空气气氛条件下加热温度对45钢脱碳层深度的影响

doi:10.13251/j.issn.0254-6051.2024.04.035

金属热处理 ›› 2024, Vol. 49 ›› Issue (4): 219-222.DOI: 10.13251/j.issn.0254-6051.2024.04.035

空气气氛条件下加热温度对45钢脱碳层深度的影响

许成^1,2, 杨玉^1,2, 王润琦^1,2, 佟欣儒^1,2, 任俊威³

1.海洋装备用金属材料及其应用国家重点实验室, 辽宁鞍山 114009;
2.鞍钢集团钢铁研究院, 辽宁鞍山 114009;
3.鞍钢股份有限公司鲅鱼圈钢铁分公司, 辽宁营口 115007

收稿日期:2023-10-24 修回日期:2024-03-05 出版日期:2024-04-25 发布日期:2024-05-27
作者简介:许成(1992—),男,工程师,硕士,主要研究方向为钢铁材料及热处理,E-mail:4648875252@qq.com

Effect of heating temperature on depth of decarburization layer of 45 steel in air atmosphere

Xu Cheng^1,2, Yang Yu^1,2, Wang Runqi^1,2, Tong Xinru^1,2, Ren Junwei³

1. State Key Laboratory of Metal Materials and Application for Marine Equipment, Anshan Liaoning 114009, China;
2. Iron and Steel Research Institute of Ansteel Group, Anshan Liaoning 114009, China;
3. Bayuquan Branch of Angang Steel Co., Ltd., Yingkou Liaoning 115007, China

Received:2023-10-24 Revised:2024-03-05 Online:2024-04-25 Published:2024-05-27

摘要/Abstract

摘要： 研究了空气气氛条件下不同加热温度(700~1300 ℃,随炉升温,达温后保温1 h,出炉空冷)对45钢表面脱碳层深度的影响,并分析了其脱碳机理。结果表明,随着加热温度的升高,45钢表面总脱碳层深度增加。700 ℃加热时几乎不产生脱碳现象,750~800 ℃主要为完全脱碳组织,850~900 ℃为完全脱碳组织与部分脱碳组织共存,950 ℃及以上主要为部分脱碳组织。

关键词: 完全脱碳, 部分脱碳, 温度

Abstract: Effect of different heating temperatures (700-1300 ℃ for 1 h, heating up along with the furnace and air cooling) under air atmosphere on decarburization depth of 45 steel surface was studied, and the mechanism of decarburization was analyzed. The results show that as the temperature increases, the depth of the decarburization layer on 45 steel surface is increased. When heated at 700 ℃, no decarburization occurs on the 45 steel surface. When heated at 750~800 ℃, it is mainly dominated by completely decarburized structure. When heated in the range of 850~900 ℃, there is a coexistence of completely decarburized structure and partially decarburized structure. When heated at 950 ℃ and above, it is primarily composed of partially decarburized structure.

Key words: complete decarbonization, partial decarburization, temperature

中图分类号:

TG156.6

许成, 杨玉, 王润琦, 佟欣儒, 任俊威. 空气气氛条件下加热温度对45钢脱碳层深度的影响[J]. 金属热处理, 2024, 49(4): 219-222.

Xu Cheng, Yang Yu, Wang Runqi, Tong Xinru, Ren Junwei. Effect of heating temperature on depth of decarburization layer of 45 steel in air atmosphere[J]. Heat Treatment of Metals, 2024, 49(4): 219-222.

参考文献

[1]熊涛, 赵刚, 徐耀文, 等. 弹簧钢50CrV4加热气氛对表面脱碳的影响[J]. 热加工工艺, 2017, 47(4): 54-58.
Xiong Tao, Zhao Gang, Xu Yaowen, et al. Effect of heating atmosphere on surface decarburization of 50CrV4 spring steel[J]. Hot Working Technology, 2017, 47(4): 54-58.
[2]于学森, 沈奎, 江卓俊, 等. 弹簧钢60Si2MnA表面脱碳规律研究[J]. 热加工工艺, 2017, 46(24): 224-231.
Yu Xuesen, Shen Kui, Jiang Zhuojun, et al. Study on surface decarburization law of spring steel 60Si2MnA[J]. Hot Working Technology, 2017, 46(24): 224-231.
[3]王慧军, 涛雅, 陈林, 等. U76CrRE钢轨热处理过程组织控制及性能[J]. 金属热处理, 2022, 47(5): 161-165.
Wang Huijun, Tao Ya, Chen Lin, et al. Microstructure control and properties of U76CrRE steel rail during heat treatment[J]. Heat Treatment of Metals, 2022, 47(5): 161-165.
[4]胡磊, 王雷, 麻晗. 高碳钢盘条的表面氧化与脱碳行为[J]. 钢铁研究学报, 2016, 28(3): 67-73.
Hu Lei, Wang Lei, Ma Han. Behaviors of oxidation and decarburization on surfaces of high carbon steel wire rods[J]. Journal of Iron and Steel Research, 2016, 28(3): 67-73.
[5]催忠圻, 覃耀春. 金属学与热处理[M]. 北京: 机械工业出版社, 2016.
[6]赵宪明, 张坤, 杨洋. 42CrMo钢表面脱碳行为研究[J]. 钢铁研究学报, 2019, 31(2): 196-201.
Zhao Xianming, Zhang Kun, Yang Yang. Investigation of surface decarburization behavior in 42CrMo steel[J]. Journal of Iron and Steel Research, 2019, 31(2): 196-201.
[7]赵小龙, 王雍期, 唐兴昌, 等. 钢坯在加热过程中的氧化机理及其研究综述[J]. 轧钢, 2019, 36(6): 66-68.
Zhao Xiaolong, Wang Yongqi, Tang Xingchang, et al. Review on the oxidation mechanism and its research of steel billet in heating process[J]. Steel Rolling, 2019, 36(6): 66-68.

[1]	贾晓斌, 秦瑞廷, 涂明金, 李媛媛, 胡永平, 周仲成. 挤压316H奥氏体不锈钢大口径管材的晶粒度控制[J]. 金属热处理, 2024, 49(4): 168-174.
[2]	李晓亮, 程晓英, 王兆丰, 任毓文, 曾繁宇. 回火温度对Nb、V合金化低合金高强度钢氢脆敏感性的影响[J]. 金属热处理, 2024, 49(3): 7-14.
[3]	赵鑫磊, 袁晓飞, 乔珺威. 固溶温度对K424合金显微组织与力学性能的影响[J]. 金属热处理, 2024, 49(3): 15-21.
[4]	张禹, 于金瑞, 于鑫泓, 冯以盛, 张云山, 赵而团. 等温淬火温度对50CrVA钢组织与性能的影响[J]. 金属热处理, 2024, 49(3): 28-32.
[5]	魏辉, 林媛, 王红霞, 王士嘉, 李旭, 张文康, 王一德. 二次冷轧中间退火温度对3.5%Si无取向硅钢组织织构的影响机理[J]. 金属热处理, 2024, 49(3): 37-43.
[6]	尤文豪, 陈霞, 陈彬. 常化工艺对取向硅钢组织织构和磁性能的影响[J]. 金属热处理, 2024, 49(3): 50-55.
[7]	刘再旺, 郭敏, 滕华湘, 杨利斌, 梁轩, 刘广会, 刘顺明. 退火温度对超深冲搪瓷钢成型性能及再结晶织构的影响[J]. 金属热处理, 2024, 49(3): 91-97.
[8]	王娇娇, 赵林林, 高云哲, 石帅, 武晓龙, 赵燕青, 周玉青, 弓俊杰. 回火温度对深井石油套管用钢组织性能的影响[J]. 金属热处理, 2024, 49(3): 112-115.
[9]	刘鹏飞, 关琳, 刘建, 陈宇, 刘宏亮. 退火工艺对低成本980 MPa级冷轧双相钢组织和性能的影响[J]. 金属热处理, 2024, 49(3): 122-127.
[10]	江畅, 陆恒昌, 韦习成, 董瀚. 发动机用SCM435钢的组织与疲劳性能[J]. 金属热处理, 2024, 49(3): 159-163.
[11]	曹佳丽, 靳红泽, 李康立, 徐亚鹏, 赵强, 王翠萍, 李梦楠. 水电用Q690CFD低合金高强钢SH-CCT曲线测定与分析[J]. 金属热处理, 2024, 49(2): 60-65.
[12]	蔡小叶, 程宗辉, 董定平, 白兵, 谢隋杰. 热处理对L-PBF成形Ti-6Al-4V钛合金显微组织和力学性能的影响[J]. 金属热处理, 2024, 49(2): 183-189.
[13]	胡生双, 陈素明, 颜家维, 岳珊, 高晓颖, 欧阳德来. 时效温度对TB18钛合金组织和力学性能的影响[J]. 金属热处理, 2024, 49(2): 190-194.
[14]	陈博文, 曾强, 李钢, 彭文雅, 刘国怀. 固溶温度对DD416镍基单晶高温合金组织及拉伸性能的影响[J]. 金属热处理, 2024, 49(1): 119-126.
[15]	陈玉波, 王培杰, 原海瑞, 李振江. 正火温度对G18CrMo2-6铸钢微观组织及力学性能的影响[J]. 金属热处理, 2024, 49(1): 137-141.

空气气氛条件下加热温度对45钢脱碳层深度的影响

Effect of heating temperature on depth of decarburization layer of 45 steel in air atmosphere