复合化学热处理对G13Cr4Mo4Ni4V钢组织和硬度的影响

doi:10.13251/j.issn.0254-6051.2022.04.039

金属热处理 ›› 2022, Vol. 47 ›› Issue (4): 226-230.DOI: 10.13251/j.issn.0254-6051.2022.04.039

复合化学热处理对G13Cr4Mo4Ni4V钢组织和硬度的影响

苏勇¹, 王帅¹, 王吉星¹, 于兴福², 刘洪秀², 刘金玲³

1.沈阳化工大学机械与动力工程学院, 辽宁沈阳 110142;
2.沈阳工业大学机械工程学院, 辽宁沈阳 110870;
3.中国航发哈尔滨轴承有限公司, 黑龙江哈尔滨 150500

收稿日期:2021-10-18 修回日期:2022-01-10 出版日期:2022-04-25 发布日期:2022-05-19
通讯作者: 于兴福,副教授,博士, E-mail:yuxingfu@163.com
作者简介:苏勇(1979—),男,副教授,博士,主要研究方向为航空轴承用钢的热处理,E-mail:suyong_1979@126.com。
基金资助:
辽宁省教育厅项目(LJ2019014)

Effect of compound chemical heat treatment on microstructure and hardness of G13Cr4Mo4Ni4V steel

Su Yong¹, Wang Shuai¹, Wang Jixing¹, Yu Xingfu², Liu Hongxiu², Liu Jinling³

1. School of Mechanical and Power Engineering, Shenyang University of Chemical Technology, Shenyang Liaoning 110142, China;
2. School of Mechanical Engineering, Shenyang University of Technology, Shenyang Liaoning 110870, China;
3. AECC Harbin Bearing Co., Ltd., Harbin Heilongjiang 150500, China

Received:2021-10-18 Revised:2022-01-10 Online:2022-04-25 Published:2022-05-19

摘要/Abstract

摘要： 采用扫描电镜、洛氏硬度计和维氏显微硬度计研究了渗氮140 h对渗碳+淬火+回火G13Cr4Mo4Ni4V钢微观组织及硬度的影响。结果表明,渗碳+淬火+回火后G13Cr4Mo4Ni4V钢有效渗碳层深度为1.45 mm,渗碳层最高硬度为785 HV,心部硬度为420 HV,经渗氮处理后有效渗碳+渗氮层深度降为1.34 mm,渗氮层深度为0.22 mm,渗氮层最高硬度可达到948 HV,心部硬度为451 HV,较未渗氮试样硬度略有提高。渗碳+淬火+回火和添加渗氮处理后G13Cr4Mo4Ni4V钢的表面洛氏硬度相当,均在62~65 HRC 之间,但渗氮处理后试样的硬度波动性较大。添加140 h渗氮的渗碳+淬火+回火后G13Cr4Mo4Ni4V钢实现了“表面硬心部韧”的目标,渗氮层深度满足工程需要,但添加渗氮处理后G13Cr4Mo4Ni4V钢在渗碳层和渗氮层出现类网状碳化物,因此在渗氮过程中需要综合考虑渗氮层深度和微观组织,以获得良好的综合力学性能。

关键词: 航空轴承钢, 复合化学热处理, 硬度, 碳化物, G13Cr4Mo4Ni4V钢

Abstract: Effect of 140 h nitriding on the microstructure and hardness of carburized+quenched+tempered G13Cr4Mo4Ni4V steel was studied by using SEM, Rockwell hardness tester and Vickers microhardness tester. The results show that the depth of the effective carburized layer of G13Cr4Mo4Ni4V steel after carburizing+quenching+tempering is 1.45 mm, the highest hardness of the carburized layer is 785 HV, and the hardness of the core is 420 HV. The depth of the effective carburized and nitrided layer after nitriding treatment is reduced to 1.34 mm, the depth of nitrided layer is 0.22 mm, the highest hardness of the nitrided and nitrided layer can reach 948 HV, and the hardness of the core is 451 HV. Nitriding does not significantly improve the hardness of the core of the specimen. The surface Rockwell hardness of the G13Cr4Mo4Ni4V steel after carburizing+quenching+tempering and after nitriding treatment is similar, which is between 62 and 65 HRC, but the hardness of the specimen after nitriding treatment fluctuates relatively larger. The 140 h nitriding of carburized+quenched+tempered G13Cr4Mo4Ni4V steel achieves the goal of “hard surface and tough core”. The depth of the nitrided layer meets the engineering needs, but the network-like carbonization appears in the carburized and nitrided layer of the steel after nitriding treatment, so in the nitriding process, it is necessary to comprehensively consider the depth and microstructure of the nitriding layer to obtain good comprehensive mechanical properties.

Key words: aviation bearing steel, compound chemical heat treatment, hardness, carbides, G13Cr4Mo4Ni4V steel

中图分类号:

TG156

苏勇, 王帅, 王吉星, 于兴福, 刘洪秀, 刘金玲. 复合化学热处理对G13Cr4Mo4Ni4V钢组织和硬度的影响[J]. 金属热处理, 2022, 47(4): 226-230.

Su Yong, Wang Shuai, Wang Jixing, Yu Xingfu, Liu Hongxiu, Liu Jinling. Effect of compound chemical heat treatment on microstructure and hardness of G13Cr4Mo4Ni4V steel[J]. Heat Treatment of Metals, 2022, 47(4): 226-230.

参考文献

[1]朱祖昌, 杨弋涛. 第一代、第二代和第三代轴承钢及其热处理技术的研究进展(一)[J]. 热处理技术与装备, 2018, 39(6): 70-76.
Zhu Zuchang, Yang Yitao. Investigative advancement in first, Second and third generational bearing steel and heat treatment technics(I)[J]. Heat Treatment Technology and Equipment, 2018, 39(6): 70-76.
[2]刘洪秀, 于兴福, 魏英华, 等. 航空轴承钢的发展及热处理技术[J]. 航空制造技术, 2020, 63(S1): 94-101.
Liu Hongxiu, Yu Xingfu, Wei Yinghua, et al. Development of aviation bearing steel and heat treatment technology[J]. Aeronautical Manufacturing Technology, 2020, 63(S1): 94-101.
[3]娄艳芝, 罗庆洪, 李春志, 等. M50NiL高温渗碳轴承钢中Fe₂Mo析出相的电镜观察[J]. 航空材料学报, 2012, 32(4): 44-48.
Lou Yanzhi, Luo Qinghong, Li Chunzhi, et al. TEM technology to Fe₂Mo in M50NiL high temperature carburizing bearing steel[J]. Aeronautical Manufacturing Technology, 2012, 32(4): 44-48.
[4]娄艳芝, 李春志, 李旭东, 等. 渗碳M50NiL钢磨削表面完整性特征及疲劳失效机理[J]. 航空材料学报, 2017, 37(6): 25-33.
Lou Yanzhi, Li Chunzhi, Li Xudong, et al. Surface integrity characteristics and fatigue failure mechanism of carburized M50NiL steel[J]. Aeronautical Manufacturing Technology, 2017, 37(6): 25-33.
[5]Zhang F, Yang Z. Development of and perspective on high-performance nanostructured bainitic bearing steel[J]. Engineering, 2019, 5(2): 319-328.
[6]丁开勇. M50NiL钢热变形行为研究[D]. 焦作: 河南理工大学, 2016.
Ding Kaiyong. Study on hot deformation behavior of M50NiL steel[D]. Jiaozuo: Henan Polytechnic University, 2016.
[7]杨曦, 兰箭, 黄海. 加热温度及保温时间对M50NiL钢奥氏体晶粒尺寸的影响[J]. 金属热处理, 2018, 43(12): 105-109.
Yang Xi, Lan Jian, Huang Hai. Effects of heating temperature and holding time on austenite grain size of M50NiL steel[J]. Heat Treatment of Metals, 2018, 43(12): 105-109.
[8]杨雨松, 王斌. 航空轴承钢M50NiL真空低压渗碳热处理工艺研究[J]. 轧钢, 2020, 37(5): 35-38, 46.
Yang Yusong, Wang Bin. Investigation on vacuum low-pressure carburizing heat treatment process of bearing steel M50NiL for aviation engine[J]. Steel Rolling, 2020, 37(5): 35-38, 46.
[9]Chen X, Yao L, Guo J, et al. Improvement in surface properties of M50NiL steel by plasma nitriding with rare earth addition[J]. 2019, 19(5): 1420-1427.
[10]Sun Z, Zhang C S, Yan M F. Microstructure and mechanical properties of M50NiL steel plasma nitrocarburized with and without rare earths addition[J]. Materials and Design, 2014, 55: 128-136.
[11]谷臣清, 罗启文, 卢正欣. 航空发动机轴承钢高温碳氮共渗的渗层组织与性能[J]. 材料热处理学报, 1998, 19(1): 27-31.
Gu Chengqing, Luo Qiwen, Lu Zhengxin. Microstructures and mechanical properties of the carbonitrided M50NiL steel[J]. Transactions of Materials and Heat Treatment,1998, 19(1): 27-31.
[12]刘金玲, 曹娜娜, 孙东, 等. 气体成分对G13Cr4Mo4Ni4V钢渗氮层性能的影响[J]. 轴承, 2019(11): 45-48.
Liu Jinling, Cao Nana, Sun Dong, et al. Influence of gas composition on performance for nitriding layer of steel G13Cr4Mo4Ni4V[J]. Bearing, 2019(11): 45-48.
[13]毕明龙, 刘金玲, 曹娜娜, 等. 渗氮温度对G13Cr4Mo4Ni4V钢渗氮层组织和性能的影响[J]. 轴承, 2020(11): 29-33.
Bi Mingling, Liu Jinling, Cao Nana, et al. Effects of nitriding temperature on microstructure and properties of nitriding layer of G13Cr4Mo4Ni4V steel[J]. Bearing, 2020(11): 29-33.
[14]罗燕, 刘义翔, 班君, 等. 不同处理工艺轴承套圈的近表层硬度及残余应力[J]. 理化检验(物理分册), 2017, 53(7): 477-481.
Luo Yan, Liu Yixiang, Ban Jun, et al. Hardness and residual stress of near surface of bearing rings with different treatment process[J]. Physical Testing and Chemical Analysis(Part A: Physical Testing), 2017, 53(7): 477-481.
[15]郑艳华, 刘秀莲, 班君, 等. M50NiL材料复合化学热处理后残余应力的预测[J]. 轴承, 2016(12): 20-22, 27.
Zheng Yanhua, Liu Xiulian, Ban Jun, et al. Prediction for residual stress of material M50NiL after composite chemical heat treating[J]. Bearing, 2016(12): 20-22, 27.
[16]何祝根. 渗碳层深度的计算与控制[J]. 机械工人(热加工), 2007(8): 53.

复合化学热处理对G13Cr4Mo4Ni4V钢组织和硬度的影响

Effect of compound chemical heat treatment on microstructure and hardness of G13Cr4Mo4Ni4V steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王英虎, 郑淮北, 刘庭耀, 宋令玺, 白青青. 固溶处理对53Cr21Mn9Ni4N耐热钢组织及碳化物的影响[J]. 金属热处理, 2022, 47(4): 39-45.
[2]	付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.
[3]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[4]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[5]	章军, 赵四新. 冷锻齿轮用16MnCrS5钢的球化退火工艺[J]. 金属热处理, 2022, 47(4): 185-188.
[6]	戴建科, 韩顺, 厉勇, 刘宪民, 王春旭, 庞学东, 李建新. 航空齿轮钢C69高温渗碳后的组织性能[J]. 金属热处理, 2022, 47(4): 219-225.
[7]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.
[8]	孙建, 黄贞益, 李景辉, 王萍. 固溶和时效处理对Fe-Mn-Al-C轻质钢组织和硬度的影响[J]. 金属热处理, 2022, 47(3): 34-38.
[9]	杨春苗, 王珊, 王淑慧, 李延珍, 刘文文. RRA过程中预时效时间对7A85铝合金组织性能的影响[J]. 金属热处理, 2022, 47(3): 44-47.
[10]	孙国进, 郜志文, 崔效炎, 郜可坤, 孙力. 双液淬火对9Cr2Mo钢辊皮组织与硬度的影响[J]. 金属热处理, 2022, 47(3): 88-91.
[11]	程体娟, 甘斌, 于鸿垚, 周海晶, 郭彩玉, 毕中南, 杜金辉. 固溶处理对新型镍基高温合金组织及性能的影响[J]. 金属热处理, 2022, 47(3): 107-112.
[12]	吴方俊, 邓小云, 揭晓华, 郑开宏, 骆智超. 热作模具用H13和Dievar钢的热疲劳性能[J]. 金属热处理, 2022, 47(3): 165-172.
[13]	李阔, 孙明月, 徐斌, 李殿中. 稀土H13模具钢横向冲击性能影响因素分析[J]. 金属热处理, 2022, 47(3): 181-185.
[14]	王荣, 龚玉辉, 殷学俊, 魏德强. 多道电子束扫描搭接率对40Cr钢组织与性能的影响[J]. 金属热处理, 2022, 47(3): 191-197.
[15]	周钟平, 张小娟, 白鹭, 余方印, 闵永安. T250钢离子渗氮后的组织和性能[J]. 金属热处理, 2022, 47(3): 210-214.