022.01.014

金属热处理 ›› 2022, Vol. 47 ›› Issue (1): 79-87.DOI: 10.13251/j.issn.0254-6051.2022.01.014

21Cr节镍型双相不锈钢高温形变过程的静态软化分析

崔聪, 高飞, 高野, 刘振宇

东北大学材料科学与工程学院, 辽宁沈阳 110819

收稿日期:2021-08-15 修回日期:2021-09-21 出版日期:2022-01-25 发布日期:2022-02-18
通讯作者: 刘振宇,教授,博士生导师,E-mail:zylin_nen@sina.com
作者简介:崔聪(1996—),女,硕士研究生,主要研究方向为双相不锈钢的组织与性能,E-mail:2435082020@qq.com。
基金资助:
兴辽英才项目(XLYC1902034)

Static softening analysis of 21Cr nickel saving duplex stainless steel during high temperature deformation process

Cui Cong, Gao Fei, Gao Ye, Liu Zhenyu

School of Materials Science and Engineering, Northeastern University, Shenyang Liaoning 110819, China

Received:2021-08-15 Revised:2021-09-21 Online:2022-01-25 Published:2022-02-18

摘要/Abstract

摘要： 采用热模拟研究了21Cr双相不锈钢在高温变形道次间隔时间内的静态软化行为,讨论了变形温度、应变速率和变形程度对静态再结晶行为及微观组织的影响。结果表明,变形条件通过影响两相内部应变分配进一步影响双相不锈钢静态软化行为。随着变形温度和变形程度增加,铁素体相内承担的应变增加,铁素体内部再结晶程度增加,促进双相不锈钢的静态软化程度增加;而随着应变速率的增加,试验钢静态软化率的变化规律与奥氏体相承担的应变变化规律相同,都呈现出先降低后升高的变化趋势,奥氏体相在应变速率为1 s^-1时的内部再结晶程度最低。21Cr双相不锈钢静态再结晶激活能约为301 kJ/mol。

关键词: 21Cr双相不锈钢, 双道次热压缩, 应变分配, 静态软化, 显微组织

Abstract: Static softening behavior of 21Cr duplex stainless steel during high temperature deformation pass interval was studied by using thermal simulation. The effects of deformation temperature, strain rate and deformation degree on static recrystallization behavior and microstructure were discussed. The results show that the deformation conditions further affect the static softening behavior of duplex stainless steel by affecting the strain distribution in the two phases. With the increase of strain temperature and deformation degree, the strain in ferrite phase increases, and the recrystallization degree in ferrite increases, which causes the increase of static softening degree of duplex stainless steel. With the increase of strain rate, the variation of static softening rate is the same as that of strain assumed by austenite phase, which shows a trend of first decreasing and then increasing. The internal recrystallization degree of austenite is the lowest when the strain rate is 1 s^-1. The activation energy of static recrystallization of the 21Cr duplex stainless steel is about 301 kJ/mol.

Key words: 21Cr duplex stainless steel, double pass hot compression, strain distribution, static softening, microstructure

中图分类号:

TG142.1

崔聪, 高飞, 高野, 刘振宇. 21Cr节镍型双相不锈钢高温形变过程的静态软化分析[J]. 金属热处理, 2022, 47(1): 79-87.

Cui Cong, Gao Fei, Gao Ye, Liu Zhenyu. Static softening analysis of 21Cr nickel saving duplex stainless steel during high temperature deformation process[J]. Heat Treatment of Metals, 2022, 47(1): 79-87.

参考文献

[1]Ma L, Hu S, Shen J, et al. Effects of Cr content on the microstructure and properties of 26Cr-3.5Mo-2Ni and 29Cr-3.5Mo-2Ni super ferritic stainless steels[J]. Journal of Materials Science and Technology, 2016, 32(6): 552-560.
[2]Nilsson J O. Super duplex stainless steels[J]. Metal Science Journal, 1992, 8(8): 685-700.
[3]Guo Y, Han E H, Wang J. Effects of forging and heat treatments on the microstructure and oxidation behavior of 316LN stainless steel in high temperature water[J]. Journal of Materials Science and Technology, 2015, 31(4): 403-412.
[4]方轶琉, 刘振宇, 张维娜, 等. 节约型双相不锈钢2101高温变形过程中微观组织演化[J]. 金属学报, 2010, 46(6): 641-646.
Fang Yiliu, Liu Zhenyu, Zhang Weina, et al. Microstructure evolution of lean duplex stainless steel 2101 during hot deformation[J]. Acta Metallurgica Sinica, 2010, 46(6): 641-646.
[5]苏煜森, 杨银辉, 曹建春, 等. 节Ni型2101双相不锈钢的高温热加工行为研究[J]. 金属学报, 2018, 54(4): 485-493.
Su Yusen, Yang Yinhui, Cao Jianchun, et al. Research on hot working behavior of low-nickel duplex stainless steel 2101[J]. Acta Metallurgica Sinica, 2018, 54(4): 485-493.
[6]Momeni A, Dehghani K, Poletti M C. Law of mixture used to model the flow behavior of a duplex stainless steel at high temperatures[J]. Materials Chemistry and Physics, 2013, 139(2): 747-755.
[7]Zhao Y, Li X, Zhang W N, et al. Strain partitioning and softening mechanisms of δ/γ in lean duplex stainless steels during hot deformation[J]. Steel Research International, 2020, 91(1): 1900212.
[8]Kazeminezhad M. On the modeling of the static recrystallization considering the initial grain size effects[J]. Materials Science and Engineering A, 2008, 486(1): 202-207.
[9]Laasraoui A, Jonas J J. Prediction of temperature distribution, flow stress and microstructure during the multipass hot rolling of steel plate and strip[J]. ISIJ International, 1991, 31(1): 95-105.
[10]Rao K P, Prasad Y K D V, Hawbolt E B. Study of fractional softening in multi-stage hot deformation[J]. Journal of Materials Processing Technology, 1998, 77(1/3): 166-174.
[11]Sun W P, Hawbolt E B. Comparison between static and metadynamic recrystallization - An application to the hot rolling of steels[J]. ISIJ International, 1997, 37(10): 1000-1009.
[12]张进学, 刘洁, 张传滨, 等. 核电用304不锈钢静态再结晶模型的建立[J]. 铸造设备与工艺, 2011(2): 13-16.
Zhang Jinxue, Liu Jie, Zhang Chuanbin, et al. Establishment of the grain size model for the static recrystallization behaviors of nuclear power 304 stainless steel[J]. Foundry Equipment and Technology, 2011(2): 13-16.
[13]Cho S H, Kang K B, Jonas J J. Effect of manganese on recrystallisation kinetics of niobium microalloyed steel[J]. Metal Science Journal, 2013, 18(4): 389-395.
[14]Kuang S, Kang Y L, Yu H, et al. Stress-strain partitioning analysis of constituent phases in dual phase steel based on the modified law of mixture[J]. International Journal of Minerals, Metallurgy and Materials, 2009, 16(4): 393-398.
[15]Chen L, Ma X, Xiao L, et al. Processing map for hot working characteristics of a wrought 2205 duplex stainless steel[J]. Materials and Design, 2011, 32(3): 1292-1297.
[16]王月香, 刘振宇, 王国栋, 等. 变形速率对2205双相不锈钢形变诱导相变的影响[J]. 东北大学学报, 2009, 30(12): 1731-1734.
Wang Yuexiang, Liu Zhenyu, Wang Guodong, et al. Influence of deformation rate on strain-induced phase transition of 2205 duplex stainless steel[J]. Journal of Northeastern University, 2009, 30(12): 1731-1734.
[17]王立新, 李花兵, 李国平, 等. 2205和2507双相不锈钢双道次热压缩条件下的微观组织演变及变形行为[J]. 材料研究学报, 2016, 30(12): 888-896.
Wang Lixin, Li Huabing, Li Guoping, et al. Microstructural evolution and flow behavior of 2205 and 2507 duplex stainless steel during double pass hot compressive deformation[J]. Chinese Journal of Materials Research, 2016, 30(12): 888-896.
[18]蔺永诚, 陈明松, 钟掘. 42CrMo钢形变奥氏体的静态再结晶[J]. 中南大学学报, 2009, 40(2): 411-416.
Lin Yongcheng, Chen Mingsong, Zhong Jue. Static recrystallization behaviors of deformed 42CrMo steel[J]. Journal of Central South University, 2009, 40(2): 411-416.
[19]Cizek P, Wynne B P. A mechanism of ferrite softening in a duplex stainless steel deformed in hot torsion[J]. Materials Science and Engineering A, 1997, 230(1): 88-94.
[20]康喜英, 赵宏伟, 高东升, 等. 高温塑性变形对超级双相不锈钢S32750的性能影响[J]. 热加工工艺, 2018, 47(7): 159-161.
Kang Xiying, Zhao Hongwei, Gao Dongsheng, et al. Effects of high temperature plastic deformation on properties of super duplex stainless steel S32750[J]. Hot Working Technology, 2018, 47(7): 159-161.

21Cr节镍型双相不锈钢高温形变过程的静态软化分析

Static softening analysis of 21Cr nickel saving duplex stainless steel during high temperature deformation process

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[3]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[4]	王庆娟, 田云飞, 高贝特, 史佳敏, 吴欢, 蔡军. 工业纯钛TA1的双道次热压缩变形及软化行为[J]. 金属热处理, 2022, 47(4): 75-79.
[5]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[6]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[7]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[8]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[9]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[10]	张宁, 高星, 王芝林, 蒋波, 刘雅政. 18CrNiMo7-6钢齿轮组织性能异常分析[J]. 金属热处理, 2022, 47(4): 268-273.
[11]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.
[12]	孙建, 黄贞益, 李景辉, 王萍. 固溶和时效处理对Fe-Mn-Al-C轻质钢组织和硬度的影响[J]. 金属热处理, 2022, 47(3): 34-38.
[13]	王方军, 刘应龙, 时瑶, 万红, 刘斌斌. 等温退火处理对Inconel 625合金箔材组织和性能的影响[J]. 金属热处理, 2022, 47(3): 77-81.
[14]	张曼雪, 景然, 张雄, 张晴, 吴倩, 刘以柔. 铸态Ti-20Zr-10Nb-xMo合金的微观组织和耐腐蚀性能[J]. 金属热处理, 2022, 47(3): 147-150.
[15]	宁静, 高坤元, 李浩楠, 文胜平, 黄晖, 吴晓蓝, 魏午, 聂祚仁. 成分和冷却速度对Al-xEr合金凝固组织的影响[J]. 金属热处理, 2022, 47(3): 151-154.