doi:10.13251/j.issn.0254-6051.2022.02.021

金属热处理 ›› 2022, Vol. 47 ›› Issue (2): 119-124.DOI: 10.13251/j.issn.0254-6051.2022.02.021

感应淬火对42CrMo钢曲轴连杆轴颈组织性能的影响

吴辉¹, 林升垚², 李新凯¹, 龚玉辉¹, 魏德强¹

1.桂林电子科技大学机电工程学院, 广西桂林 541004;
2.桂林福达股份有限公司, 广西桂林 541199

收稿日期:2021-10-15 修回日期:2021-12-17 出版日期:2022-02-25 发布日期:2022-04-01
通讯作者: 魏德强,教授,硕导,E-mail:wdq@quet.edu.cn
作者简介:吴辉(1994—),男,硕士研究生,主要研究方向为金属材料表面改性,E-mail:huiy8534520@163.com。
基金资助:
国家自然科学基金(51665009);广西高校中青年教师基础能力提升项目(2020KY05026);广西自然科学基金(2017GXNSFDA198007,2020JJB160001)

Effect of induction hardening on microstructure and properties of 42CrMo steel crankshaft connecting rod journal

Wu Hui¹, Lin Shengyao², Li Xinkai¹, Gong Yuhui¹, Wei Deqiang¹

1. School of Mechanical and Electrical Engineering, Guilin University of Electronic Technology, Guilin Guangxi 541004, China;
2. Guilin Fuda Co., Ltd., Guilin Guangxi 541199, China

Received:2021-10-15 Revised:2021-12-17 Online:2022-02-25 Published:2022-04-01

摘要/Abstract

摘要： 采用OM、SEM、X射线应力分析、力学性能测试等手段,分析了感应淬火处理对42CrMo钢曲轴连杆轴颈截面组织和残余应力的影响,探讨了不同淬火功率对淬硬层形貌、显微组织和力学性能的影响。结果表明,42CrMo钢曲轴连杆轴颈截面由淬硬层、过渡层和基体3部分组成,淬硬层组织为均匀细小的马氏体,过渡层组织为马氏体和回火索氏体的混合组织,基体组织为回火索氏体。经感应淬火处理,42CrMo钢曲轴连杆轴颈表面残余应力由拉应力变为压应力,随着感应淬火功率的增加,淬硬层深度增加,组织不断细化,当感应淬火功率为2500 W,组织最为均匀细小,表面硬度达到了751.3 HV0.1,耐磨性大幅提升;但是淬火功率过高会导致组织粗化,当感应淬火功率为2600 W时,组织有所粗化,硬度也有所降低。

关键词: 42CrMo钢曲轴连杆轴颈, 感应淬火, 显微组织, 力学性能

Abstract: Effect of induction hardening treatment on sectional microstructure and residual stress of the 42CrMo steel crankshaft connecting rod journal was analyzed by means of OM, SEM, X-ray stress analysis and mechanical property test. The effect of quenching power on morphology, microstructure and mechanical properties of the hardened layer was discussed. The results show that the 42CrMo steel crankshaft connecting rod journal is composed of three parts: the hardened layer, the transition layer and the matrix. The microstructure of the hardened layer is uniform and fine martensite, the transition layer is a mixture of martensite and tempered sorbite, and the matrix is tempered sorbite. After induction hardening, the surface residual stress of the 42CrMo steel crankshaft connecting rod journal changes from tensile stress to compressive stress. With the increase of induction hardening power, the depth of hardened layer increases and the microstructure is refined continuously. When the quenching power is 2500 W, the microstructure is the most uniform and fine, the surface hardness reaches 751.3 HV0.1, and the wear resistance is greatly improved. However, too high induction hardening power will lead to microstructure coarsening. When the induction hardening power is 2600 W, the microstructure is coarsened and the hardness is reduced.

Key words: 42CrMo steel crankshaft connecting rod journal, induction hardening, microstructure, mechanical properties

中图分类号:

吴辉, 林升垚, 李新凯, 龚玉辉, 魏德强. 感应淬火对42CrMo钢曲轴连杆轴颈组织性能的影响[J]. 金属热处理, 2022, 47(2): 119-124.

Wu Hui, Lin Shengyao, Li Xinkai, Gong Yuhui, Wei Deqiang. Effect of induction hardening on microstructure and properties of 42CrMo steel crankshaft connecting rod journal[J]. Heat Treatment of Metals, 2022, 47(2): 119-124.

参考文献

[1]Qin W J, Dong C, Li X. Assessment ofbending fatigue strength of crankshaft sections with consideration of quenching residual stress[J]. Journal of Materials Engineering and Performance, 2016, 25(3): 938-947.
[2]陈浩, 秦训鹏, 汪舟, 等. 三维点式感应淬火电磁热耦合场数值模拟[J]. 中国表面工程, 2013, 26(1): 79-85.
Chen Hao, Qin Xunpeng, Wang Zhou, et al. Finite element analysis of coupled electromagnetic thermal field for 3D spot induction hardening[J]. China Surface Engineering, 2013, 26(1): 79-85.
[3]张沈洁, 李瑞卿, 孔春花, 等. 42CrMo钢驱动轮轴的感应热处理[J]. 金属热处理, 2016, 41(1): 43-47.
Zhang Shenjie, Li Ruiqing, Kong Chunhua, et al. Induction hardening of 42CrMo steel driving axle[J]. Heat Treatment of Metals, 2016, 41(1): 43-47.
[4]Gao K, Qin X, Wang Z, et al. Effect of spot continual induction hardening on the microstructure of steels: Comparison between AISI 1045 and 5140 steels[J]. Materials Science and Engineering A, 2016, 651: 535-547.
[5]Kim M, Shin J, Choi Y, et al. Improvement of mechanical properties of spheroidized 1045 steel by induction heat treatment[J]. Metallurgical and Materials Transactions A, 2016, 47(4): 1761-1769.
[6]梁耀, 于晓华, 种晓宇, 等. 淬火温度对轧辊用高硼铁基合金组织和力学性能的影响[J]. 金属热处理, 2020, 45(8): 86-91.
Liang Yao, Yu Xiaohua, Chong Xiaoyu, et al. Effect of quenching temperature on microstructure and mechanical properties of high-boron Fe-based alloy for roll[J]. Heat Treatment of Metals, 2020, 45(8): 86-91.
[7]Lin C. Corrosion resistance and mechanical property enhancement of SPCC steel using an induction heat treatment[J]. International Journal of Electrochemical Science, 2017, 12(9): 7965-7976.
[8]周磊, 李启鹏, 薛德志, 等. LY2铝合金的激光冲击强化区硬度和残余应力测试分析[J]. 航空精密制造技术, 2010, 46(1): 43-45.
Zhou Lei, Li Qipeng, Xue Dezhi, et al. Measurement and analysis of hardness and residual stress for laser shock processing field of aluminum alloy LY2[J]. Aviation Precision Manufacturing Technology, 2010, 46(1): 43-45.
[9]孙渊, 张栋, 午丽娟, 等. 材料残余应力对硬度测试影响程度的分析[J]. 华东理工大学学报(自然科学版), 2012, 38(5): 652-656.
Sun Yuan, Zhang Dong, Wu Lijuan, et al. Influence of residual stress on indentation hardness[J]. Journal of East China University of Science and Technology, 2012, 38(5): 652-656.
[10]王荣, 钟盛, 胡超凡, 等. 曲轴感应淬火及残余应力的仿真与试验研究[J]. 热加工工艺, 2018, 47(2): 231-236.
Wang Rong, Zhong Sheng, Hu Chaofan, et al. Simulation and experimental study on induction hardening and residual stress of crankshaft[J]. Hot Working Technology, 2018, 47(2): 231-236.
[11]方华, 高峥, 袁兆成, 等. 曲轴中频感应淬火过程模拟及残余应力计算[J]. 汽车工程, 2004(3): 354-358.
Fang Hua, Gao Zheng, Yuan Zhaocheng, et al. Numerical simulation on medium-frequency induction hardening and calculation of residual stress of crankshaft[J]. Automotive Engineering, 2004(3): 354-358.
[12]Jung M, Kang M, Woo W, et al. Evaluations of stress-free lattice spacings and residual stresses in a quenched carbon steel cylinder using neutron diffraction[J]. Materials Science and Engineering A, 2013, 565: 392-395.
[13]黄惠茹, 李晓阳, 张琳琳, 等. 淬火低碳钢硬度、残余应力和微观组织间的关系[J]. 科学技术与工程, 2017, 17(34): 191-196.
Huang Huiru, Li Xiaoyang, Zhang Linlin, et al. Relationship among hardness, residual stress and microstructure of quenching low-carbon steel[J]. Science Technology and Engineering, 2017, 17(34): 191-196.
[14]陈明伟, 侯增寿. 淬冷过程瞬态温度场有限元分析及淬硬层深度预测[J]. 太原工业大学学报, 1994(4): 14-20.
Chen Mingwei, Hou Zengshou. Analysis of transient temperature fields during quenching by FEM and prediction of hardened depth[J]. Journal of Taiyuan University of Technology, 1994(4): 14-20.
[15]赵正阳, 姜含, 郭博静, 等. 感应淬火硬化层深度的预测方法及其精度探讨[J]. 金属热处理, 2017, 42(3): 159-164.
Zhao Zhengyang, Jiang Han, Guo Bojing, et al. Prediction method and its precision discussion for hardened layer depth of induction quenching[J]. Heat Treatment of Metals, 2017, 42(3): 159-164.

感应淬火对42CrMo钢曲轴连杆轴颈组织性能的影响

Effect of induction hardening on microstructure and properties of 42CrMo steel crankshaft connecting rod journal

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[3]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[4]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[5]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[6]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[7]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[8]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[9]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[10]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[11]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[12]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[13]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[14]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[15]	陈强, 陈林芳, 杨明华. 18CrNiMo7-6钢的可控气氛高温渗碳工艺[J]. 金属热处理, 2022, 47(4): 231-239.