均匀化处理Al-Mg-Mn合金的组织及热变形行为

doi:10.13251/j.issn.0254-6051.2022.11.005

金属热处理 ›› 2022, Vol. 47 ›› Issue (11): 32-38.DOI: 10.13251/j.issn.0254-6051.2022.11.005

均匀化处理Al-Mg-Mn合金的组织及热变形行为

马宝霞, 乔洋, 毛明轩, 孙江辉, 吴昌桐, 刘泽瑀

哈尔滨理工大学材料科学与化学工程学院, 黑龙江哈尔滨 150040

收稿日期:2022-05-20 修回日期:2022-08-28 出版日期:2022-11-25 发布日期:2023-01-04
作者简介:马宝霞(1978—),女,副教授,博士,主要研究方向为金属材料制备与热处理,E-mail:mabaoxia@126.com

Microstructure and hot deformation behavior of Al-Mg-Mn alloy after homogenization

Ma Baoxia, Qiao Yang, Mao Mingxuan, Sun Jianghui, Wu Changtong, Liu Zeyu

School of Materials Science and Chemical Engineering, Harbin University of Science and Technology, Harbin Heilongjiang 150040, China

Received:2022-05-20 Revised:2022-08-28 Online:2022-11-25 Published:2023-01-04

摘要/Abstract

摘要： 研究了半连续水冷铸造方法制备的Al-Mg-Mn合金均匀化处理过程中显微组织的演变过程,同时采用 Gleeble-1500热模拟试验机对均匀化退火态合金的高温塑性变形行为进行了研究,分析了合金流变应力与变形温度和变形量之间的关系,并对合金变形过程中显微组织变化进行了探讨。结果表明,均匀化处理后原铸态合金中粗大的非平衡析出相逐渐溶解,变细、断裂,趋于球化,呈珠链状,数量减少。在热模拟变形过程中,475 ℃×15 h 均匀化退火态Al-Mg-Mn合金流变应力随着变形温度升高而降低;随着变形量增加,流变应力的峰值增大。随着变形温度升高,合金热变形组织首先发生缓慢的回复,位错密度降低,进而形成亚晶、出现再结晶晶粒组织特征。

关键词: Al-Mg-Mn合金, 均匀化退火, 显微组织, 热变形

Abstract: Microstructure evolution of Al-Mg-Mn alloy prepared by the direct chill casting was studied during the homogenization process. The plastic deformation behavior of the alloy at high temperature was investigated by using Gleeble-1500 thermal simulation testing machine. The relationship between flow stress and deformation temperature, deformation amount of the alloy was analyzed, and the microstructure change of the alloy during deformation was also discussed. The results show that after homogenization, coarse non-equilibrium precipitates of the as-cast alloy gradually dissolve and decrease in the amount, and become fine, break, tend to spheroidize, appear as bead chains. During the thermal simulating deformation process, the flow stress of the alloy homogenization annealed at 475 ℃ for 15 h decreases with the increase of deformation temperature, and the peak value of the flow stress increases with the increase of deformation amount. As the deformation temperature rises, the hot deformed microstructure firstly recovers slowly, the dislocation density decreases, then forms sub-grains and microstructure with recrystallized grain characteristics.

Key words: Al-Mg-Mn alloy, homogenization annealing, microstructure, hot deformation

中图分类号:

TG146.2

马宝霞, 乔洋, 毛明轩, 孙江辉, 吴昌桐, 刘泽瑀. 均匀化处理Al-Mg-Mn合金的组织及热变形行为[J]. 金属热处理, 2022, 47(11): 32-38.

Ma Baoxia, Qiao Yang, Mao Mingxuan, Sun Jianghui, Wu Changtong, Liu Zeyu. Microstructure and hot deformation behavior of Al-Mg-Mn alloy after homogenization[J]. Heat Treatment of Metals, 2022, 47(11): 32-38.

参考文献

[1]Parker B A, Zhou Z F, Nolle P. The effect of small additions of scandium on the properties of aluminum alloys[J]. Journal of Materials Science, 1995, 30: 452-458.
[2]Popovic M, Romhanji E. Stress corrosion cracking susceptibility of Al-Mg alloy sheet with high Mg content[J]. Journal of Materials Processing Technology, 2002, 125-126: 275-280.
[3]王旭东, 陈龙飞. 热轧Al-Mg-Mn-Er-Zr合金板材的低温冲击性能[J]. 金属热处理, 2014, 39(12): 76-79.
Wang Xudong, Chen Longfei. Impact properties of Al-Mg-Mn-Er-Zr alloy at cryogenic temperature[J]. Heat Treatment of Metals, 2014, 39(12): 76-79.
[4]Popovic M, Romhanji E. Characterization of microstructural changes in an Al-6.8wt.%Mg alloy by electrical resistivity measurements[J]. Materials Science & Engineering A, 2008, 492: 460-467.
[5]García-Bernal M A, Mishra R S, Verma R, et al. Hot deformation behavior of friction-stir processed strip-cast 5083 aluminum alloys with different Mn contents[J]. Materials Science and Engineering A, 2012, 534: 186-192.
[6]Mondal C, Mukhopadhyay A K. On the nature of T(Al₂Mg₃Zn₃) and S(Al₂CuMg) phases present in as-cast and annealed 7055 aluminum alloy[J]. Materials Science and Engineering A, 2005, 391(1/2): 367-376.
[7]邱楚, 郭世杰, 纪艳丽. 6061 铝合金均匀化过程中 AlMnSi 弥散颗粒的析出尺寸对再结晶行为的影响[J]. 金属热处理, 2020, 45(8): 27-33.
Qiu Chu, Guo Shijie, Ji Yanli. Effect of AlMnSi dispersion particle size on recrystallization of 6061 aluminum alloy during homogenization[J]. Heat Treatment of Metals, 2020, 45(8): 27-33.
[8]Rokhlin L L, Dobatkina T V, Bochvar N R, et al. Investigation of phase equilibria in alloys of the Al-Zn-Mg-Cu-Zr-Sc system[J]. Journal of Alloys and Compounds, 2004, 367(1/2): 10-16.
[9]Morere B, Shahani R, Maurice C, et al. The influence of Al₃Zr dispersoids on the recrystallization of hot-deformed AA 7010 alloys[J]. Metallurgical and Materials Transactions A, 2001, 32(3): 625-632.
[10]孙景旺, 王渠东, 丁文江. 铸造Al-Mg-Mn合金的显微组织及力学性能[J]. 特种铸造及有色合金, 2012, 32(1): 85-89.
Sun Jingwang, Wang Qudong, Ding Wenjiang. Microstructure and tensile properties of Al-Mg-Mn alloy[J]. Special Casting and Nonferrous Alloys, 2012, 32(1): 85-89.
[11]Engler O, Liu Z, Kuhnke K. Impact of homogenization on particles in the Al-Mg-Mn alloy AA 5454-Experiment and simulation[J]. Journal of Alloys and Compounds, 2013, 560: 111-122.
[12]Mathew E V, Ramachandran T R, Gupta K P, et al. Homogenization of commercial Al-Mn alloys[J]. Journal of Materials Science Letters, 1984, 3(7): 605-610.
[13]Eivani A R, Ahmed H, Zhou J, et al. Evolution of grain boundary phases during the homogenization of AA7020 aluminum alloy[J]. Metallurgical and Materials Transactions A, 2009, 40(3): 717-728.
[14]Goswami R, Spanos G, Pao P S, et al. Precipitation behavior of the phase in Al-5083[J]. Materials Science and Engineering A, 2010, 527(4/5): 1089-1095.

[1]	高星, 张宁, 丁燕, 蒋波. 热处理时间对激光选区成形TC4钛合金组织及力学性能的影响[J]. 金属热处理, 2022, 47(9): 12-17.
[2]	潘冉, 刘宝胜, 曾元松, 曲海涛, 王东, 慕延宏. 深冷处理对15%SiC_p/2009铝基复合材料组织与力学性能的影响[J]. 金属热处理, 2022, 47(9): 65-70.
[3]	季德静, 杨维宇, 白雅琼. 高强韧工程机械用钢Q690D的淬火工艺优化[J]. 金属热处理, 2022, 47(9): 108-112.
[4]	王世凯, 王睿, 康燕, 于志强, 闫志杰. 淬火温度对Cr5MoVNi钢组织和性能的影响[J]. 金属热处理, 2022, 47(9): 125-129.
[5]	熊维亮, 梁文, 吴腾, 梁亮, 吴浩鸿. 控冷工艺对热轧双相钢组织与性能的影响[J]. 金属热处理, 2022, 47(9): 130-133.
[6]	范朝, 程宗辉, 张志强. 激光热输入对激光增材修复1Cr17Ni2不锈钢组织与力学性能的影响[J]. 金属热处理, 2022, 47(9): 140-145.
[7]	李敬, 刘辰, 杨跃辉, 苑少强, 艾晨光. 厚规格Q690D高强钢板的连续冷却转变行为[J]. 金属热处理, 2022, 47(9): 171-174.
[8]	田伟, 潘伟, 钟庆元. 0Cr16Ni5Mo马氏体不锈钢δ-铁素体含量及奥氏体晶粒度的控制[J]. 金属热处理, 2022, 47(9): 194-201.
[9]	周文浩. 高强度桥梁钢Q690q的连续冷却转变行为[J]. 金属热处理, 2022, 47(9): 202-207.
[10]	谯德高, 罗晓阳, 胡双喜, 侯园园, 张志坚, 唐兴昌. 280VK冷轧高强钢退火过程的组织演变及析出机理[J]. 金属热处理, 2022, 47(9): 220-226.
[11]	赵竞, 王丽萍, 冯义成, 姜文勇, 王雷, 郭二军. 硅含量对耐热球墨铸铁显微组织和力学性能的影响[J]. 金属热处理, 2022, 47(9): 227-233.
[12]	关蕴奇, 李亮, 胡文祥, 史正良, 徐嘉. Ni含量对淬回火态40CrNiMo钢显微组织和力学性能的影响[J]. 金属热处理, 2022, 47(9): 245-249.
[13]	张铮, 陈进磊, 张敏, 乔珺威. 热变形对塑料模具钢SDFT600贝氏体相变的影响[J]. 金属热处理, 2022, 47(8): 1-6.
[14]	何博, 彭天恩, 胡学文, 蒋波, 郭锐, 石践, 汪飞, 王海波. Nb对高Ti耐候钢连续冷却后显微组织及硬度的影响[J]. 金属热处理, 2022, 47(8): 46-51.
[15]	秦铁玉, 宋春燕, 马汝成, 张学峰, 郝威, 贵永亮. Si含量对Fe-Cr-Si系合金组织与耐蚀性能的影响[J]. 金属热处理, 2022, 47(8): 77-82.

均匀化处理Al-Mg-Mn合金的组织及热变形行为

Microstructure and hot deformation behavior of Al-Mg-Mn alloy after homogenization

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价