7A04铝合金壳体失效分析

doi:10.13251/j.issn.0254-6051.2023.04.047

金属热处理 ›› 2023, Vol. 48 ›› Issue (4): 298-302.DOI: 10.13251/j.issn.0254-6051.2023.04.047

7A04铝合金壳体失效分析

王翠英, 杨有才, 柯美武, 褚小菲, 王伟

豫西工业集团河南北方红阳机电有限公司, 河南南阳 474678

收稿日期:2022-07-18 修回日期:2022-11-22 发布日期:2023-05-27
作者简介:王翠英(1995—)，女，硕士，主要研究方向为金属热处理及科研试制，E-mail:2806757838@qq.com

Failure analysis of 7A04 aluminum alloy shell

Wang Cuiying, Yang Youcai, Ke Meiwu, Chu Xiaofei, Wang Wei

Henan North Hongyang Mechanical and Electrical Co., Ltd., Western Henan Industrial Group, Nanyang Henan 474678, China

Received:2022-07-18 Revised:2022-11-22 Published:2023-05-27

摘要/Abstract

摘要： 7A04铝合金壳体在使用过程中发生开裂失效,通过对失效件的外观、断口宏微观形貌观察,以及对失效件和库存件材质、显微组织、力学性能和表面应力等方面的测试,对壳体的开裂原因进行了分析。结果表明,失效壳体为沿纵向脆性断裂,壳体横向力学性能较低,使用过程中承受较大的工作应力是导致开裂的主要原因。

关键词: 7A04铝合金, 壳体, 开裂, 失效分析

Abstract: Cracking failure occurred in 7A04 aluminum alloy shell during service. The causes of cracking were analyzed by observing the appearance of failed part and macro and micro morphologies of fracture, testing and comparing the material, microstructure, mechanical properties and surface stress of failed parts and inventory parts. The results show that the failed shell is brittle fractured along longitudinal direction of the shell, the main cause of the cracking is that the transverse mechanical properties of the shell is relatively low, and the working stress beared by the shell is large.

Key words: 7A04 aluminum alloy, shell, cracking, failure analysis

中图分类号:

U214.8⁺2

王翠英, 杨有才, 柯美武, 褚小菲, 王伟. 7A04铝合金壳体失效分析[J]. 金属热处理, 2023, 48(4): 298-302.

Wang Cuiying, Yang Youcai, Ke Meiwu, Chu Xiaofei, Wang Wei. Failure analysis of 7A04 aluminum alloy shell[J]. Heat Treatment of Metals, 2023, 48(4): 298-302.

参考文献

[1]崔长齐, 杨丽红, 王秋菊, 等. 承受高冲击载荷铝合金薄壁件开裂的原因与预防[J]. 精密成形工程, 2013, 5(6): 11-14, 41.
Cui Changqi, Yang Lihong, Wang Qiuju, et al. Cause and prevention for crack of aluminum alloy thin-walled housing bearing high impact load[J]. Journal of Netshape Forming Engineering, 2013, 5(6): 11-14, 41.
[2]高新宇. 7A04T6铝合金厚壁管材环状裂纹分析与预防措施[J]. 铝加工, 2017(4): 54-58.
Gao Xinyu. Annular crack analysis and precautionary measures for 7A04T6 aluminum alloy pipe with thick wall[J]. Aluminium Fabrication, 2017(4): 54-58.
[3]于建民, 张治民, 王强. 高强铝合金轮辋失效分析[J]. 机械强度, 2018, 40(1): 55-60.
Yu Jianmin, Zhang Zhimin, Wang Qiang. Failure analysis of high strength aluminum alloy wheel[J]. Journal of Mechanical Strength, 2018, 40(1): 55-60.
[4]李贝贝, 王元清, 支新航, 等. 我国7×××系高强铝合金及其研究进展[J]. 建筑钢结构进展, 2021, 23(7): 1-10.
Li Beibei, Wang Yuanqing, Zhi Xinhang, et al. A review on the research of the 7××× series high strength aluminum alloys as structural material in China[J]. Progress in Steel Building Structures, 2021, 23(7): 1-10.
[5]丛福官, 赵刚, 田妮, 等. 7×××系超高强铝合金的强韧化研究进展及发展趋势[J]. 轻合金加工技术, 2012, 40(10): 23-33.
Cong Fuguan, Zhao Gang, Tian Ni, et al. Research progress and development trend of strengthening-toughening of ultra-high strength 7××× aluminum alloy[J]. Light Alloy Fabrication Technology, 2012, 40(10): 23-33.
[6]杨有才, 柯美武, 孙志刚. 7A04铝合金T6处理开裂失效分析[J]. 金属热处理, 2015, 40(4): 204-206.
Yang Youcai, Ke Meiwu, Sun Zhigang. Failure analysis of 7A04 aluminum alloy by T6 heat treatment[J]. Heat Treatment of Metals, 2015, 40(4): 204-206.
[7]杨勇彪, 张治民, 王强. 挤压7A04铝合金轮辋断裂失效分析[J]. 轻合金加工技术, 2013, 41(6): 58-62.
Yang Yongbiao, Zhang Zhimin, Wang Qiang. Fracture failure analysis of extruded 7A04 aluminum alloy wheel rim[J]. Light Alloy Fabrication Technology, 2013, 41(6): 58-62.
[8]丁慧麟, 金荣芳. 金属构件缺陷、失效分析与实例[M]. 北京: 化学工业出版社, 2020: 22-23.

[1]	李新生, 刘永超, 刘珑, 徐建, 毕京华, 刘国强, 阎怀英, 丁宁. 风电机组大型锻件淬火开裂原因分析[J]. 金属热处理, 2023, 48(3): 296-300.
[2]	刘华东, 邵百明, 黎军顽. 汽车稳定杆断裂分析[J]. 金属热处理, 2023, 48(1): 253-256.
[3]	赵全育, 梁嘉俊, 陈旭鹏, 童波, 夏国华, 严琴, 丁志敏. 42CrMo钢六角头螺栓热镀锌裂纹分析[J]. 金属热处理, 2023, 48(1): 257-260.
[4]	孙璐, 李建英, 魏焕君, 李征, 李涛, 程晓英. 超高强马氏体钢开裂失效分析[J]. 金属热处理, 2023, 48(1): 261-265.
[5]	程桥, 王军, 徐良, 田建明, 陈重毅, 麻永林. 脉冲磁场对7A04铝合金固溶工艺显微组织和力学性能的影响[J]. 金属热处理, 2022, 47(9): 60-64.
[6]	李天夫, 屈伸, 董晨, 张哲峰. 数控机床主轴轴承失效分析[J]. 金属热处理, 2022, 47(4): 258-262.
[7]	郑凯, 钟振前, 曹文全, 林双平, 刘明. 18CrNiMo7-6钢齿轮热处理后开裂失效分析[J]. 金属热处理, 2022, 47(12): 275-280.
[8]	许鸿翔, 王红伟, 蒲江涌, 赵少甫, 陈生超, 戎泽玉. 20Cr2Ni4钢渗碳淬火弧齿锥齿轮磨削烧伤的检测与分析[J]. 金属热处理, 2022, 47(11): 271-275.
[9]	吴昊, 邓想涛, 李成儒, 隋轶, 张涛, 纪汶伯, 王昭东. 耐磨钢NM400冷弯开裂分析[J]. 金属热处理, 2021, 46(9): 262-267.
[10]	史可庆, 郭甫, 安龙森, 陈云, 杜子阳, 武萌, 徐钦佩. 42CrMo4钢风电主轴的热处理工艺[J]. 金属热处理, 2021, 46(8): 201-204.
[11]	聂小龙, 高加强, 孟开仁, 王军艺, 刘新宽. 60Si2Mn弹簧钢的断裂失效分析[J]. 金属热处理, 2021, 46(8): 246-249.
[12]	赵新娥. 8418钢熔铝料桶开裂分析[J]. 金属热处理, 2021, 46(6): 236-239.
[13]	车鹏程, 邵文柱, 程义, 王硕, 徐航, 李宪爽, 谭舒平. 瞬时过热对高铬镍奥氏体钢断裂和析出相形变的影响机理[J]. 金属热处理, 2021, 46(5): 235-241.
[14]	燕友增, 张皓, 曹奇, 孟高强, 夏国锋, 徐泷. 一级行星架内孔淬火开裂原因分析[J]. 金属热处理, 2021, 46(4): 236-238.
[15]	周永强. 35CrMo钢圆柱销纵向开裂原因分析[J]. 金属热处理, 2021, 46(4): 239-242.

7A04铝合金壳体失效分析

Failure analysis of 7A04 aluminum alloy shell

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价