镍基合金Inconel 740H和617B的组织稳定性和耐蚀性对比

doi:10.13251/j.issn.0254-6051.2023.05.004

摘要/Abstract

摘要： 对镍基高温合金Inconel 740H和617B在750 ℃和780 ℃进行了5000 h的时效及模拟燃煤环境腐蚀试验。使用透射电镜(TEM)、配备能谱(EDS)的扫描电镜(SEM)等对试样表面和截面微观组织进行了分析。结果表明,时效前Inconel 740H合金晶内的γ′相约为5 nm,750 ℃和780 ℃时效后分别为70 nm和95 nm左右。617B合金时效前未观察到γ′相,时效后γ′相析出,并分别长大到100 nm和130 nm左右,说明Inconel 740H合金的组织稳定性比617B合金好。在750 ℃和780 ℃模拟燃煤环境的试验证明,Inconel 740H合金比617B合金具有更好的耐腐蚀性,617B合金目前还无法取代Inconel 740H合金。

关键词: Inconel 740H合金, 617B合金, 时效, 组织稳定性, 耐腐蚀性

Abstract: Nickel based superalloys Inconel 740H and 617B were aged at 750 ℃ and 780 ℃ for 5000 h, and then corroded in simulated coal-fired environment. The surface and cross sectional microstructures were characterized by TEM, EDS and SEM. The results show that the size of intragranular γ′ phase in the Inconel 740H alloy is about 5 nm before aging, while after aging at 750 ℃ and 780 ℃ for 5000 h, the average size of γ′ phase is about 70 nm and 95 nm, respectively. The intragranular γ′ phase in the 617B alloy is not observed before aging, while after aging, the γ′ phase is precipitated and grows to about 100 nm and 130 nm, respectively, which shows that the microstructure stability of the Inconel 740H alloy is better than that of the 617B alloy. The corrosion test results in simulating coal-fired environment at 750 ℃ and 780 ℃ show that the Inconel 740H alloy has better corrosion resistance than 617B alloy, so the 617B alloy cannot replace Inconel 740H alloy at present.

Key words: Inconel 740H alloy, 617B alloy, aging, microstructure stability, corrosion resistance

中图分类号:

TG146

侯世香, 刘燕, 刘东雨. 镍基合金Inconel 740H和617B的组织稳定性和耐蚀性对比[J]. 金属热处理, 2023, 48(5): 18-24.

Hou Shixiang, Liu Yan, Liu Dongyu. Comparison of microstructure stability and corrosion resistance of nickel based alloys Inconel 740H and 617B[J]. Heat Treatment of Metals, 2023, 48(5): 18-24.

参考文献

[1]林富生, 谢锡善, 赵双群, 等. 我国700 ℃超超临界锅炉过热器管用高温合金选材探讨[J]. 动力工程学报, 2011, 31(12): 960-968.
Lin Fusheng, Xie Xishan, Zhao Shuangqun, et al. Selection of superalloys for superheater tubes of domestic 700 ℃ A-USC boiler[J]. Journal of Chinese Society of Power Engineering, 2011, 31(12): 960-968.
[2]杨磊. 700 ℃ 超超临界电站锅炉过热器管2种候选材料的抗腐蚀性研究[D]. 北京: 华北电力大学, 2018.
Yang Lei. Comparison of high temperature corrosion of two candidate alloys of 700 ℃ ultra-supercritical boiler superheater[D]. Beijing: North China Electric Power University, 2018.
[3]张红军, 周荣灿, 侯淑芳, 等. 先进超超临界机组用Inconel 740合金的组织稳定性研究[J]. 中国电机工程学报, 2011, 31(8): 108-113.
Zhang Hongjun, Zhou Rongcan, Hou Shufang, et al. Study on microstructure stability of Inconel 740 for advanced ultra supercritical unit[J]. Proceedings of the CSEE, 2011, 31(8): 108-113.
[4]谢锡善, 赵双群, 董建新, 等. 超超临界电站用Inconel 740镍基合金的组织稳定性及其改型研究[J]. 动力工程学报, 2011, 31(8): 638-643.
Xie Xishan, Zhao Shuangqun, Dong Jianxin, et al. Structural stability and improvement of Inconel alloy 740 for ultra supercritical power plants[J]. Journal of Chinese Society of Power Engineering, 2011, 31(8): 638-643.
[5]Christoper J Cowen, Paul E Danielson, Paul D Jablonski. The microstructural evolution of Inconel alloy 740 during solution treatment, aging, and exposure at 760 ℃[J]. Journal of Materials Engineering and Performance, 2011, 20(6): 1078-1083.
[6]党莹樱, 赵新宝, 尹宏飞, 等. Inconel 740H合金750 ℃长期时效后的组织稳定性[J]. 材料工程, 2016, 44(9): 58-62.
Dang Yingying, Zhao Xinbao, Yin Hongfei, et al. Microstructure stability of Inconel 740H alloy after long term exposure at 750 ℃[J]. Journal of Materials Engineering, 2016, 44(9): 58-62.
[7]符锐, 林富生, 赵双群, 等. Inconel 740H主要强化元素对热力学平衡相析出行为的影响[J]. 动力工程学报, 2013, 33(5): 405-412.
Fu Rui, Lin Fusheng, Zhao Shuangqun, et al. Influence of strengthening elements on precipitation of thermodynamic equilibrium phase in Inconel alloy 740H[J]. Journal of Chinese Society of Power Engineering, 2013, 33(5): 405-412.
[8]Chong Y, Liu Z D, Godfrey A, et al. Microstructure evolution and mechanical properties of Inconel 740H during aging at 750 ℃[J]. Materials Science and Engineering A, 2014, 589: 153-164.
[9]郭岩, 周荣灿, 张红军, 等. 镍基合金740H的组织结构与析出相分析[J]. 中国电机工程学报, 2015, 35(17): 4439-4444.
Guo Yan, Zhou Rongcan, Zhang Hongjun, et al. Microstructure and precipitates of alloy 740H[J]. Proceedings of the CSEE, 2015, 35(17): 4439-4444.
[10]侯世香, 吴正发, 袁晓娜, 等. Inconel 740H合金在模拟煤灰/烟气中的抗腐蚀性研究[J]. 腐蚀科学与防护技术, 2016, 28(3): 247-252.
Hou Shixiang, Wu Zhengfa, Yuan Xiaona, et al. The study of corrosion resistance of Inconel 740H in simulated coal-ash/flue-gas environments[J]. Corrosion Science and Protection Technology, 2016, 28(3): 247-252.
[11]Aung N N, Liu X B. Effect of temperature on coal ash hot corrosion resistance of Inconel 740 superalloy[J]. Corrosion Science, 2014, 82: 227-238.
[12]Liu D Y, Yan L Y, Hou S X. The evaluation of high temperature corrosion of the Inconel 740H in simulated coal-fired environments[J]. Corrosion Science, 2019, 161: 1-7.
[13]向雪梅. 温度/应力互作用与典型镍基髙温合金组织稳定性关联研究[D]. 北京: 北京科技大学, 2021.
Xiang Xuemei. Investigation on the relationship between temperature stress-interaction and microstructure stability of typical Ni-based superalloy[D]. Beijing: University of Science and Technology Beijing, 2021.
[14]郭岩, 王彩侠, 李太江, 等. 700 ℃超超临界机组用617B镍基合金的组织结构和析出相[J]. 材料研究学报, 2016, 30(11): 841-847.
Guo Yan, Wang Caixia, Li Taijiang, et al. Microstructure and precipitates of alloy 617B used for 700 ℃ advanced ulta-supercritical power units[J]. Chinese Journal of Material Research, 2016, 30(11): 841-847.
[15]郭岩, 李聚涛, 杨强斌, 等. 镍基合金617B的组织结构与力学性能稳定性[J]. 金属热处理, 2016, 41(5): 28-41.
Guo Yan, Li Jutao, Yang Qiangbin, et al. Stabilities of microstructure and mechanical properties of alloy 617B[J]. Heat Treatment of Metals, 2016, 41(5): 28-41.
[16]郭岩, 周荣灿, 侯淑芳, 等. 617合金760 ℃时效组织结构及力学性能分析[J]. 中国电机工程学报, 2010, 30(26): 86-89.
Guo Yan, Zhou Rongcan, Hou Shufang, et al. Analysis of microstructure and mechanical properties of alloy 617 aged at 760 ℃[J]. Proceedings of the CSEE, 2010, 30(26): 86-89.
[17]杨权, 谭舒平. 617合金的组织稳定性[J]. 钢铁, 2014, 49(2): 60-64.
Yang Quan, Tan Shuping. Analysis for the microstructure stability of alloy 617[J]. Iron and Steel, 2014, 49(2): 60-64.
[18]向雪梅, 董建新, 江河. 617B镍基高温合金长期时效组织演变[J]. 稀有金属材料与工程, 2019, 48(3): 865-872.
Xiang Xuemei, Dong Jianxin, Jiang He. Microstructure evolution of 617B Ni-based superalloy during long-term aging[J]. Rear Metal Materials and Engineering, 2019, 48(3): 865-872.
[19]Guo Y, Zhang Z B, Zhou R C, et al. Microstructure and mechanical properties of alloy 617B[J]. Transactions of Nonferrous Metals Society of China, 2015, 25: 1106-1113.