冷塑性变形及退火工艺对Ti45Nb合金组织和性能的影响

doi:10.13251/j.issn.0254-6051.2024.05.018

金属热处理 ›› 2024, Vol. 49 ›› Issue (5): 112-117.DOI: 10.13251/j.issn.0254-6051.2024.05.018

冷塑性变形及退火工艺对Ti45Nb合金组织和性能的影响

王泽龙^1,2, 冯兆龙^1,2, 李伟^1,3, 孙思博^1,2

1.钒钛资源综合利用国家重点实验室, 四川攀枝花 617000;
2.成都先进金属材料产业技术研究院股份有限公司, 四川成都 610300;
3.攀钢集团研究院有限公司, 四川攀枝花 617000

收稿日期:2023-10-25 修回日期:2024-03-24 出版日期:2024-05-25 发布日期:2024-06-28
作者简介:王泽龙（1992—），男，工程师，硕士，主要研究方向为钛合金丝材开发，E-mail：836727680@qq.com。

Effects of cold deformation and annealing process on microstructure and properties of Ti45Nb alloy

Wang Zelong^1,2, Feng Zhaolong^1,2, Li Wei^1,3, Sun Sibo^1,2

1. State Key Laboratory of Comprehensive Utilization of Vanadium and Titanium Resources, Panzhihua Sichuan 617000, China;
2. Chengdu Institute of Advanced Metal Materials Industrial Technology Co., Ltd., Chengdu Sichuan 610300, China;
3. Pangang Group Research Institute Co., Ltd., Panzhihua Sichuan 617000, China

Received:2023-10-25 Revised:2024-03-24 Online:2024-05-25 Published:2024-06-28

摘要/Abstract

摘要： 采用辊模拉拔技术对Ti45Nb合金丝材进行冷变形,利用OM、EBSD以及拉伸试验等手段研究了冷塑性成形和退火工艺对Ti45Nb合金丝材微观组织和力学性能的影响规律。结果表明,随着冷变形量的增加,Ti45Nb合金丝材的晶粒尺寸逐渐减小,晶粒的取向密度指数逐渐增强,<110>丝织构占据主导地位。同时,Ti45Nb合金丝材的抗拉强度和屈服强度逐渐升高,但是剪切强度无明显变化。采用水冷的方式可以显著提高退火后Ti45Nb合金丝材的塑性,防止顶锻试验开裂。Ti45Nb合金丝材完全再结晶温度为670 ℃左右,随着退火温度升高,晶粒尺寸明显长大,抗拉强度和屈服强度呈现出上升趋势。

关键词: Ti45Nb合金, 冷变形, 热处理, 微观组织, 力学性能

Abstract: Cold deformation of Ti45Nb alloy wire was carried out using roller die drawing technology. The effects of cold plastic forming and annealing process on microstructure and mechanical properties of the Ti45Nb alloy wire were studied by means of OM, EBSD and tensile test. The results indicate that with the increase of cold deformation, the grain size of the Ti45Nb alloy wire gradually decreases, the orientation density index of the grains gradually increases, and the <110> silk texture dominates. At the same time, the tensile strength and yield strength of the Ti45Nb alloy wire gradually increase, but its shear strength does not change significantly. The use of water cooling can significantly improve the plasticity of the annealed Ti45Nb alloy wires and prevent cracking during compression deformation. The complete recrystallization temperature of the Ti45Nb wire is around 670 ℃. As the annealing temperature increases, the grain size significantly increases, and the tensile strength and yield strength show an upward trend.

Key words: Ti45Nb alloy, cold deformation, heat treatment, microstructure, mechanical properties

中图分类号:

TG146.24

王泽龙, 冯兆龙, 李伟, 孙思博. 冷塑性变形及退火工艺对Ti45Nb合金组织和性能的影响[J]. 金属热处理, 2024, 49(5): 112-117.

Wang Zelong, Feng Zhaolong, Li Wei, Sun Sibo. Effects of cold deformation and annealing process on microstructure and properties of Ti45Nb alloy[J]. Heat Treatment of Metals, 2024, 49(5): 112-117.

参考文献

[1]肖浩, 孙杨, 范娟娟, 等. β钛合金热处理工艺研究进展[J]. 金属热处理, 2023, 48(11): 258-265.
Xiao Hao, Sun Yang, Fan Juanjuan, et al. Research progress on heat treatment of β titanium alloy[J]. Heat Treatment of Metals, 2023, 48(11): 258-265.
[2]李蒙, 凤伟中, 关蕾, 等. 航空航天紧固件用钛合金材料综述[J]. 有色金属材料与工程, 2018, 39(4): 49-53.
Li Meng, Feng Weizhong, Guan Lei, et al. Summary of titanium alloy for fastener in aerospace[J]. Nonferrous Metal Materials and Engineering, 2018, 39(4): 49-53.
[3]宁聪琴, 周玉. 医用钛合金的发展及研究现状[J]. 材料科学与工艺, 2002, 10(1): 100-106.
Ning Congqin, Zhou Yu. Development and research status of biomedical titanium alloys[J]. Materials Science and Technology, 2002, 10(1): 100-106.
[4]商国强, 王新南, 唐斌, 等. 紧固件用Ti-45Nb合金丝材的性能评价[J]. 中国有色金属学报, 2010, 20(S1): 70-74.
Shang Guoqiang, Wang Xinnan, Tang Bin, et al. Property evaluation of Ti-45Nb alloy wires used in fastener[J]. The Chinese Journal of Nonferrous Metals, 2010, 20(S1): 70-74.
[5]林杨, 张建国, 王泓, 等. 时效温度对Ti-45Nb合金组织与性能的影响[J]. 金属热处理, 2014, 39(10): 125-127.
Lin Yang, Zhang Jianguo, Wang Hong, et al. Effect of aging temperature on microstructure and properties of Ti-45Nb alloy[J]. Heat Treatment of Metals, 2014, 39(10): 125-127.
[6]Völker B, Maier-Kiener V, Werbach K, et al. Influence of annealing on microstructure and mechanical properties of ultrafine-grained Ti45Nb[J]. Materials and Design, 2019, 179: 107864.
[7]李健, 庄宇盛, 李春慧, 等. 冷变形及时效对新型β钛合金组织性能的影响[J]. 金属热处理, 2022, 47(11): 70-76.
Li Jian, Zhuang Yusheng, Li Chunhui, et al. Effect of cold rolling and aging on microstructure and properties of novel β-titanium alloys[J]. Heat Treatment of Metals, 2022, 47(11): 70-76.
[8]任德春, 刘玉敬, 张慧博, 等. 冷变形和时效热处理对TB9钛合金组织和性能影响[J]. 稀有金属材料与工程, 2020, 49(3): 1083-1089.
Ren Dechun, Liu Yujing, Zhang Huibo, et al. Influence of cold deformation and aging heat treatment on microstructure and mechanical property of TB9 titanium alloy[J]. Rare Metal Materials and Engineering, 2020, 49(3): 1083-1089.
[9]任德春, 苏虎虎, 张慧博, 等. 冷旋锻变形对TB9钛合金显微组织和拉伸性能的影响[J]. 金属学报, 2019, 55(4): 480-488.
Ren Dechun, Su huhu, Zhang Huibo, et al. Effect of cold rotary-swaging deformation on microstructure and tensile properties of TB9 titanium alloy[J]. Acta Metallurgica Sinica, 2019, 55(4): 480-488.
[10]王文娟, 李建康. 眼镜框架用TB5钛合金丝材的辊模拉拔[J]. 热加工工艺, 2014, 43(17): 125-126, 131.
Wang Wenjuan, Li Jiankang. Roller die drawing of TB5 titanium alloy wire for glasses frame[J]. Hot Working Technology, 2014, 43(17): 125-126, 131.
[11]张志强, 董利民, 关少轩, 等. TC16钛合金辊模拉丝过程中的显微组织和力学性能[J]. 金属学报, 2017, 53(4): 415-422.
Zhang Zhiqiang, Dong Limin, Guan Shaoxuan, et al. Microstructure and mechanical properties of TC16 titanium alloy by room temperature roller die drawing[J]. Acta Metallurgica Sinica, 2017, 53(4): 415-422.
[12]Karim E A, Joakim L, Lars P. Experimental comparison of roller die and conventional wire drawing[J]. Journal of Materials Processing Technology, 2018, 257: 7-14.
[13]苏连朋. β型二元TiNb合金塑性变形及其组织性能研究[D]. 太原: 太原理工大学, 2019.
Su Lianpeng. Study on plastic deformation and microstructure, properties of β-type binary TiNb alloys[D]. Taiyuan: Taiyuan University of Technology, 2019.

[1]	何宗政, 吴名冬, 袁硕, 姚树伟, 肖代红, 黄兰萍, 刘文胜. Zn/Mg比对7075铝合金显微组织、力学性能和耐蚀性能的影响[J]. 金属热处理, 2024, 49(5): 1-9.
[2]	鲍峥, 程翔, 王若民, 缪春辉, 陈国宏, 汤文明. 不同服役期TP347HFG钢管显微组织与力学性能的对比[J]. 金属热处理, 2024, 49(5): 10-16.
[3]	杨希锐, 江宝世, 胡锋涛, 李艳军, 盛超杰, 王晨. 高温长期服役S30432钢管的组织与性能[J]. 金属热处理, 2024, 49(5): 17-21.
[4]	王书亮, 毛一点, 李奇霖, 周禄江, 西宇辰, 张华礼. V对富Fe非等原子比FeCrCoNi高熵合金组织及性能的影响[J]. 金属热处理, 2024, 49(5): 22-28.
[5]	王英虎, 王婀娜, 蔡晓文. 铜含量对303易切削钢中硫化物形貌及力学性能的影响[J]. 金属热处理, 2024, 49(5): 29-35.
[6]	郭炜, 管博, 陈威, 吴丹. 多次闭模压缩对不同Si含量AZ31合金显微组织和耐磨性能的影响[J]. 金属热处理, 2024, 49(5): 36-39.
[7]	冯兴旺, 张可, 刘久江, 石如星, 苏文博, 刘帅, 李志鹏, 杨滨. 蒸汽发生器用SA508-3钢锻后热处理的数值模拟及其试验验证[J]. 金属热处理, 2024, 49(5): 55-61.
[8]	石红昌, 黄安明, 刘兴, 强斌. 焊后热处理对150 mm厚容器钢板残余应力影响的数值模拟[J]. 金属热处理, 2024, 49(5): 62-67.
[9]	李波, 向伟, 张枫, 秦锋英, 袁武华. 预时效处理对亚稳态β钛合金TB18组织性能的影响[J]. 金属热处理, 2024, 49(5): 106-111.
[10]	邢振强, 庞景宇, 张宏伟, 纪宇, 朱正旺, 张龙, 王爱民, 张海峰. 冷轧、退火和时效对Fe₅₀Ni₂₅Cr₁₅Al₁₀高熵合金组织和性能的影响[J]. 金属热处理, 2024, 49(5): 118-123.
[11]	张增光, 史吉鹏, 王新宇, 刘艳梅, 杨立新, 康冲, 刘刚. 退火温度对Ti60钛合金激光焊接接头组织与力学性能的影响[J]. 金属热处理, 2024, 49(5): 130-134.
[12]	张勇, 马青山, 李如杨, 胡效东. S11306铁素体不锈钢厚板焊后热处理特性[J]. 金属热处理, 2024, 49(5): 146-152.
[13]	石磊, 田鹏勇, 施莹, 白雪, 杨芳. 两相区退火对铁素体/贝氏体双相钢组织性能的影响[J]. 金属热处理, 2024, 49(5): 158-161.
[14]	朱艳强, 李永刚, 何琼, 刘哲兵. 深冷处理对X70管线钢组织与力学性能的影响[J]. 金属热处理, 2024, 49(5): 168-172.
[15]	蒲博闻, 刘玉婷, 王延荣, 刁占英, 何敬卫. 调质处理对34CrNiMo6钢连杆锻件组织与硬度的影响[J]. 金属热处理, 2024, 49(5): 173-178.

冷塑性变形及退火工艺对Ti45Nb合金组织和性能的影响

Effects of cold deformation and annealing process on microstructure and properties of Ti45Nb alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价