化学成分对316L奥氏体不锈钢组织及变形行为的影响

doi:10.13251/j.issn.0254-6051.2022.05.013

金属热处理 ›› 2022, Vol. 47 ›› Issue (5): 81-86.DOI: 10.13251/j.issn.0254-6051.2022.05.013

化学成分对316L奥氏体不锈钢组织及变形行为的影响

莫金强^1,2,3, 冯光宏¹, 徐梅^2,3, 张威^2,3, 李阳^2,3

1.钢铁研究总院有限公司冶金工艺研究所, 北京 100081;
2.先进不锈钢材料国家重点实验室, 山西太原 030003;
3.太原钢铁(集团)有限公司, 山西太原 030003

收稿日期:2022-01-12 修回日期:2022-03-12 出版日期:2022-05-25 发布日期:2022-06-16
作者简介:莫金强(1984—),男,高级工程师,博士研究生,主要研究方向为先进不锈钢设计及制造技术,E-mail: mojq@tisco.com.cn
基金资助:
山西省科技重大专项(20191102006)

Effect of chemical composition on microstructure and deformation behavior of 316L austenitic stainless steel

Mo Jinqiang^1,2,3, Feng Guanghong¹, Xu Mei^2,3, Zhang Wei^2,3, Li Yang^2,3

1. Metallurgical Technology Institute, Central Iron and Steel Research Institute, Beijing 100081, China;
2. State Key Laboratory of Advanced Stainless Steel, Taiyuan Shanxi 030003, China;
3. Taiyuan Iron and Steel (Group) Co., Ltd., Taiyuan Shanxi 030003, China

Received:2022-01-12 Revised:2022-03-12 Online:2022-05-25 Published:2022-06-16

摘要/Abstract

摘要： 利用万能试验机对不同镍当量(Nieq)的316L不锈钢热轧钢板进行常温单轴拉伸试验,借助扫描电镜(SEM)和透射电镜(TEM)对其拉伸变形前后的微观组织进行观察,探索镍当量对316L不锈钢微观组织及性能的影响规律。结果表明,固溶态试验钢的组织均为奥氏体组织及少量高温δ相,强度随Nieq的升高而降低,塑性和韧性随Nieq升高而增加;拉伸断口均呈韧性断裂特征,且随Nieq的提高,韧窝的数量减少,韧窝尺寸增加;TEM显示,变形后的试验钢均未发生马氏体相变,Nieq较低时,变形量大的地方位错密度高,发生位错交互作用,局部有形变孪晶生成,且随着Nieq的增加,形变孪晶密度增大,出现相互交叉、阻滞。

关键词: 316L奥氏体不锈钢, 拉伸性能, 断口形貌, 显微组织, 形变孪晶

Abstract: Room temperature uniaxial tensile test was carried out by universal testing machine for hot-rolled 316L stainless steel plate with different nickel equivalents, then microstructure of the steel before and after the tensile deformation was observed by scanning electron microscope (SEM) and transmission electron microscope(TEM), and the effect of nickel equivalent(Nieq) on microstructure and properties of 316L stainless steel was explored. The results show that the microstructure at solid solution state is austenite and a small amocmt of high temperature δ phase, the strength decreases with the increase of Nieq, and the plasticity and toughness increase with the increase of Nieq. The tensile fracture is characterized by ductile fracture, and with the increase of Nieq, the number of dimples decreases while the size of dimples increases. The TEM observation shows that no martensitic transformation occurs in the deformed tested steel, when the Nieq is low, the dislocation density in the place with large deformation is high, dislocation interaction occurs, and deformation twins are formed locally. With the increase of Nieq, the density of deformation twin increases, and resulting in crossing and hysteresis.

Key words: 316L austenitic stainless steel, tensile properties, fracture morphology, microstructure, deformation twins

中图分类号:

TG142.1

莫金强, 冯光宏, 徐梅, 张威, 李阳. 化学成分对316L奥氏体不锈钢组织及变形行为的影响[J]. 金属热处理, 2022, 47(5): 81-86.

Mo Jinqiang, Feng Guanghong, Xu Mei, Zhang Wei, Li Yang. Effect of chemical composition on microstructure and deformation behavior of 316L austenitic stainless steel[J]. Heat Treatment of Metals, 2022, 47(5): 81-86.

参考文献

[1]孙宝壮, 周霄骋, 李晓荣, 等. 不同组织的316L不锈钢在NH₄Cl环境下应力腐蚀行为与机理[J]. 中国腐蚀与防护学报, 2021, 41(6): 811-818.
Sun Baozhuang, Zhou Xiaocheng, Li Xiaorong, et al. Stress corrosion cracking behavior of 316L stainless steel with varying microstructure in ammonium chloride environment[J]. Journal of Chinese Society for Corrosion and Protection, 2021, 41(6): 811-818.
[2]范宇恒. 不锈钢微观组织结构对其氢脆性能的影响[D]. 合肥: 中国科学技术大学, 2019.
Fan Yuheng. Effect of microstructures on the hydrogen embrittlement of stainless steels[D]. Hefei: University of Science and Technology of China, 2019.
[3]Matsuo T, Yamabe J, Matsuoka S. Effects of hydrogen on tensile properties and fracture surface morphologies of type 316L stainless steel[J]. International Journal of Hydrogen Energy, 2014, 39(7): 3542-3551.
[4]褚武杨. 氢损伤和滞后断裂[M]. 北京: 冶金工业出版社, 1988.
[5]管真, 孙永庆, 李莉, 等. 15-5PH不锈钢的氢脆敏感性[J]. 金属热处理, 2019, 44(12): 226-232.
Guan Zhen, Sun Yongqing, Li Li, et al. Hydrogen embrittlement sensitivity of 15-5PH stainless steel[J]. Heat Treatment of Metals, 2019, 44(12): 226-232.
[6]Lin J, Chen F, Liu F, et al. Hydrogen permeation behavior and hydrogen-induced defects in 316L stainless steels manufactured by additive manufacturing[J]. Materials Chemistry and Physics, 2020, 250: 123038.
[7]张慧云, 孟宪明, 郑留伟, 等. 敏化处理对不同状态304奥氏体不锈钢氢脆敏感性的影响[J]. 金属热处理, 2021, 46(8): 164-169.
Zhang Huiyun, Meng Xianming, Zheng Liuwei, et al. Effect of sensitization on hydrogen embrittlement sensitivity of 304 austenitic stainless steel in different states[J]. Heat Treatment of Metals, 2021, 46(8): 164-169.
[8]燕春光, 陈胜虎, 李雅平, 等. 氢对316H不锈钢拉伸性能的影响[J]. 钢铁研究学报, 2019(11): 1004-1011.
Yan Chunguang, Chen Shenghu, Li Yaping, et al. Influence of hydrogen on tension property of 316H stainless steel[J]. Journal of Iron and Steel Research, 2019(11): 1004-1011.
[9]Neuharth J J, Cavalli M N. Investigation of high-temperature hydrogen embrittlement of sensitized austenitic stainless steels[J]. Engineering Failure Analysis, 2015, 49: 49-56.
[10]蔡肖, 施巧英, 邢百汇, 等. 高压氢气环境中δ铁素体对304奥氏体不锈钢氢脆敏感性的影响[J]. 机械工程材料, 2019(2): 7-12.
Cai Xiao, Shi Qiaoying, Xing Baihui, et al. Effect of δ-ferrite on susceptibility to hydrogen embrittlement of 304 austenitic stainless steel in high-pressure hydrogen[J]. Materials for Mechanical Engineering, 2019(2): 7-12.
[11]Zhang L, Wen M, Masaaki I, et al. Effect of nickel equivalent on hydrogen gas embrittlement of austenitic stainless steels based on type 316 at low temperatures[J]. Acta Materialia, 2008, 56(14): 3414-3421.
[12]Zhang L, Li Z Y, Zheng J Y, et al. Influence of low temperature prestrain on hydrogen gas embrittlement of metastable austenitic stainless steels[J]. International Journal of Hydrogen Energy, 2013, 38(25): 11181-11187.
[13]余存烨. 奥氏体不锈钢氢脆[J]. 全面腐蚀控制, 2015, 29(8): 11-15.
Yu Cunye. Hydrogen environment on austenite stainless steel[J]. Total Corrosion Control, 2015, 29(8): 11-15.
[14]申勇峰, 李晓旭, 薛文颖, 等. 304不锈钢拉伸变形过程中的马氏体相变[J]. 东北大学学报(自然科学版), 2012, 33(8): 1125-1128.
Shen Yongfeng, Li Xiaoxu, Xue Wenying, et al. Changes in martensite fraction of 304SS in tensile deformation[J]. Journal of Northeastern University(Natural Science), 2012, 33(8): 1125-1128.
[15]王建华, 任立军. 高锰钢加工硬化机理研究[J]. 煤矿机械, 2003(1): 24-27.
Wang Jianhua, Ren Lijun. Research hardening austenitic steel development[J]. Coal Mine Machinery, 2003(1): 24-27.
[16]杨卓越, 苏杰, 陈嘉砚, 等. C、Cr、Ni和Mn含量对304不锈钢变形诱发马氏体相变的影响[J]. 钢铁, 2007(5): 61-64, 78.
Yang Zhuoyue, Su Jie, Chen Jiayan, et al. Effect of C, Cr, Ni and Mn content on deformation-induced martensite transformation in 304 austenitic stainless steel[J]. Iron and Steel, 2007(5): 61-64, 78.
[17]Byun T S, Lee E H, Hunn J D. Plastic deformation in 316LN stainless steel-characterization of deformation microstructures[J]. Journal of Nuclear Materials, 2003, 321(1): 29-39.
[18]Talonen J, Anninen H. Damping properties of austenitic stainless steels containing strain-induced martensite[J]. Metallurgical and Materials Transactions A, 2004, 35(8): 2401-2406.
[19]徐梅. 高屈服强度TWIP钢动态变形及其构件压溃吸能行为的研究[D]. 北京: 北京科技大学, 2018.
Xu Mei. The study of high yield strength TWIP steel on the behavior characteristics of dynamic deformation and crushing energy absorbing of its structure components[D]. Beijing: University of Science and Technology Beijing, 2018.
[20]Meyers M A, Vöhringer O, Lubarda V A. The onset of twinning in metals: A constitutive description[J]. Acta Materialia, 2001, 49(19): 4025-4039.

化学成分对316L奥氏体不锈钢组织及变形行为的影响

Effect of chemical composition on microstructure and deformation behavior of 316L austenitic stainless steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	赵思杰, 李航, 牛利冲, 李杰, 冯运莉. Al含量对热轧FeMnCoCr系高熵合金组织和性能的影响[J]. 金属热处理, 2022, 47(5): 47-52.
[2]	刘璇, 黄国平, 刘海定, 何曲波, 张楠. 固溶处理对Ni48Cr21Cu2Mo合金组织与力学性能的影响[J]. 金属热处理, 2022, 47(5): 105-110.
[3]	刘丹, 陈杰, 刘文鉴, 周文浩, 罗登, 张青学. 回火温度对Q1100超高强钢组织和性能的影响[J]. 金属热处理, 2022, 47(5): 111-117.
[4]	宿鹏吉, 麻永林, 董丽丽, 温铠, 罗家豪, 刘宝志. 磁场预退火对取向硅钢二次再结晶组织及织构的影响[J]. 金属热处理, 2022, 47(5): 131-135.
[5]	张春雨, 颜瑜, 陈贤帅, 杜如虚. 真空退火处理对选区激光熔化TA2纯钛显微组织及力学性能的影响[J]. 金属热处理, 2022, 47(5): 155-160.
[6]	张明皓, 韩颢源, 徐跃明, 李俏, 高直, 周乐育. 真空渗碳18CrNiMo7-6钢中碳化物的析出规律[J]. 金属热处理, 2022, 47(5): 171-176.
[7]	沈统, 杨丽, 李振, 冯凌宵. 渗扩时间比对AISI 316不锈钢渗氮层组织与性能的影响[J]. 金属热处理, 2022, 47(5): 183-188.
[8]	陈今良, 冯中学, 张利民, 易健宏. 冷轧变形对CrCoNi合金组织与性能的影响[J]. 金属热处理, 2022, 47(5): 204-207.
[9]	陈利超, 王长喜, 苏植成, 王宇宇, 任井涛, 李静, 邓亭, 赵莉萍. 时效工艺对WE43镁合金组织与力学性能的影响[J]. 金属热处理, 2022, 47(5): 208-212.
[10]	李照国, 潘吉祥, 纪显彬, 魏海霞, 王珂. 淬火工艺对6Cr13马氏体不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(5): 226-229.
[11]	张德勇, 冯仰峰, 李维娟, 李伟, 许继勇, 祁敏翔. 终冷温度对Q345R钢组织及性能的影响[J]. 金属热处理, 2022, 47(5): 230-233.
[12]	石如星, 林乙丑, 张沛, 齐国赛, 于文平, 苏文博. 旋回破碎机4Cr13钢主轴套激光淬火后的磨削裂纹分析[J]. 金属热处理, 2022, 47(5): 257-261.
[13]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[14]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[15]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.