真空时效加热到温时间滞后现象对FV520B钢组织及性能的影响

于晃¹, 王飞宇¹, 包翠敏¹, 王全振¹, 陈炜¹, 曲德毅¹, 蒋申柱¹, 马煜林²

1.沈阳鼓风机集团股份有限公司, 辽宁沈阳 110869;
2.沈阳大学机械工程学院, 辽宁沈阳 110044

收稿日期:2022-01-21 修回日期:2022-04-29 出版日期:2022-07-25 发布日期:2022-08-12
作者简介:于晃(1988—),男,工程师,硕士,主要研究方向为各类鼓、压风机及泵类产品零部件热处理及数值模拟分析,E-mail:403354359@qq.com
基金资助:
辽宁省自然基金博士启动项目(2019-BS-168)

Effect of heating arrival time lag on microstructure and properties of FV520B steel during vacuum aging

Yu Huang¹, Wang Feiyu¹, Bao Cuimin¹, Wang Quanzhen¹, Chen Wei¹, Qu Deyi¹, Jiang Shenzhu¹, Ma Yulin²

1. Shenyang Blower Works Group Corporation, Shenyang Liaoning 110869, China;
2. College of Mechanical Engineering, Shenyang University, Shenyang Liaoning 110044, China

Received:2022-01-21 Revised:2022-04-29 Online:2022-07-25 Published:2022-08-12

摘要/Abstract

摘要： 通过对FV520钢真空热处理温度实时跟踪,分析了不同加热温度下到温时间滞后的情况,并研究了在600 ℃时效温度下不同保温时间对显微组织及力学性能的影响。结果表明:真空炉加热到温时间滞后的现象随着加热温度的降低,滞后时间随之延长;FV520B钢在真空时效保温初期时,由于心部温度尚未达到加热设定的温度,随着保温时间的延长,显微组织发生较大转变,残留奥氏体含量增加,沉淀相逐渐析出;屈服强度随保温时间的延长而降低,冲击吸收能量随着保温时间的延长而增加;可以通过真空炉电能消耗判断工件是否均温,可用于指导热处理工艺参数的制定。

关键词: FV520钢, 真空时效, 加热到温时间, 显微组织, 力学性能

Abstract: By real-time tracing of vacuum heat treatment temperature of FV520B steel, the heating time lag at different heating temperatures was analyzed and the effect of different holding time on the microstructure and mechanical properties aging at 600 ℃ for different time was studied. The results show that the time lag of vacuum heat treatment increases with the decrease of heating temperature. In the early stage of vacuum aging of the FV520B steel, due to the time lag, the temperature in the workpiece core does not reach the set heating temperature. With the extension of the holding time, the microstructure changes greatly, the content of retained austenite increases and the precipitated phase gradually precipitates. The yield strength decreases and the impact absorbed energy increases with the prolongation of holding time. The power consumption of vacuum furnace can be used to determine whether the workpiece temperature is uniform, which can be used to guide the design of heat treatment process parameters.

Key words: FV520 steel, vacuum aging, heating arrival time, microstructure, mechanical proprieties

中图分类号:

TG156.1

于晃, 王飞宇, 包翠敏, 王全振, 陈炜, 曲德毅, 蒋申柱, 马煜林. 真空时效加热到温时间滞后现象对FV520B钢组织及性能的影响[J]. 金属热处理, 2022, 47(7): 98-101.

Yu Huang, Wang Feiyu, Bao Cuimin, Wang Quanzhen, Chen Wei, Qu Deyi, Jiang Shenzhu, Ma Yulin. Effect of heating arrival time lag on microstructure and properties of FV520B steel during vacuum aging[J]. Heat Treatment of Metals, 2022, 47(7): 98-101.

参考文献

[1]牛静, 董俊明, 薛锦, 等. 高韧性不锈钢FV520B的析出硬化行为研究[J]. 铸造技术, 2006, 27(9): 921-924.
Niu Jing, Dong Junming, Xue Jin, et al. Study on precipitation-hardening behavior of high toughness stainless steel FV520(B) [J]. Casting Technology, 2006, 27(9): 921-924.
[2]张善庆. 真空热处理加热滞后时间的研究[J]. 金属热处理, 2000, 13(1): 38-39.
Zhang Shanqing. Study on vacuum heat treatment thermal hysteresis time[J]. Heat Treatment of Metals, 2000, 13(1): 38-39.
[3]赵亮. FV520B钢不同时效温度的极化曲线和力学性能[J]. 热处理技术与装备, 2015, 36(2): 35-38.
Zhao Liang. Polarization curve and mechanical properties of FV520(B) steel at different aging temperatures[J]. Heat Treatment Technology and Equipment, 2015, 36(2): 35-38.
[4]肖福仁. 调整处理对FV520(B)不锈钢组织与性能的影响[J]. 材料热处理学报, 1999, 20(4): 35-40.
Xiao Furen. Influence of intermediate treatment on microstructure and properties of stainless steel FV520(B)[J]. Transactions of Metal Heat Treatment, 1999, 20(4): 35-40.
[5]张敏, 黄晓江, 李继红, 等. 时效温度对沉淀硬化不锈钢FV520B组织及低温力学性能的影响[J]. 热加工工艺, 2010, 39(20): 149-151, 155.
Zhang Min, Huang Xiaojiang, Li Jihong, et al. Effects of aging temperature on microstructure and low temperature mechanical properties of FV520(B) steel[J]. Hot Working Technology, 2010, 39(20): 149-155.
[6]刘瑞良, 闫牧夫, 乔英杰, 等. 马氏体不锈钢及其拉伸性能[J]. 金属热处理, 2013, 38(2): 87-91.
Liu Ruiliang, Yan Mufu, Qiao Yingjie, et al. Heat treatment and tensile properties of martensitic stainless steel[J]. Heat Treatment of Metals, 2013, 38(2): 87-91.
[7]彭良贵, 刘伟杰, 吴淑通, 等. 热处理工艺对低碳马氏体钢冲击性能的影响[J]. 金属热处理, 2014, 39(10): 1-6.
Peng Lianggui, Liu Weijie, Wu Shutong, et al. Effect of heat treatment process on impact property of low carbon martensite steel[J]. Heat Treatment of Metals, 2014, 39(10): 1-6.
[8]邓德伟, 陈蕊, 田鑫, 等. 热处理对17-4PH马氏体不锈钢显微组织及性能的影响[J]. 金属热处理, 2013, 38(4): 32-36.
Deng Dewei, Chen Rui, Tian Xin, et al. Influence of heat treatment on microstructure and properties of 17-4PH martensitic stainless steel [J]. Heat Treatment of Metals, 2013, 38(4): 32-36.

[1]	姜超, 贾东永, 周志勇, 田政, 郭星晔, 王哲, 韩修柱. 激光选区熔化高强铝合金件的热处理及空间环境性能[J]. 金属热处理, 2022, 47(7): 1-8.
[2]	童锐, 于兴福, 刘永宝, 夏云志, 苏勇, 金映丽. 轴承用8Cr4Mo4V钢真空气淬及等温盐浴淬火后的性能对比分析[J]. 金属热处理, 2022, 47(7): 9-14.
[3]	田紫维, 姚彦欣, 刘佳兴, 王智怡, 胡章权, 蒋波. 冷却速度对微合金化中碳非调质钢组织和性能的影响[J]. 金属热处理, 2022, 47(7): 27-33.
[4]	韦小园, 魏午, 郭骁, 程志强, 文胜平, 石薇, 黄晖. 退火处理对含铒Al-6Mg-1Mn铝合金组织和性能的影响[J]. 金属热处理, 2022, 47(7): 47-51.
[5]	张明军, 李远, 李相辉. 热等静压工艺对K4125镍基高温合金显微组织的影响[J]. 金属热处理, 2022, 47(7): 71-75.
[6]	王华, 王泽钰, 宋嘉明, 瞿宗宏, 赖运金, 梁书锦. 固溶处理对粉末冶金GH4099合金组织及性能的影响[J]. 金属热处理, 2022, 47(7): 86-91.
[7]	樊立峰, 亢泽, 贾丽英, 徐惠敏, 高军. 淬火后的逆相变退火温度对5%Mn冷轧中锰钢组织与性能的影响[J]. 金属热处理, 2022, 47(7): 92-97.
[8]	陈波, 张继国, 华永兴, 尹树春, 吴磊, 梁振威, 孙扩. 高端车用热成形钢CR300MB的研发与应用[J]. 金属热处理, 2022, 47(7): 107-113.
[9]	付锡彬, 孟少博, 刘文胜, 张可, 李昭东, 曹燕光, 章小峰, 雍岐龙. 固溶处理对Fe-30Mn-10Al-1C低密度钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(7): 114-119.
[10]	韩俊刚, 邵志文, 宋运坤, 陈小虎, 丁博远, 顾娇娇. 热处理对针阀体用4Cr5MoSiV1钢组织及性能的影响[J]. 金属热处理, 2022, 47(7): 120-124.
[11]	殷剑, 金康, 黎诚, 董奇, 沈智, 张波. 时效处理对7022铝合金组织与弯曲性能的影响[J]. 金属热处理, 2022, 47(7): 144-150.
[12]	蒋文淼, 胡志华, 栾道成, 张旭, 凌俊华, 阴志铭, 李缘, 周新宇, 王正云. 新型贝氏体板簧钢的组织及性能[J]. 金属热处理, 2022, 47(7): 151-155.
[13]	董彦超, 马铁军, 金头男, 袁乃博, 金头男. 含铝高硼高速钢显微组织的电镜表征[J]. 金属热处理, 2022, 47(7): 177-182.
[14]	徐祺昊, 杨礼林, 夏明, 秦晨, 赵莉萍. 稀土Ce对H13钢CCT曲线的影响[J]. 金属热处理, 2022, 47(7): 197-202.
[15]	房国梁, 王茂林. 16MnCr5钢大马力柴油机凸轮轴渗碳淬火组织演变[J]. 金属热处理, 2022, 47(7): 269-271.

真空时效加热到温时间滞后现象对FV520B钢组织及性能的影响

Effect of heating arrival time lag on microstructure and properties of FV520B steel during vacuum aging

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价