添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响

doi:10.13251/j.issn.0254-6051.2022.04.003

金属热处理 ›› 2022, Vol. 47 ›› Issue (4): 17-23.DOI: 10.13251/j.issn.0254-6051.2022.04.003

添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响

梁恩溥¹, 徐乐¹, 杨勇², 王毛球¹

1.钢铁研究总院有限公司特殊钢研究院, 北京 100081;
2.重庆长安望江工业集团有限公司, 重庆 404135

收稿日期:2022-01-16 修回日期:2022-02-17 出版日期:2022-04-25 发布日期:2022-05-19
通讯作者: 徐乐,教授,硕士生导师,E-mail:xule@nercast.com
作者简介:梁恩溥(1996—),男,硕士研究生,主要研究方向为高强度马氏体钢的开发和氢脆敏感性,E-mail:liangenpu24@163.com。
基金资助:
农机装备材料生产应用示范平台(TC200H01X/05)

Effects of Al and Cu additions on microstructure and mechanical properties of 40CrNi3MoV steel

Liang Enpu¹, Xu Le¹, Yang Yong², Wang Maoqiu¹

1. Research Institute of Special Steels, Central Iron and Steel Research Institute Co., Ltd., Beijing 100081, China;
2. Chongqing Chang'an Wangjiang Industry Group Co., Ltd., Chongqing 404135, China

Received:2022-01-16 Revised:2022-02-17 Online:2022-04-25 Published:2022-05-19

摘要/Abstract

摘要： 利用OM、SEM、TEM以及力学性能测试等表征手段研究了添加Al、Cu的40CrNi3MoV钢在900 ℃油冷淬火及450~650 ℃回火后的显微组织和力学性能的变化规律。结果表明,试验钢经淬火+回火后的显微组织主要为回火索氏体,同时析出了纳米级NiAl-Cu析出相,最佳回火温度区间为500~550 ℃。由于基体中析出纳米尺度B2结构的NiAl析出相,对添加Al的试验钢中微裂纹的扩展有较强的阻碍作用, 500~550 ℃回火时抗拉强度最高增幅达200 MPa;进一步添加Cu后,富Cu相和位错的相互作用使得试验钢的屈服强度提高了150 MPa。500 ℃回火时抗拉强度为1706 MPa,屈服强度为1505 MPa,试验钢的拉伸和冲击断口呈现出典型的解理断裂特征,有明显的撕裂棱。

关键词: 40CrNi3MoV钢, NiAl-Cu纳米复合析出, 回火温度, 力学性能, 显微组织

Abstract: Change of microstructure and mechanical properties of 40CrNi3MoV steel with Al and Cu additions after oil quenched at 900 ℃ and then tempering at 450-650 ℃ was studied by OM, SEM, TEM and mechanical properties test. The results show that the microstructure of the tested steel after quenching and tempering is mainly tempered sorbite with nano-scale NiAl-Cu precipitates and the range of optimal tempering temperature is 500-550 ℃. The precipitation of NiAl precipitates with nano-scale B2 structure in the matrix has a strong hindering effect on the propagation of micro-cracks in the tested steel with Al addition, and the resulted maximum increase of tensile strength of the steel is 200 MPa. While after further addition of Cu, the yield strength increment of the tested steel is 150 MPa due to the interaction of the Cu-rich phase and dislocations. In such state, the tested steel owns tensile strength and yield strength of 1706 MPa and 1505 MPa respectively, and its tensile and impact fractures show typical cleavage fracture characteristics with obvious tearing edges.

Key words: 40CrNi3MoV steel, NiAl-Cu nanocomposite precipitation, tempering temperature, mechanical properties, microstructure

中图分类号:

TG142

梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.

Liang Enpu, Xu Le, Yang Yong, Wang Maoqiu. Effects of Al and Cu additions on microstructure and mechanical properties of 40CrNi3MoV steel[J]. Heat Treatment of Metals, 2022, 47(4): 17-23.

参考文献

[1]刘燕, 王毛球, 刘国权. 回火温度对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2014, 39(6): 41-45.
Liu Yan, Wang Maoqiu, Liu Guoquan. Effect of tempering temperature on microstructure and mechanical properties of 40CrNi3MoV steel[J]. Heat Treatment of Metals, 2014, 39(6): 41-45.
[2]王小龙, 王毛球, 孟彬, 等. 回火工艺对Cr-Ni-Mo-V高强钢组织和力学性能的影响[J]. 金属热处理, 2017, 42(12): 135-140.
Wang Xiaolong, Wang Maoqiu, Meng Bin, et al. Effect of tempering process on microstructure and mechanical properties of Cr-Ni-Mo-V high strength steel[J]. Heat Treatment of Metals, 2017, 42(12): 135-140.
[3]王毛球, 董瀚, 王琪, 等. 高强度炮钢的组织和力学性能[J]. 兵器材料科学与工程, 2003, 26(2): 7-10.
Wang Maoqiu, Dong Han, Wang Qi, et al. Microstructure and mechanical properties of high strength gun steel[J]. Ordnance Materials Science and Engineering, 2003, 26(2): 7-10.
[4]邹伟龙, 王毛球, 时捷, 等. 热处理对25CrNi3MoV钢组织与力学性能的影响[J]. 金属热处理, 2008, 33(7): 69-72.
Zou Weilong, Wang Maoqiu, Shi Jie, et al. Influence of heat treatment on microstructure and mechanical properties of 25CrNi3MoV steel[J]. Heat Treatment of Metals, 2008, 33 (7): 69-72.
[5]张楠, 吕超然, 徐乐. 火炮身管用钢现状及发展趋势[J]. 中国冶金, 2019, 29(5): 6-9.
Zhang Nan, Lu Chaoran, Xu Le. Current status and development trend of gun barrel steel[J]. China Metallurgy, 2019, 29(5): 6-9.
[6]罗海文, 沈国慧. 超高强高韧化钢的研究进展和展望[J]. 金属学报, 2020, 56(4): 494-512.
Luo Haiwen, Shen Guohui. Progress and perspective of ultra-high strength steels having high toughness[J]. Acta Metallurgica Sinica, 2020, 56(4): 494-512.
[7]Millán J, Sandlöbes S, Al-Zubi A, et al. Designing Heusler nanoprecipitates by elastic misfit stabilization in Fe-Mn maraging steels[J]. Acta Materialia, 2014, 76: 94-105.
[8]杜瑜宾, 张守清, 胡小锋, 等. 含1.4%Cu的HSLA钢的组织和力学性能[J]. 金属学报, 2020, 56(10): 1343-1354.
Du Yubin, Zhang Shouqing, Hu Xiaofeng, et al. Microstructure and mechanical properties of HSLA steel containing 1.4% Cu[J]. Acta Metallurgica Sinica, 2020, 56 (10): 1343-1354.
[9]Kapoor M, Isheim D, Ghosh G, et al. Aging characteristics and mechanical properties of 1600 MPa body-centered cubic Cu and B2-NiAl precipitation-strengthened ferritic steel[J]. Acta Materialia, 2014, 73: 56-74.
[10]沈琴. 钢中富Cu相和NiAl相复合析出机制的研究[D]. 上海: 上海大学, 2018.
Shen Qin. Co-precipitation mechanisms research of Cu-rich and NiAl phases in steel[D]. Shanghai: Shanghai University, 2018.
[11]Jiao Z B, Luan J H, Miller M K, et al. Precipitation mechanism and mechanical properties of an ultra-high strength steel hardened by nanoscale NiAl and Cu particles[J]. Acta Materialia, 2015, 97: 58-67.
[12]韩永强, 王宇斌, 陈旋, 等. 三维原子探针表征10Ni3MnCuAl钢时效过程中析出相NiAl和Cu的变化规律[J]. 材料导报, 2019, 33(24): 4136-4140.
Han Yongqiang, Wang Yubin, Chen Xuan, et al. Characterization of NiAl and Cu precipitates in 10Ni3MnCuAl steel by three dimensional atomic probe during aging[J]. Materials Reports, 2019, 33(24): 4136-4140.
[13]Xu S S, Liu Y W, Zhang Y, et al. Precipitation kinetics and mechanical properties of nanostructured steels with Mo additions[J]. Materials Research Letters, 2020, 8(5): 187-194.
[14]Zhou B C, Yang T, Zhou G, et al. Mechanisms for suppressing discontinuous precipitation and improving mechanical properties of NiAl-strengthened steels through nanoscale Cu partitioning[J]. Acta Materialia, 2021, 205: 116561.

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[3]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[4]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[5]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[6]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[7]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[8]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[9]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[10]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[11]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[12]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[13]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[14]	陈强, 陈林芳, 杨明华. 18CrNiMo7-6钢的可控气氛高温渗碳工艺[J]. 金属热处理, 2022, 47(4): 231-239.
[15]	刘乃瑜, 曹磊, 郑少梅. 不同沉积温度下CrCN涂层的力学性能[J]. 金属热处理, 2022, 47(4): 240-244.

添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响

Effects of Al and Cu additions on microstructure and mechanical properties of 40CrNi3MoV steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价