热处理对WC-Co硬质合金顶锤组织与力学性能的影响

doi:10.13251/j.issn.0254-6051.2023.06.011

金属热处理 ›› 2023, Vol. 48 ›› Issue (6): 63-67.DOI: 10.13251/j.issn.0254-6051.2023.06.011

热处理对WC-Co硬质合金顶锤组织与力学性能的影响

郝世明¹, 毛志平^2,3, 谢敬佩^2,3

1.河南科技大学物理工程学院, 河南洛阳 471023;
2.河南科技大学材料科学与工程学院, 河南洛阳 471023;
3.有色金属新材料与先进加工技术省部共建协同创新中心, 河南洛阳 471023

收稿日期:2022-11-17 修回日期:2023-04-15 发布日期:2023-08-11
作者简介:郝世明(1975—),男,副教授,博士,主要研究方向为金属基复合材料的制备、微结构和性能,E-mail:haoshm@haust.edu.cn
基金资助:
郑洛新国家自主创新示范区创新引领型产业集群专项(2012002110008);河南省科技攻关项目(222102230088)

Effect of heat treatment on microstructure and mechanical properties of WC-Co cemented carbide anvil

Hao Shiming¹, Mao Zhiping^2,3, Xie Jingpei^2,3

1. School of Physics and Engineering, Henan University of Science and Technology, Luoyang Henan 471023, China;
2. School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang Henan 471023, China;
3. Provincial and Ministerial Co-Construction of Collaborative Innovation Center for Non-Ferrous Metal New Materials and Advanced Processing Technology, Luoyang Henan 471023, China

Received:2022-11-17 Revised:2023-04-15 Published:2023-08-11

摘要/Abstract

摘要： 为了消除顶锤加工中引入的加工缺陷, 通过对WC-Co硬质合金顶锤进行温度600 ℃、时长5 h的退火处理, 使用扫描电镜(SEM)、XRD和显微硬度计等对其组织结构、WC晶粒邻接度、WC粒径分布以及硬度进行了研究。结果表明, 热处理促使WC-Co硬质合金顶锤中钴元素分布和WC粒径变得更均匀, 碳化钨的晶粒邻接度下降, 合金硬度升高。

关键词: WC-Co硬质合金, 顶锤, 热处理, 晶粒邻接度, 硬度

Abstract: In order to eliminate the processing defects introduced in the hammer processing, the WC-Co cemented carbide anvil was annealed at 600 ℃ for 5 h, and its microstructure, WC grain contiguity, WC grain size distribution and hardness were studied by means of scanning electron microscope (SEM), XRD and microhardness tester. The results show that the heat treatment makes the distributions of cobalt element and WC particle size in the WC-Co cemented carbide anvil more uniform, the grain contiguity of tungsten carbide decreases, and the alloy hardness increases.

Key words: WC-Co cemented carbide, anvil, heat treatment, grain contiguity, hardness

中图分类号:

TQ164

郝世明, 毛志平, 谢敬佩. 热处理对WC-Co硬质合金顶锤组织与力学性能的影响[J]. 金属热处理, 2023, 48(6): 63-67.

Hao Shiming, Mao Zhiping, Xie Jingpei. Effect of heat treatment on microstructure and mechanical properties of WC-Co cemented carbide anvil[J]. Heat Treatment of Metals, 2023, 48(6): 63-67.

参考文献

[1] Ferreira J A M, Amaral M A P, Antunes F V, et al. A study on the mechanicalbehaviour of WC/Co hard metals[J]. International Journal of Refractory Metals and Hard Materials, 2009, 27(1): 1-8.
[2]Baik S I, Choi E G, Jun J H, et al. Defect structure induced by iron injection in WC-Co[J]. Scripta Materialia, 2008, 58(7): 614-617.
[3] Abdel-Aal H A, Nouari M, Mansori M E. The effect of thermal property degradation on wear of WC-Co inserts in dry cutting[J]. Wear, 2008, 265(11/12): 1670-1679.
[4] Kim C S, Massa T R, Rohrer G S. Modeling theinfluence of orientation texture on the strength of WC-Co composites[J]. Journal of the American Ceramic Society, 2007, 90(1): 199-204.
[5]郭建中, 龙建国. 热处理对硬质合金顶锤性能和结构的影响[J]. 硬质合金, 2001, 18(2): 85-88.
Guo Jianzhong, Long Jianguo. Effect of heat treatment on the property and structure of cemented carbide anvil[J]. Cemented Carbides, 2001, 18(2): 85-88.
[6]何平, 李晋尧, 邹丹. 提高WC-Co硬质合金顶锤质量的研究[J]. 稀有金属材料与工程, 1996, 25(3): 41-44.
He Ping, Li Jinyao, Zou Dan. Research on improving the properties of WC-Co cemented carbide header[J]. Rare Metal Materials and Engineering, 1996, 25(3): 41-44.
[7]唐云锋, 黄继武, 左锐, 等. 淬火与深冷处理对YG6硬质合金微观结构与性能的影响[J]. 硬质合金, 2015, 32(6): 372-378.
Tang Yunfeng, Huang Jiwu, Zuo Rui, et al. Influence of quenching and cryogenic treatment on microstructure and properties of YG6 cemented carbide[J]. Cemented Carbides, 2015, 32(6): 372-378.
[8]王忆民, 李锐, 曹群. 淬火回火热处理对WC-25%Co硬质合金组织与性能的影响[J]. 硬质合金, 2014, 31(3): 148-154.
Wang Yimin, Li Rui, Cao Qun. Effects of quenching and tempering on microstructure and properties of WC-25%Co cemented carbide[J]. Cemented Carbides, 2014, 31(3): 148-154.
[9]刘益兴, 雍薇, 彭晖, 等. 退火热处理对WC-6%Co超细晶硬质合金抗弯强度的影响[J]. 硬质合金, 2020, 37(2): 127-132.
Liu Yixing, Yong Wei, Peng Hui, et al. Effect of annealing heat treatment on transverse rupture strength of WC-6%Co ultrafine grained cemented carbide[J]. Cemented Carbides, 2020, 37(2): 127-132.
[10]顾金宝, 时凯华, 王可, 等. 热处理工艺对WC-10%Co粗晶硬质合金性能及微观结构的影响[J]. 硬质合金, 2019, 36(2): 150-157.
Hu Jinbao, Shi Kaihua, Wang Ke, et al. Effect of heat treatment process on properties and microstructure of WC-10%Co coarse-grained cemented carbide[J]. Cemented Carbides, 2019, 36(2): 150-157.
[11]Gu L, Huang J, Tang Y, et al. Influence of different post treatments on microstructure and properties of WC-Co cemented carbides[J]. Journal of Alloys and Compounds, 2015, 620: 116-119.
[12]沈利群. 硬质合金热处理研究进展[J]. 热处理, 2002, 17(2): 1-6.
Shen Liqun. Progress of heat treatment for cemented carbide[J]. Heat Treatment, 2002, 17(2): 1-6.
[13]周旭峰. 硬质合金大规格顶锤缺陷消除的研究[D]. 长沙: 中南大学, 2004.
Zhou Xufeng. Research on the elimination of defects of cemented carbide large-size top hammer[D]. Changsha: Central South University, 2004.

[1]	袁志钟, 王梦飞, 段旭斌, 杨海峰, 李表敏, 罗锐, 赵小强, 程晓农. 热处理对42CrMo钢截齿微观组织与力学性能的影响[J]. 金属热处理, 2023, 48(6): 1-8.
[2]	陈朔, 陈学敏, 徐祺昊, 杨礼林, 唐祖川, 赵莉萍. 淬、回火温度对含铈H13钢组织及硬度的影响[J]. 金属热处理, 2023, 48(6): 36-40.
[3]	陈梦浩, 王哲峰, 韩劲, 贺瑞军, 张旺峰, 郭嘉琪, 孔令利, 倪志铭. 脉冲磁场对TC4钛合金表面硬度及微观组织的影响[J]. 金属热处理, 2023, 48(6): 41-46.
[4]	周永东, 龚兰芳, 刘梓屹. 焊后时效处理对7020铝合金应力腐蚀倾向影响[J]. 金属热处理, 2023, 48(6): 80-84.
[5]	李钧正, 韩志杰, 赵海涛. 高强度R400HT钢轨热处理工艺优化[J]. 金属热处理, 2023, 48(6): 101-106.
[6]	欧阳瑞洁, 苗春昊, 张海, 杨文博, 董翔宇. 热处理温度对金属隔膜用工业纯钛力学性能的影响[J]. 金属热处理, 2023, 48(6): 114-117.
[7]	徐海峰, 李海, 李凤敏, 付胜敏, 明科宇, 郁言. 新型槽帮钢的连续冷却转变曲线及微观组织[J]. 金属热处理, 2023, 48(6): 191-196.
[8]	史耀君, 周华杉, 孙华, 夏少华. 油压减振器活塞杆表面激光熔覆不锈钢的组织与性能[J]. 金属热处理, 2023, 48(6): 202-205.
[9]	徐亮亮, 谭敦强. Mn含量及退火工艺对Cu-xMn-0.2Ce-0.2Zr合金组织性能的影响[J]. 金属热处理, 2023, 48(6): 219-228.
[10]	韩啸, 贺瑞军, 朱硕, 王赟, 冯润华, 孔令利. 基于Ansys模拟的钛合金筒形工件离子渗氮温度场分析[J]. 金属热处理, 2023, 48(6): 258-264.
[11]	吕虎跃, 陈旭阳, 丛培武, 陆文林, 杜春辉. 汽车齿轮高压气淬试验及气淬室的结构优化[J]. 金属热处理, 2023, 48(6): 264-269.
[12]	袁志钟, 戴起勋, 王安东, 鞠玉琳, 曹甫洋, 罗锐. 金属材料学的“思想”[J]. 金属热处理, 2023, 48(5): 1-5.
[13]	黄天阳, 郑家圣, 田林海, 林乃明, 王振霞, 秦林, 吴玉程. 钨表面WTaVNbMo难熔高熵合金层的组织与性能[J]. 金属热处理, 2023, 48(5): 6-11.
[14]	吴裕, 唐奇, 苏晓峰, 蒋文龙, 周丹晴. 奥氏体不锈钢表面激光熔覆锆涂层的组织及硬度[J]. 金属热处理, 2023, 48(5): 12-17.
[15]	章益, 侯嘉鹏, 袁衢龙, 张振军, 陈玲, 张哲峰. 电致热处理工业纯铝线的强度演化规律[J]. 金属热处理, 2023, 48(5): 49-53.

热处理对WC-Co硬质合金顶锤组织与力学性能的影响

Effect of heat treatment on microstructure and mechanical properties of WC-Co cemented carbide anvil

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价