W6Mo5Cr4V2钢离子渗硫层与液体渗硫层的摩擦磨损性能对比

doi:10.13251/j.issn.0254-6051.2023.01.042

金属热处理 ›› 2023, Vol. 48 ›› Issue (1): 245-248.DOI: 10.13251/j.issn.0254-6051.2023.01.042

W6Mo5Cr4V2钢离子渗硫层与液体渗硫层的摩擦磨损性能对比

郑昭卓¹, 金虹¹, 王凡¹, 姜皓苧², 马晓锋², 马宁²

1.空军装备部驻北京地区军事代表局驻北京地区第五军事代表室, 北京 101300;
2.中国航发北京航科发动机控制系统科技有限公司, 北京 100220

收稿日期:2022-08-22 修回日期:2022-11-18 出版日期:2023-01-25 发布日期:2023-02-03
作者简介:郑昭卓(1978—),男,高级工程师,硕士,主要研究方向为航空发动机控制系统质量监督,E-mail:309517308@qq.com。

Comparison of tribological performance between ion sulfurized layer and liquid sulfurized layer of W6Mo5Cr4V2 steel

Zheng Zhaozhuo¹, Jin Hong¹, Wang Fan¹, Jiang Haoning², Ma Xiaofeng², Ma Ning²

1. No. 5 Military Representative Office in Beijing of Military Representative Bureau of Air Force Armament Department, Beijing 101300, China;
2. AECC Beijing Hangke Engine Control System Technology Co., Ltd., Beijing 100220, China

Received:2022-08-22 Revised:2022-11-18 Online:2023-01-25 Published:2023-02-03

摘要/Abstract

摘要： 采用离子渗硫和液体渗硫技术分别在W6Mo5Cr4V2钢表面制备渗硫层,采用摩擦磨损试验、磨损表面形貌测量和EDS分析了两种渗硫层的摩擦磨损性能、磨痕形貌、磨损程度和渗层S含量的变化,并通过运转考核试验,从外观、尺寸检测和微观磨损形貌综合对比了离子渗硫件和液体渗硫件的稳定性和可靠性。结果表明,离子渗硫层的摩擦因数、寿命、磨痕最大深度、磨损面积和渗层中S含量等均等同或优于液体渗硫层。运转考核试验结果表明,离子渗硫和液体渗硫均可满足工件使用需要。

关键词: 离子渗硫, 摩擦磨损性能, 液体渗硫

Abstract: Tribological performance as wear properties, wear scar morphology, wear degree and S content change of sulfurized layer on the surface of the W6Mo5Cr4V2 steel prepared by ion sulfurization and liquid sulfurization were analyzed by means of friction and wear test, wear surface morphology measurement and EDS analysis, and the stability and reliability of ion sulfurized part and liquid sulfurized part were comprehensively compared by appearance, size detection and microscopic wear morphology through operation test. The results indicate the friction coefficient, service life, maximum depth and area of wear scar and sulfur content of ion sulfurized layer are all equal to or better than those of liquid sulfurized layer. The operation test results show that both ion sulfuration and liquid sulfuration can meet the performance needs of the products.

Key words: ion sulfurization, tribological performance, liquid sulfurization

中图分类号:

TG156.84

郑昭卓, 金虹, 王凡, 姜皓苧, 马晓锋, 马宁. W6Mo5Cr4V2钢离子渗硫层与液体渗硫层的摩擦磨损性能对比[J]. 金属热处理, 2023, 48(1): 245-248.

Zheng Zhaozhuo, Jin Hong, Wang Fan, Jiang Haoning, Ma Xiaofeng, Ma Ning. Comparison of tribological performance between ion sulfurized layer and liquid sulfurized layer of W6Mo5Cr4V2 steel[J]. Heat Treatment of Metals, 2023, 48(1): 245-248.

参考文献

[1]张弋飞. 硫蒸气辉光放电合成表面润滑材料(FeS)的性能及其应用[J]. 机械工程材料, 1990(1): 38-43.
Zhang Yifei. Properties and applications of a lubricant layer of FeS by the glow discharge technology in sulphurvapour[J]. Materials for Mechanical Engineering, 1990(1): 38-43.
[2]杨显, 王静, 何川, 等. 材料表面渗硫技术的研究进展[J]. 机械工程师, 2018(8): 15-19.
Yang Xian, Wang Jing, He Chuan, et al. Research progress of material surface sulfurizing technology[J]. Mechanical Engineer, 2018(8): 15-19.
[3]石万凯, 李宁, 韩振华. 低温离子渗硫FeS涂层的摩擦学性能研究[J]. 重庆理工大学学报(自然科学), 2015, 29(9): 48-52.
Shi Wankai, Li Ning, Han Zhenhua. Research on tribological properties of sulfide layer produced by ion sulphurization[J]. Journal of Chongqing University of Technology(Natural Science), 2015, 29(9): 48-52.
[4]王海斗, 庄大明, 王昆林, 等. 低温离子渗硫层的干摩擦学性能对比研究[J]. 材料热处理学报, 2002, 23(4): 30-33, 73.
Wang Haidou, Zhuang Daming, Wang Kunlin, et al. A comparative study on wear-resistance of ion sulfide layers of different steels[J]. Transactions of Materials and Heat Treatment, 2002, 23(4): 30-33, 73.
[5]张红桃, 唐华, 陈贝贝, 等. GCr15钢渗硫层的摩擦学性能研究[J]. 润滑与密封, 2015, 40(11): 75-79.
Zhang Hongtao, Tang Hua, Chen Beibei, et al. Investigation on tribological properties of GCr15 steel with sulphurized layer[J]. Lubrication Engineering, 2015, 40(11): 75-79.
[6]王海斗, 庄大明, 王昆林, 等. 离子硫化层与热喷涂硫化层的摩擦学性能比较[J]. 材料工程, 2003(3): 14-16, 43.
Wang Haidou, Zhuang Daming, Wang Kunlin, et al. Study on tribological properties of ion sulfuration and thermal sprayed FeS solid lubrication layers[J]. Journal of Materials Engineering, 2003(3): 14-16, 43.
[7]雍青松, 马国政, 王海斗, 等. 低温离子渗硫技术的发展历程和研究应用现状[J]. 材料导报, 2016, 30(17): 115-119.
Yong Qingsong, Ma Guozheng, Wang Haidou, et al. Development and application status of low-temperature ion sulfurizing technology[J]. Materials Reports, 2016, 30(17): 115-119.

W6Mo5Cr4V2钢离子渗硫层与液体渗硫层的摩擦磨损性能对比

Comparison of tribological performance between ion sulfurized layer and liquid sulfurized layer of W6Mo5Cr4V2 steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 6

编辑推荐

Metrics

本文评价

[1]	李德, 单琼飞, 王鑫, 刘勇, 周孟, 张毅. GCr15轴承钢低温离子渗硫层的组织与耐磨性能[J]. 金属热处理, 2022, 47(12): 181-187.
[2]	刘冉, 高苑, 吴韬. Al/Si比例对TC4合金表面激光熔覆Ti-Al-Si涂层组织与摩擦性能的影响[J]. 金属热处理, 2021, 46(3): 135-139.
[3]	余国庆, 景然, 王国迪, 张曼雪, 冯甜, 解念锁. MAO电压对TC4合金氧化膜层摩擦磨损性能的影响[J]. 金属热处理, 2021, 46(11): 126-130.
[4]	田武, 戴姣燕, 鲍明东, 张丽俊, 常勇强, 王世民, 于盛旺. 高温下硅锰相的演变及其对硅锰黄铜耐磨性能的影响[J]. 金属热处理, 2020, 45(3): 15-19.
[5]	刘阳光, 许晓静, 宋振华, 汪洋, 朱亮亮, 朱劲松. 氧化镧添加剂和盐浴共渗温度对TC4钛合金硼氧共渗组织与性能的影响[J]. 金属热处理, 2020, 45(10): 180-186.
[6]	孔维欢1,2,侯惠君2,卢德宏1,韦春贝2,张玲玲2. 不同周期渗银后表面型抗菌不锈钢的组织及性能[J]. 金属热处理, 2017, 42(2): 146-151.