42CrMo钢锻件斑点状偏析形成原因分析

徐全¹, 陈民涛², 党淑娥¹, 张英凡¹, 焦永星¹, 白宏亮²

1.太原科技大学材料科学与工程学院, 山西太原 030024;
2.太原重工股份有限公司技术中心, 山西太原 030024

收稿日期:2024-06-04 修回日期:2024-09-03 出版日期:2024-11-25 发布日期:2025-01-09
通讯作者: 党淑娥,教授,博士,E-mail:shuedang@163.com
作者简介:徐全(1992—),男,硕士研究生,主要研究方向为金属热处理,E-mail:xuquan900517@163.com。
基金资助:
山西省科技重大专项计划“揭榜挂帅”项目(202101110401009)

Formation reason analysis of spot segregation in 42CrMo steel forgings

Xu Quan¹, Chen Mintao², Dang Shue¹, Zhang Yingfan¹, Jiao Yongxing¹, Bai Hongliang²

1. School of Materials Science and Engineering, Taiyuan University of Science and Technology, Taiyuan Shanxi 030024, China;
2. Technology Center, Taiyuan Heavy Industry Co., Ltd., Taiyuan Shanxi 030024, China

Received:2024-06-04 Revised:2024-09-03 Online:2024-11-25 Published:2025-01-09

摘要/Abstract

摘要： 利用OM、SEM、EDS等技术,对风电齿轮箱用42CrMo钢锻件表面的亮白色斑点状偏析进行观察分析。结果表明,锻件表面的亮白色斑点偏析为回火贝氏体。这是由于42CrMo钢钢锭存在成分偏析,锻造后呈条状和斑点状贝氏体偏析;经常规锻后热处理(正火+高温回火)后,成分未均匀化,贝氏体偏析演变为聚集的颗粒状Cr、Mo碳化物偏析;再经调质处理后,组织转变为回火索氏体基体上存在着大小不一、分布不均的回火贝氏体。

关键词: 42CrMo钢锻件, 斑点状偏析, 贝氏体

Abstract: Bright white spot segregation on the surface of 42CrMo steel forgings used in wind turbine gearbox was observed and analyzed by OM, SEM, EDS and other technologies. The results show that the bright white spots segregating on the surface of the forging are tempered bainite. This is due to the existence of composition segregation of the 42CrMo steel ingot, which shows strip and spot bainite segregation after forging. After conventional post-forging heat treatment (normalizing+high temperature tempering), the chemical composition is not homogenized, and the bainite segregation evolves into aggregated granular Cr and Mo carbide segregation. After further quenching and tempering treatment, the microstructure is tempered bainite with varying sizes and uneven distribution in the tempered sorbite matrix.

Key words: 42CrMo steel forgings, spot segregation, bainite

中图分类号:

TG157

徐全, 陈民涛, 党淑娥, 张英凡, 焦永星, 白宏亮. 42CrMo钢锻件斑点状偏析形成原因分析[J]. 金属热处理, 2024, 49(11): 308-314.

Xu Quan, Chen Mintao, Dang Shue, Zhang Yingfan, Jiao Yongxing, Bai Hongliang. Formation reason analysis of spot segregation in 42CrMo steel forgings[J]. Heat Treatment of Metals, 2024, 49(11): 308-314.

参考文献

[1]Chen M S, Yuan W Q, Lin Y C. et al. Modeling and simulation of dynamic recrystallization behavior for 42CrMo steel by an extended cellular automaton method[J]. Vacuum, 2017, 146: 142-151.
[2]Jiang B, Zhou L, Wen X, et al. Heat treatment properties of 42CrMo steel for bearing ring of varisized shield tunneling machine[J]. Acta Metallurgica Sinica(English Letters), 2014, 27(3): 383-388.
[3]李鸿娟, 向成功, 吴琼, 等. 淬火与回火工艺对42CrMo钢显微组织和奥氏体晶粒长大规律的影响[J]. 金属热处理, 2023, 48(1): 181-185.
Li Hongjuan, Xiang Chenggong, Wu Qiong, et al. Effect of quenching and tempering process on microstructure and austenite grain growth of 42CrMo steel[J]. Heat Treatment of Metals, 2023, 48(1): 181-185.
[4]Zhang J, Liu Z, Sun J, et al. Microstructure and mechanical property of electropulsing tempered ultrafine grained 42CrMo steel[J]. Materials Science and Engineering A, 2020, 782: 139213.
[5]Quan G, Tong Y, Luo G, et al. A characterization for the flow behavior of 42CrMo steel[J]. Computational Materials Science, 2010, 50(1): 167-171.
[6]Lu Y, Zhu Z, Li D, et al. Constitutive model of 42CrMo steel under a wide range of stain rates based on crystal plasticity theory[J]. Materials Science and Engineering A, 2017, 679: 215-222.
[7]苑静之, 时乐智, 许文花, 等. 42CrMo钢风电主轴开裂失效的组织缺陷分析[J]. 金属热处理, 2020, 45(7): 206-209.
Yuan Jingzhi, Shi Yuezhi, Xu Wenhua, et al. Structure-defect analysis of crack failure in 42CrMo wind power spindle[J]. Heat Treatment of Metals, 2020, 45(7): 206-209.
[8]邢嘉倪, 蔡欣, 郑雷刚, 等. 淬火及回火温度对新型中碳合金钢42CrMo4M组织性能的影响[J]. 材料热处理学报, 2022, 43(5): 124-133.
Xing Jiani, Cai Xin, Zheng Leigang, et al. Effect of quenching and tempering temperature on microstructure and mechanical properties of a new medium carbon alloy steel 42CrMo4M[J]. Transactions of Materials and Heat Treatment, 2022, 43(5): 124-133.
[9]居龙, 冯超, 赵劲彪, 等. 42CrMo高强度螺栓在海洋大气环境中的应力腐蚀开裂风险评估[J]. 腐蚀与防护, 2019, 40(9): 644-649.
Ju Long, Feng Chao, Zhao Jinbiao, et al. Risk assessment of stress corrosion cracking of 42CrMo high strength steel botts in seacoast environment[J]. Corrosion and Protection, 2019, 40(9): 644-649.
[10]吕超然, 史超, 蒋伟斌, 等. 回火温度对42CrMo钢组织和力学性能的影响[J]. 金属热处理, 2021, 46(1): 32-37.
Lü Chaoran, Shi Chao, Jiang Weibin, et al. Effect of tempering temperature on microstructure and mechanical properties of 42CrMo steel[J]. Heat Treatment of Metals, 2021, 46(1): 32-37.
[11]Wang C, Yu L, Ding R, et al. Microstructure and mechanical properties of a novel medium Mn steel with Cr and Mo microalloying[J]. Materials Science and Engineering A, 2021, 825: 141926.
[12]蒋波, 霍朝霞, 周乐育, 等. 奥氏体变形和Mn对42CrMo钢连续冷却相变组织的影响[J]. 材料热处理学报, 2014, 35(8): 119-124.
Jing Bo, Huo Zhaoxia, Zhou Leyu, et al. Effect of austenite deformation and manganese content on microstructure of continuous cooling transformation of 42CrMo steel[J]. Transactions of Materials and Heat Treatment, 2014, 35(8): 119-124.
[13]孔昌昌, 秦凤明, 张晓峰, 等. 含Mo元素CL60钢CCT曲线的测定及分析[J]. 材料热处理学报, 2019, 40(8): 138-144.
Kong Changchang, Qin Fengming, Zhang Xiaofeng, et al. Detection and analysis of CCT curve of CL60 steel with Mo element[J]. Transactions of Materials and Heat Treatment, 2019, 40(8): 138-144.
[14]桂晓露, 刘蓉, 高古辉, 等. Cr元素对贝氏体钢连续转变规律的影响[J]. 材料热处理学报, 2016, 37(10): 154-158.
Gui Xiaolu, Liu Rong, Gao Guhui, et al. Effect of Cr on continuous cooling transformation characteristic of bainitic steels[J]. Transactions of Materials and Heat Treatment, 2016, 37(10): 154-158.
[15]彭聪, 陈霞, 张益. Mo对低碳贝氏体钢相变动力学及组织性能影响研究[J]. 热加工工艺, 2017, 46(12): 95-98.
Peng Cong, Chen Xia, Zhang Yi. Effects of Mo on phase transformation kinetics and microstructure and mechanical properties of low carbon bainitic steel[J]. Hot Working Technology, 2017, 46(12): 95-98.
[16]谭谆礼, 白秉哲, 方鸿生. Mo在新型空冷低碳Mn-Si-Cr系贝氏体钢中的作用[J]. 金属热处理, 2007, 32(9): 48-51.
Tan Zhunli, Bai Bingzhe, Fang Hongsheng. Influence of Mo on microstructure and properties of novel air-cooled low carbon Mn-Si-Cr bainitic steels[J]. Heat Treatment of Metals, 2007, 32(9): 48-51.
[17]Kong J, Xie C. Effect of molybdenum on continuous cooling bainite transformation of low-carbon microalloyed steel[J]. Materials and Design, 2006, 27(10): 1169-1173.
[18]De-Castro D, Eres-Castellanos A, Vivas J, et al. Morphological and crystallographic features of granular and lath-like bainite in a low carbon microalloyed steel[J]. Materials Characterization, 2022, 184: 111703.
[19]Li Z J, Chen Y B, Yuan H R, et al. Microstructure and properties of low alloy CrMo steel processed with varied isothermal temperatures[J]. Materials Today Communications, 2023, 35: 106158.
[20]刘宗昌, 王海燕, 任慧平, 等. 贝氏体碳化物形成机理[J]. 热处理技术与装备, 2007, 28(4): 19-23.
Liu Zongchang, Wang Haiyan, Ren Huiping, et al. Formation mechanism of bainite carbide[J]. Heat Treatment Technology and Equipment, 2007, 28(4): 19-23.
[21]乔斌. 粒状贝氏体的形成[J]. 淮海工学院学报(自然科学版), 1998, 7(2): 13-16.
Qiao Bin. Theprinciples of granular bainite[J]. Journal of Huaihai Institute of Technology: Natural Sciences Edition, 1998, 7(2): 13-16.
[22]郭富玉, 闵娜, 袁俊丰, 等. 扩散退火对DIEVAR钢枝晶偏析和元素分布的影响[J]. 材料热处理学报, 2021, 42(7): 79-88.
Guo Fuyu, Min Na, Yuan Junfeng, et al. Effect of diffusion annealing on dendrite segregation and element distribution of DIEVAR steel[J]. Transactions of Materials and Heat Treatment, 2021, 42(7): 79-88.
[23]Bach P W, Beyer J, Verbraak C A. Atom probe analysis of bainitic phase boundaries in a low alloyed Cr Mo steel[J]. Scripta Metallurgica, 1980, 14(2): 205-210.

42CrMo钢锻件斑点状偏析形成原因分析

Formation reason analysis of spot segregation in 42CrMo steel forgings

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	任鹏帅, 秦凤, 周骞, 赵雷杰, 崔护, 彭子奥, 武常生. 等温淬火对含铝无碳化物贝氏体钢组织和性能的影响[J]. 金属热处理, 2024, 49(9): 103-109.
[2]	陈彦孜, 刘馨宇, 苏航, 谢本昌, 岑耀东, 陈林. 基于模拟软件的贝氏体钢轨热处理工艺优化[J]. 金属热处理, 2024, 49(7): 38-41.
[3]	周蕾, 王莹, 张永健, 赵晓丽, 惠卫军. V+Ti微合金化Mn-Cr系贝氏体型非调质钢的氢脆敏感性[J]. 金属热处理, 2024, 49(7): 106-112.
[4]	刘晨希, 胡昕明, 欧阳鑫, 邢梦楠, 王储. 淬火温度对690 MPa级低焊接裂纹敏感性容器钢组织性能的影响[J]. 金属热处理, 2024, 49(5): 124-129.
[5]	石磊, 田鹏勇, 施莹, 白雪, 杨芳. 两相区退火对铁素体/贝氏体双相钢组织性能的影响[J]. 金属热处理, 2024, 49(5): 158-161.
[6]	唐建良, 蒋杨英, 闫洪军. ML45CrMo钢16.8级螺栓的等温淬火工艺[J]. 金属热处理, 2024, 49(5): 231-233.
[7]	谢红申, 李明, 冷婉晴, 刁晓刚, 李洲, 徐流杰. 等温淬火对高钒耐磨合金组织与力学性能的影响[J]. 金属热处理, 2024, 49(4): 123-131.
[8]	张禹, 于金瑞, 于鑫泓, 冯以盛, 张云山, 赵而团. 等温淬火温度对50CrVA钢组织与性能的影响[J]. 金属热处理, 2024, 49(3): 28-32.
[9]	杨颖, 潘诗良, 许媛媛, 王泽民, 王占勇. 超低碳贝氏体钢双相区回火过程中逆转变奥氏体的演变[J]. 金属热处理, 2024, 49(3): 182-189.
[10]	田亚强, 姚硕, 张明山, 李红斌, 胡宝佳, 陈连生. 贝氏体等温温度对两相区轧制舰船用钢组织性能的影响[J]. 金属热处理, 2024, 49(11): 167-171.
[11]	于金瑞, 吴康俊, 于鑫泓, 冯以盛, 赵而团. 含偏析贝氏体弹簧钢的等温转变特性[J]. 金属热处理, 2024, 49(1): 53-60.
[12]	陈玉波, 王培杰, 原海瑞, 李振江. 正火温度对G18CrMo2-6铸钢微观组织及力学性能的影响[J]. 金属热处理, 2024, 49(1): 137-141.
[13]	刘艳锋, 刘小民, 王法云, 赵宇清, 李晓增, 潘永红. 火车制动杠杆吊座用40Cr螺栓断裂原因分析[J]. 金属热处理, 2024, 49(1): 279-283.
[14]	李德明, 雷宁宁, 张晋刚, 宫涛, 周广浩. 快速回火对690 MPa级别工程机械用钢板组织和性能的影响[J]. 金属热处理, 2023, 48(9): 75-80.
[15]	鄢文泽, 闫文青, 林轩艺, 王红鸿. 铌微合金化对低合金高强钢模拟焊接热影响区粒状贝氏体相变及SH-CCT曲线的影响[J]. 金属热处理, 2023, 48(9): 150-156.