关键词: 磨削烧伤, 二次淬火, 淬火裂纹

Abstract: Longitudinal cracks were found on the 1-2 teeth of the tail end of the 30CrMnSiNi2 bolt thread through magnetic particle testing. Combining with the bolt production process, the causes of microcrack formation were analyzed by means of macro and micro morphology observation of the microcracks and microstructure and hardness examination of the bolt. The results show that due to improper cooling during grinding, secondary quenching occurred at the 1-2 teeth of the thread end tail tooth, resulting in fine needle-like martensite appears, causing grinding burns and quenching cracks under secondary quenching stress. In order to avoid such problems recurrence, it is recommended reinforcing the grinding cooling detection and related personnel training and improving the equipment maintenance system.

Key words: grinding burn, secondary quenching, quenching crack