超级奥氏体不锈钢654SMO在900 ℃下的时效析出行为

doi:10.13251/j.issn.0254-6051.2023.01.012

金属热处理 ›› 2023, Vol. 48 ›› Issue (1): 68-74.DOI: 10.13251/j.issn.0254-6051.2023.01.012

超级奥氏体不锈钢654SMO在900 ℃下的时效析出行为

赵政翔¹, 李静媛¹, 廖露海¹, 徐芳泓², 张威²

1.北京科技大学材料科学与工程学院北京材料基因工程高精尖创新中心, 北京 100083;
2.太原钢铁(集团)有限公司先进不锈钢材料国家重点实验室, 山西太原 030003

收稿日期:2022-08-22 修回日期:2022-11-07 出版日期:2023-01-25 发布日期:2023-02-03
通讯作者: 李静媛,教授,博士,E-mail:lijy@ustb.edu.cn
作者简介:赵政翔(1998—),男,硕士研究生,主要研究方向为超级奥氏体不锈钢的热塑性,E-mail:1610961688@qq.com。
基金资助:
国家自然科学基金(U1806220);山西省科技重大专项(20191102006)

Aging precipitation behavior of super austenitic stainless steel 654SMO at 900 ℃

Zhao Zhengxiang¹, Li Jingyuan¹, Liao Luhai¹, Xu Fanghong², Zhang Wei²

1. Beijing Advanced Innovation Center for Materials Genome Engineering, School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China;
2. State Key Laboratory of Advanced Stainless Steel Materials, Taiyuan Iron and Steel (Group) Co., Ltd., Taiyuan Shanxi 030003, China

Received:2022-08-22 Revised:2022-11-07 Online:2023-01-25 Published:2023-02-03

摘要/Abstract

摘要： 对超级奥氏体不锈钢654SMO在900 ℃进行不同时间的时效处理,通过扫描电镜(SEM)、透射电镜(TEM)观察了析出相的显微形貌,使用能谱分析和选区电子衍射分析了析出相的成分和结构,并结合JMA方程对析出相的析出动力学进行了研究。结果表明,超级奥氏体不锈钢654SMO中的析出相主要是σ相和Cr₂N相。时效10 min~1 h时,钢中析出相主要是σ相,σ相的析出位置依次是晶界、非共格孪晶界、共格孪晶界和晶内。时效1~12 h过程中,σ相开始在晶内形成针状相,随着时效时间的延长,析出相的数量越来越多,并在晶内相互交错,交织成网状。在时效24、48 h后,由于σ相富含Cr,以及σ相与奥氏体相晶界结构差异大,Cr₂N相以条状或不规则的块状依附在σ相上形核生长。超级奥氏体不锈钢654SMO中析出相的析出动力学方程为X=1－exp(－0.0487t^0.729)。

关键词: 超级奥氏体不锈钢, 时效, 显微组织, 析出相, 析出动力学

Abstract: Super austenitic stainless steel 654SMO was aged at 900 ℃ for different time. The microstructure of the precipitated phase was observed by scanning electron microscope (SEM) and transmission electron microscope (TEM). The composition and structure of the precipitated phase were analyzed by energy spectrum analysis and selected area electron diffraction. The precipitation kinetics was studied by JMA equation. The results show that the precipitated phases in the super austenitic stainless steel 654SMO are mainly σ phase and Cr₂N phase.During the aging process from 10 min to 1 h,the precipitated phases in the steel is mainly σ phase. The precipitation position of σ phase is grain boundary, non-coherent twin boundary, coherent twin boundary, and finally within grains in the sequence. During the aging process from 2 h to 12 h, the σ phase begin to form needle-like phase in the grain.With the prolongation of aging time, the amount of precipitated phases become more and more.In addition, they interlace with each other and form a network in the grain.After aging for 24 h and 48 h, because σ phase is rich in Cr element and the grain boundary structure is very different between σ phase and austenite phase,Cr₂N phases nucleate on the σ phases in strips or irregular chunks.The precipitation kinetics equation of precipitated phase in the steel 654SMO is X=1－exp(－0.0487t^0.729).

Key words: super austenitic stainless steel, aging, microstructure, precipitated phase, precipitation kinetics

中图分类号:

赵政翔, 李静媛, 廖露海, 徐芳泓, 张威. 超级奥氏体不锈钢654SMO在900 ℃下的时效析出行为[J]. 金属热处理, 2023, 48(1): 68-74.

Zhao Zhengxiang, Li Jingyuan, Liao Luhai, Xu Fanghong, Zhang Wei. Aging precipitation behavior of super austenitic stainless steel 654SMO at 900 ℃[J]. Heat Treatment of Metals, 2023, 48(1): 68-74.

参考文献

[1]孙长庆. 超级奥氏体不锈钢的发展, 性能与应用(上)[J]. 化工设备设计, 1999, 36(6): 38-44.
Sun Changqing. Development, performance and application of supper austenitic stainless steel(Part 1)[J]. Chemical Equipment Design, 1999, 36(6): 38-44.
[2]张树才, 姜周华, 李花兵, 等. 超级奥氏体不锈钢654SMO的研究进展[J]. 钢铁研究学报, 2019, 31(2): 132-144.
Zhang Shucai, Jiang Zhouhua, Li Huabing, et al. Research and development progress of supper austenitic stainless steel 654SMO[J]. Journal of Iron and Steel Research, 2019, 31(2): 132-144.
[3]Dou Yunpeng, Han Sike, Wang Liwei, et al. Characterization of the passive properties of 254SMO stainless steel in simulated desulfurized flue gas condensates by electrochemical analysis, XPS and ToF-SIMS[J]. Corrosion Science, 2020, 165: 108405.
[4]高建兵, 范思鹏, 张树才, 等. 新型超级奥氏体不锈钢654SMO偏析行为及均匀化工艺[J]. 钢铁, 2018, 53(8): 83-89.
Gao Jianbing, Fan Sipeng, Zhang Shucai, et al. Segregation behavior and homogenizing treatment of a new type super austenitic stainless steel 654SMO[J]. Iron and Steel, 2018, 53(8): 83-89.
[5]Lee T H, Kim S J, Jung Y C. Crystallographic details of precipitates in Fe-22Cr-21Ni-6Mo-(N) superaustenitic stainless steels aged at 900 ℃[J]. Metallurgical and Materials Transactions A, 2000, 31(7): 1713-1723.
[6]Ronald L P, Clara H, Doris M E, et al. A Short review on wrought austenitic stainless steels at high temperatures: Processing, microstructure, properties and performance[J]. Materials Research, 2007, 10(4): 453-460.
[7]Koutsoukis T, Redjamia A, Fourlaris G. Phase transformations and mechanical properties in heat treated superaustenitic stainless steels[J]. Materials Science and Engineering A, 2013, 561: 477-485.
[8]Betrabet H S, Nishimoto K, Wilde B E, et al. Electrochemical and microstructural investigation of grain boundary precipitation in AISI 304 stainless steels containing nitrogen[J]. Corrosion, 1987, 43(2): 77-84.
[9]Lo K H, Shek C H, Lai J. Recent developments in stainless steels[J]. Materials Science and Engineering R, 2009, 65(4/6): 39-104.
[10]Koutsoukis T, RedjaMia A, Fourlaris G. Characterization of precipitation sequences in superaustenitic stainless steels[J]. Solid State Phenomena, 2011, 172-174: 493-498.
[11]Zhang S, Jiang Z, Li H, et al. Precipitation behavior and phase transformation mechanism of super austenitic stainless steel S32654 during isothermal aging[J]. Materials Characterization, 2018, 137: 244-255.
[12]Lee T H, Kim S J, Takaki S. Time-temperature-precipitation characteristics of high-nitrogen austenitic Fe-18Cr-18Mn-2Mo-0.9N steel[J]. Metallurgical and Materials Transactions A, 2006, 37: 3445-3454.
[13]Zhang S C, Li H B, Jiang Z H, et al. Influence of N on precipitation behavior, associated corrosion and mechanical properties of super austenitic stainless steel S32654[J]. Journal of Materials Science and Technology, 2020, 42(7): 145-157.
[14]Heino S. Role of Mo and W during sensitization of superaustenitic stainless steel-crystallography and composition of precipitates[J]. Metallurgical and Materials Transactions A, 2000, 31(8): 1893-1905.
[15]臧华勋, 肖学山, 童潮山, 等. 新型耐蚀超级奥氏体不锈钢中的高温析出相[J]. 钢铁研究学报, 2009, 21(2): 44-47.
Zang Huaxun, Xiao Xueshan, Tong Chaoshan, et al. High temperature precipitated phases of new corrosion-resistant super austenitic-steel[J]. Journal of Iron and Steel Research, 2009, 21(2): 44-47.
[16]Koutsoukis T, Papadopoulou E G, Zormalia S, et al. Precipitation sequences in cold deformed superaustenitic stainless steels[J]. Metal Science Journal, 2010, 26(9): 1041-1048.
[17]Marin R, Combeau H, Zollinger J, et al. σ-phase formation in super austenitic stainless steel during directional solidification and subsequent phase transformations[J]. Metallurgical and Materials Transactions A, 2020, 51: 3526-3534.
[18]Easterling K E. Phase Transformations in Metals and Alloys[M]. Third Edition (Revised Reprint). Chapman & Hall, 1992.
[19]Lee T H, Kim S J, Jung Y C. Crystallographic details of precipitates in Fe-22Cr-21Ni-6Mo-(N) superaustenitic stainless steels aged at 900 ℃[J]. Metallurgical and Materials Transactions A, 2000, 31(7): 1713-1723.
[20]Vanderschaeve F, Taillard R, Foct J. Discontinuous precipitation of Cr₂N in a high nitrogen, chromium-manganese austenitic stainless steel[J]. Journal of Materials Science, 1995, 30(23): 6035-6046.
[21]Lee T H, Ha H Y, Kim S J. Precipitation of second phases in high-interstitial-alloyed austenitic steel[J]. Metallurgical and Materials Transactions A, 2011, 42(12): 3543-3548.

超级奥氏体不锈钢654SMO在900 ℃下的时效析出行为

Aging precipitation behavior of super austenitic stainless steel 654SMO at 900 ℃

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	邓煜华, 黎振华, 姚碧波, 滕宝仁, 李颢. 热处理对选区激光熔化钴铬合金组织与性能的影响[J]. 金属热处理, 2023, 48(1): 23-28.
[2]	张伟锋, 何肖飞, 尉文超, 李莉, 王毛球. Nb微合金化对Cr-Ni-Mo-V系高强钢组织及力学性能的影响[J]. 金属热处理, 2023, 48(1): 29-34.
[3]	顾海, 张捷, 孙健华, 吴国庆, 孙中刚. 激光熔化沉积2195铝锂合金微观组织演变及力学性能[J]. 金属热处理, 2023, 48(1): 52-59.
[4]	陈晶阳, 任晓冬, 张明军, 张丽辉, 汤鑫, 肖程波. 铸造镍基高温合金K439B的组织及典型性能[J]. 金属热处理, 2023, 48(1): 100-104.
[5]	吴跃. Super304H耐热钢时效过程中的奥氏体晶粒长大及力学性能[J]. 金属热处理, 2023, 48(1): 105-111.
[6]	宋少威, 董明振, 尉文超, 闫永明, 王毛球, 周芸. 17Cr2Ni2MoVNb齿轮钢中NbC析出相对晶粒长大的影响[J]. 金属热处理, 2023, 48(1): 122-126.
[7]	王文正, 马永福, 马劲红, 张桂营, 田亚强, 程新超, 李红斌, 陈连生. Q355D热轧H型钢的CCT曲线及冲击性能[J]. 金属热处理, 2023, 48(1): 127-132.
[8]	元亚莎, 汪雨昌, 王文焱, 石如星, 元莎, 张玉栋. 回火温度对55NiCrMoV7热作模具钢组织和性能的影响[J]. 金属热处理, 2023, 48(1): 133-138.
[9]	张仁珊, 张鹏, 宗晓辉, 康学勤. 时效时间对T91钢显微组织和力学性能的影响[J]. 金属热处理, 2023, 48(1): 145-148.
[10]	张家豪, 陈连生, 高天洋, 徐海卫, 韩赟, 李红斌, 田亚强. 过时效温度对连续退火制备DP1180钢组织性能的影响[J]. 金属热处理, 2023, 48(1): 149-154.
[11]	戴建科, 韩顺, 厉勇, 刘雨, 雷斯敏, 王春旭. 淬火温度对新型齿轮钢组织及力学性能的影响[J]. 金属热处理, 2023, 48(1): 163-168.
[12]	赵培林, 杨栋, 吴会亮, 刘超, 李超, 李春传, 郑力. 正火处理对建筑结构用超厚规格H型钢抗层状撕裂性能的影响[J]. 金属热处理, 2023, 48(1): 175-180.
[13]	李鸿娟, 向成功, 吴琼, 王正才. 淬火与回火工艺对42CrMo钢显微组织和奥氏体晶粒长大规律的影响[J]. 金属热处理, 2023, 48(1): 181-185.
[14]	卢晓禹, 董磊, 黄利, 刘宝志. 高磁感取向硅钢27QG090的常化退火工艺[J]. 金属热处理, 2023, 48(1): 186-189.
[15]	杨胶溪, 黄凯, 武飞宇, 孙宏波, 阳代军, 李曙光, 葛学元, 王淼辉. Mg-Gd-Y-Zr镁合金高速激光熔覆Al-Si涂层的组织与性能[J]. 金属热处理, 2023, 48(1): 217-223.