抛丸预处理对45钢气体渗碳效率及渗层特性的影响

doi:10.13251/j.issn.0254-6051.2022.11.025

金属热处理 ›› 2022, Vol. 47 ›› Issue (11): 143-146.DOI: 10.13251/j.issn.0254-6051.2022.11.025

抛丸预处理对45钢气体渗碳效率及渗层特性的影响

曹培, 顾晓文, 严韶云

上海上大热处理有限公司, 上海 201800

收稿日期:2022-07-18 修回日期:2022-10-03 出版日期:2022-11-25 发布日期:2023-01-04
作者简介:曹培(1993—),男,工程师,硕士,主要研究方向为金属热处理,E-mail:1581366507@qq.com

Effect of shot blasting pretreatment on gas carburizing efficiency and layer properties of 45 steel

Cao Pei, Gu Xiaowen, Yan Shaoyun

Shanghai University Heat-treatment Co., Ltd., Shanghai 201800, China

Received:2022-07-18 Revised:2022-10-03 Online:2022-11-25 Published:2023-01-04

摘要/Abstract

摘要： 采用光学显微镜、显微硬度计等方法研究了抛丸预处理对45钢气体渗碳效率及渗层特性的影响。结果表明,在相同气体渗碳工艺情况下,抛丸预处理对45钢气体渗碳有明显促进作用,抛丸预处理渗碳试样有效硬化层由0.994 mm增加到1.486 mm,渗碳效率提升39%以上,表面硬度提高10%以上。相较于未抛丸渗碳试样,抛丸预处理使渗碳试样截面梯度硬度升高且由表及里下降更为平缓,降低渗碳层脆性。

关键词: 45钢, 抛丸处理, 渗碳效率, 显微硬度

Abstract: Effect of shot blasting pretreatment on gas carburizing efficiency and layer properties of 45 steel was studied by means of optical microscope and microhardness tester. The results show that under the same gas carburizing process, shot blasting pretreatment can obviously promote the gas carburizing of the 45 steel, the effective hardening layer of the pretreated carburized specimen increases from 0.994 mm to 1.486 mm, the carburizing efficiency increases by more than 39%, and the surface hardness increases by more than 10%. Compared with the non-shot blasting carburized specimen, shot blasting pretreatment makes the gradient hardness of carburized specimen section increase and decrease more gently from the outside to the inside, reducing the brittleness of carburized layer.

Key words: 45 steel, shot blasting, carburizing efficiency, microhardness

中图分类号:

TG156.8

曹培, 顾晓文, 严韶云. 抛丸预处理对45钢气体渗碳效率及渗层特性的影响[J]. 金属热处理, 2022, 47(11): 143-146.

Cao Pei, Gu Xiaowen, Yan Shaoyun. Effect of shot blasting pretreatment on gas carburizing efficiency and layer properties of 45 steel[J]. Heat Treatment of Metals, 2022, 47(11): 143-146.

参考文献

[1]Wang F F, Zhou C, Zheng L, et al. Improvement of the corrosion and tribological properties of CSS-42L aerospace bearing steel using carbon ion implantation[J]. Applied Surface Science, 2017(392): 305-311.
[2]Zhang S, Wang W, Zhang H, et al. The effect of hardness distribution by carburizing on the elastic-plastic contact performance[J]. Tribology International, 2016(100): 24-34.
[3]Song L, Gu X M, Sun F, et al. Reduced internal oxidation by a rapid carburizing technology enhanced by pre-oxidation for 18CrNiM07-6 gear steel[J]. Vacuum, 2019(160): 210-212.
[4]Xie F, Hu J, Zhou Z H, et al. Effects of direct current field on powder pack aluminizing[J]. Surface Engineering, 2011, 27(2): 134-138.
[5]李远睿, 潘建成, 史兴华, 等. 20钢纺织钢领无毒盐浴C-N-RE共渗研究[J]. 钢铁研究学报, 2007, 19(3): 66-70.
Li Yuanrui, Pan Jiancheng, Shi Xinghua, et al. Nonpoisonous liquid RE-Carbonitriding for textile ring of 20 steel[J]. Journal of Iron and Steel Research, 2007, 19(3): 66-70.
[6]Li D, Wu J Q, Miao B, et al. Enhancement of wear resistance by sand blasting-assisted rapid plasma nitriding for 304 austenitic stainless steel[J]. Surface Engineering, 2020, 36(5): 524-530.
[7]Tang L, Jia W J, Hu J. An enhanced rapid plasma nitriding by laser shock peening[J]. Materials Letters, 2018, 2: 91-93.
[8]Lu K, Lu J. Nanostructured surface layer on metallic materials induced by surface mechanical attrition treatment[J]. Materials Science and Engineering A, 2004, 375/377: 38-45.
[9]王仁智. 金属材料的喷丸强化原理及其强化机理综述[J]. 中国表面工程, 2012, 25(6): 1-9.
Wang Renzhi. Overview on the shot peening principle and its strengthening mechanisms for metallic materials[J]. China Surface Engineering, 2012, 25(6): 1-9.
[10]缪小吉, 宋璐, 卢阳阳, 等. 喷砂预处理对20CrMnMo钢气体渗碳效率及渗层特性的影响[J]. 材料热处理学报, 2021, 42(5): 124-128.
Miao Xiaoji, Song Lu, Lu Yangyang, et al. Effect of sand blasting pretreatment on gas carburizing efficiency and carburized layer characteristics of 20CrMnMo steel[J]. Transactions of Materials and Heat Treatment, 2021, 42(5): 124-128.

[1]	朱德荣, 李豪, 柳翊, 王利鸽, 陈智勇, 张慧贤, 梁莉. 固溶时效对SLM成形316L不锈钢块体件显微组织及硬度的影响[J]. 金属热处理, 2022, 47(8): 237-241.
[2]	周留研, 刘利国, 马晖, 陈东旭. AZ31B镁合金盐浴碳氮钒共渗工艺[J]. 金属热处理, 2022, 47(7): 259-263.
[3]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.
[4]	梁怀南, 刘志奇, 陈东良, 宋建丽, 林乃明. 压印模具表面织构电火花成形工艺参数的分析[J]. 金属热处理, 2022, 47(3): 20-27.
[5]	周钟平, 张小娟, 白鹭, 余方印, 闵永安. T250钢离子渗氮后的组织和性能[J]. 金属热处理, 2022, 47(3): 210-214.
[6]	师佑杰, 李永刚, 李文辉, 王兴富. 深冷处理对TC4钛合金表面性能的影响[J]. 金属热处理, 2022, 47(2): 183-187.
[7]	张孟良, 汤文博, 李百奇, 王笑生, 黎文强, 王腾飞. 等离子熔覆添加和内生联合WC颗粒增强铁基涂层的组织和性能[J]. 金属热处理, 2022, 47(2): 200-204.
[8]	王皓民, 汪国庆, 熊杨凯, 江昊, 赵远涛, 方志强, 李文戈. 激光熔覆VC-Cr₇C₃复合熔覆层的组织与力学性能[J]. 金属热处理, 2022, 47(11): 245-252.
[9]	丁轩, 甘玉荣, 蒋爱娟, 李辉, 杨明球. 时效处理对7A55铝合金微观组织和性能的影响[J]. 金属热处理, 2021, 46(9): 120-123.
[10]	缪小进, 夏思海, 武美萍, 俞经虎, 赵子硕, 崔宸, 张春雷. 添加CeO₂对铝合金表面激光熔覆铝钛熔覆层性能的影响[J]. 金属热处理, 2021, 46(9): 234-240.
[11]	李海涛, 樊帅奇, 张蕾涛, 戴姣燕, 徐金富. 45钢激光氮合金化涂层的组织性能及工艺优化[J]. 金属热处理, 2021, 46(8): 209-213.
[12]	王自力, 陈荣发, 郑志伟, 何玉龙, 史敏杰, 王锴, 周晓进. 42CrMo钢活塞杆表面氧氮复合渗层的显微组织和耐磨性能[J]. 金属热处理, 2021, 46(8): 225-229.
[13]	陈滋鑫, 周后明, 徐采星, 达丽梅, 朱宇旭, 何方佳, 王泽达. 基于30CrMnSiNi2A钢的飞机起落架激光熔覆再制造工艺[J]. 金属热处理, 2021, 46(6): 45-52.
[14]	佟健博, 李雪飞, 黄利军, 张文强. 近β钛合金表面包覆渗氧强化[J]. 金属热处理, 2021, 46(6): 74-78.
[15]	苏学虎. 1Cr13不锈钢硼-碳复合渗工艺及其性能[J]. 金属热处理, 2021, 46(6): 120-125.

抛丸预处理对45钢气体渗碳效率及渗层特性的影响

Effect of shot blasting pretreatment on gas carburizing efficiency and layer properties of 45 steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价