时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响

doi:10.13251/j.issn.0254-6051.2022.01.036

金属热处理 ›› 2022, Vol. 47 ›› Issue (1): 217-225.DOI: 10.13251/j.issn.0254-6051.2022.01.036

时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响

谭皎, 张伯岩, 朱文光, 孙巧艳

西安交通大学金属材料强度国家重点实验室, 陕西西安 710049

收稿日期:2021-08-13 修回日期:2021-10-19 出版日期:2022-01-25 发布日期:2022-02-18
通讯作者: 孙巧艳,教授,E-mail:qysun@xjtu.edu.cn
作者简介:谭皎(1996—),女,硕士研究生,主要研究方向为钛合金的组织性能,E-mail:jiaozi@stu.xjtu.edu.cn。
基金资助:
国家自然科学基金项目(51671158),国家重点基础研究发展计划(973计划)(2014CB644003)

Effect of aging temperature on microstructure and mechanical properties of Ti-5Al-4Zr-10Mo-3Cr titanium alloy

Tan Jiao, Zhang Boyan, Zhu Wenguang, Sun Qiaoyan

State Key Laboratory for Mechanical Behavior of Materials, Xi'an Jiaotong University, Xi'an Shaanxi 710049, China

Received:2021-08-13 Revised:2021-10-19 Online:2022-01-25 Published:2022-02-18

摘要/Abstract

摘要： 研究了Ti-5Al-4Zr-10Mo-3Cr合金经过β相区固溶(880 ℃)、不同温度时效(540~620 ℃)处理后次生α相(α_s)析出形貌及其对力学性能的影响。结果表明:随着时效温度由540 ℃升高至620 ℃,合金中析出α_s相片层厚度由0.030 μm增加到0.142 μm,屈服强度由1353 MPa降低至1074 MPa,断后伸长率由2.5%升高至11.4%,即时效析出的微米级片层α_s能够显著调控合金的力学性能。此外,时效温度升高使合金的拉伸断裂由沿晶脆性断裂为主转变为韧窝穿晶为主的韧性断裂方式。Ti-5Al-4Zr-10Mo-3Cr合金时效析出的片层状α_s相的厚度大于0.1 μm,合金的断后伸长率≥6%。当时效温度为600 ℃时,合金的硬度为387 HV10,抗拉强度为1182 MPa,伸长率为8.5%,具有良好的强塑性匹配。

关键词: β钛合金, 时效处理, 微观组织, 力学性能

Abstract: Precipitation behavior and mechanical properties of secondary α phase (α_s) in the Ti-5Al-4Zr-10Mo-3Cr alloy after solution treatment in β phase region (at 880 ℃) and aging at different temperatures (540-620 ℃) were studied. The results show that with the aging temperature increasing from 540 ℃ to 620 ℃, the thickness of precipitated α_s increases from 0.030 μm to 0.142 μm, the yield strength decreases from 1353 MPa to 1074 MPa, and the elongation after fracture increases from 2.5% to 11.4%. This indicates that the micro-scaled α_s precipitated by aging can regulate the mechanical properties of the alloy. In addition, with the increase of aging temperature, the tensile fracture of the alloy changes from intergranular brittle fracture to dimple transgranular ductile fracture. The thickness of the α precipitation in the Ti-5Al-4Zr-10Mo-3Cr alloy is greater than 0.1 μm, which brings about the elongation after fracture larger than 6%. When the aging temperature is 600 ℃, the hardness, tensile strength and elongation after fracture are 387 HV10, 1182 MPa and 8.5% respectively, possessing good combination of strength and ductility.

Key words: β-titanium alloy, aging treatment, microstructure, mechanical properties

中图分类号:

TG146.2⁺3

谭皎, 张伯岩, 朱文光, 孙巧艳. 时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响[J]. 金属热处理, 2022, 47(1): 217-225.

Tan Jiao, Zhang Boyan, Zhu Wenguang, Sun Qiaoyan. Effect of aging temperature on microstructure and mechanical properties of Ti-5Al-4Zr-10Mo-3Cr titanium alloy[J]. Heat Treatment of Metals, 2022, 47(1): 217-225.

参考文献

[1]张翥, 王群骄, 莫畏. 钛的金属学和热处理[M]. 北京: 冶金工业出版社, 2009: 1-4.
[2]夏晓洁, 吴国清, 黄正, 等. 固溶时效处理对高强高韧钛合金显微组织与力学性能的影响[J]. 北京航空航天大学学报, 2015, 41(7): 1294-1299.
Xia Xiaojie, Wu Guoqing, Huang Zheng, et al. Effects of solution-aging treatment on microstructure and mechanical properties of a high-strength and high-toughness titanium alloy[J]. Journal of Beijing University of Aeronautics and Astronautics, 2015, 41(7): 1294-1299.
[3]Shekhar S, Sarkar R, Kar S K, et al. Effect of solution treatment and aging on microstructure and tensile properties of high strength β titanium alloy Ti-5Al-5V-5Mo-3Cr[J]. Materials and Design, 2015, 66: 596-610.
[4]Ren L, Xiao W L, Chang H, et al. Microstructural tailoring and mechanical properties of a multi-alloyed near β titanium alloy Ti-5321 with various heat treatment[J]. Materials Science and Engineering: A, 2018, 711: 553-561.
[5]Ahmed M, Li T, Casillas G, et al. The evolution of microstructure and mechanical properties of Ti-5Al-5Mo-5V-2Cr-1Fe during ageing[J]. Journal of Alloys and Compounds, 2015, 629: 260-273.
[6]Banerjee D, Williams J C. Perspectives on titanium science and technology[J]. Acta Materialia, 2013, 61(3): 844-879.
[7]Li C, Chen J, Li W, et al. Effect of heat treatment variations on the microstructure evolution and mechanical properties in a β metastable Ti alloy[J]. Journal of Alloys and Compounds, 2016, 684: 466-473.
[8]Manda P, Nandam S R, Chakkingal U, et al. Microstructure, texture and mechanical properties of hot rolled metastable β-titanium alloy Ti-5Al-3.5Mo-7.2V-3Cr[J]. Materials Today: Proceedings, 2017, 4(2): 851-856.
[9]Chen Y Y, Du Z X, Xiao S L, et al. Effect of aging heat treatment on microstructure and tensile properties of a new β high strength titanium alloy[J]. Journal of Alloys and Compounds, 2014, 586: 588-592.
[10]Du Z X, Xiao S L, Xu L J, et al. Effect of heat treatment on microstructure and mechanical properties of a new β high strength titanium alloy[J]. Materials and Design, 2014, 55: 183-190.
[11]赵永庆, 陈永楠, 张学敏, 等. 钛合金相变及热处理[M]. 长沙: 中南大学出版社, 2012: 128-155.
[12]Zhu W G, Sun Q Y, Tan C S, et al. Tensile brittleness and ductility improvement in a novel metastable β titanium alloy with lamella structure[J]. Journal of Alloys and Compounds, 2020, 827: 154311.
[13]Dong R F, Li J S, Kou H C, et al. ω-assisted refinement of α phase and its effect on the tensile properties of a near β titanium alloy[J]. Journal of Materials Science and Technology, 2020, 44(9): 26-32.
[14]Ivasishin O M, Markovsky P E, Matviychuk Y V, et al. A comparative study of the mechanical properties of high-strength β-titanium alloys[J]. Journal of Alloys and Compounds, 2008, 457: 296-309.
[15]Li C L, Mi X J, Ye W J, et al. A study on the microstructures and tensile properties of new beta high strength titaniumalloy[J]. Journal of Alloys and Compounds, 2013, 550: 23-30.
[16]Du Z, Ma Y, Liu F, et al. Improving mechanical properties of near beta titanium alloy by high-low duplex aging[J]. Materials Science and Engineering: A, 2019, 754(29): 702-707.
[17]Du Z, Guo H, Liu J, et al. Microstructure evolution during aging heat treatment and its effects on tensile properties and dynamic Young's modulus of a biomedical β titanium alloy[J]. Materials Science and Engineering A, 2020, 791: 139677.
[18]Zhu W G, Kou W, Tan C, et al. Face centered cubic substructure and improved tensile property in a novel β titanium alloy Ti-5Al-4Zr-10Mo-3Cr[J]. Materials Science and Engineering A, 2019, 771: 138611.
[19]王安东, 张禄祥, 陈彩凤, 等. 固溶时效处理对Ti-5322钛合金组织与性能的影响[J]. 金属热处理, 2020, 45(12): 24-28.
Wang Andong, Zhang Luxiang, Chen Caifeng, et al. Effect of solution and aging treatment on microstructure and tensile properties of Ti-5322 alloy[J]. Heat Treatment of Metals, 2020, 45(12): 24-28.
[20]乔虹, 刘运玺, 陈玮, 等. 热处理对EBM Ti-4Al-5V-5Mo-6Cr-1Nb合金显微组织与拉伸性能的影响[J]. 航空制造技术, 2020, 63(19): 85-90.
Qiao Hong, Liu Yunxi, Chen Wei, et al. Effect of heat treatment on microstructure and tensile properties of EBM Ti-4Al-5V-5Mo-6Cr-1Nb alloy[J]. Aeronautical Manufacturing Technology, 2020, 63(19): 85-90.
[21]Zhang H Y, Li X H, Lin L, et al. Effect of aging temperature on microstructural evolution and mechanical properties of a novel β titanium alloy[J]. Rare Metal Materials and Engineering, 2019, 48(12): 3812-3818.
[22]Zhu W G, Lei J, Tan C S, et al. A novel high-strength β-Ti alloy with hierarchical distribution of α-phase: The superior combination of strength andductility[J]. Materials and Design, 2019, 168: 107640.
[23]Devaraj A, Joshi V V, Srivastava A, et al. A low-cost hierarchical nanostructured beta-titanium alloy with high strength[J]. Nature Communications, 2016, 7: 11176.
[24]Mantri S A, Choudhuri D, Alam T, et al. Tuning the scale of α precipitates in β-titanium alloys for achieving high strength[J]. Scripta Materialia, 2018, 154: 139-144.
[25]Terlinde G T, Duerig T W, Williams J C. Microstructure, tensile deformation, and fracture in aged Ti-10V-2Fe-3Al[J]. Metallurgical Transactions A, 1983, 14(10): 2105-2115.
[26]Vinjamuri R, Bishoyi B D, Sabat R K, et al. Microstructure, texture, mean free path of dislocations and mechanical properties of Ti-6A1-4V alloy during uniaxial compression at elevated temperatures[J]. Materials Science and Engineering: A, 2020, 776: 139042.
[27]Julia R G, Warren C O, William D N. Size dependence of mechanical properties of gold at the micron scale in the absence of straingradients[J]. Acta Materialia, 2005, 53(6): 1821-1830.

时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响

Effect of aging temperature on microstructure and mechanical properties of Ti-5Al-4Zr-10Mo-3Cr titanium alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[2]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[3]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[4]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[5]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[6]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[7]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[8]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[9]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[10]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[11]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[12]	胡静, 陶科, 杨庆松, 李刚, 张德汉. 机械抛光后的时效工艺对0Cr25Al5电热合金拉拔性能的影响[J]. 金属热处理, 2022, 47(4): 171-177.
[13]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[14]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[15]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.