Heat treatment process based on 07MnNiMoDR steel heat treatment process window

doi:10.13251/j.issn.0254-6051.2021.10.024

Abstract

Abstract: Relationship between quenching and tempering prcesses and grain size and polygonal ferrite content of the 07MnNiMoDR steel was studied, and the austenite size window and tempered polygonal ferrite content window during quenching and tempering were established, and a more precise heat treatment process was determined. The results show that the austenite grain size increases with the increase of austenitizing temperature and holding time, and there is an optimal range of uniformity. The reasonable quenching process is heating at (940±10) ℃ and holding for (80±10) min. When the temperature rises, polygonal ferrite appears at about 650 ℃, of which content increases with the increase of tempering temperature and holding time. The reasonable tempering process is heating at (665±5) ℃ for (165±15) min. The optimal heat treatment process consists of quenching at 940 ℃ for 80 min and tempering at 660 ℃ for 180 min. The final performance test results show that the elongation, impact absorbed energy and yield strength are increased by 40.88%, 206.25% and 12.1%, respectively, compared with the national standard.

Key words: 07MnNiMoDR steel, austenite grain size window, polygonal ferrite content window, optimum heat treatment process, performance testing

CLC Number:

TG142.1

Liu Feng, Pang Yuhua, Luo Yuan, Sun Qi, Wang Hai, Liu Dong. Heat treatment process based on 07MnNiMoDR steel heat treatment process window[J]. Heat Treatment of Metals, 2021, 46(10): 137-143.

References

[1]徐帅. 07MnMoVR钢调质热处理的组织与性能研究[D]. 沈阳: 东北大学, 2012.
Xu Shuai. Research on the microstructure and mechanical property of 07MnMoVR steel inquenching and tempering heat treatment[D]. Shenyang: Northeastern University, 2012.
[2]姜在伟, 吴俊平, 张仪杰, 等. 低温容器用07MnNiMoDR钢的热处理优化[J]. 金属热处理, 2020, 45(11): 182-186.
Jiang Zaiwei, Wu Junping, Zhang Yijie, et al. Heat treatment optimization of 07MnNiMoDR steel for low temperature vessel[J]. Heat Treatment of Metals, 2020, 45(11): 182-186.
[3]冯路路, 张敬忠, 居峰, 等. 低焊接裂纹敏感性钢07MnNiMoDR的组织性能研究[J]. 材料与冶金学报, 2019, 18(4): 274-279.
Feng Lulu, Zhang Jingzhong, Ju Feng, et al. Study on microstructure and properties of low weld crack sensitive steel 07MnNiMoDR[J]. Journal of Materials and Metallurgy, 2019, 18(4): 274-279.
[4]王成, 易勋, 梁宝珠, 等. 调质高强度压力容器用07MnNiMoDR钢板轧钢工艺探索及低温韧性研究[J]. 中国金属通报, 2020(9): 107-108.
Wang Cheng, Yi Xun, Liang Baozhu, et al. Research on rolling process and low temperature toughness of 07MnNiMoDR steel plate for quenched and tempered high strength pressure vessel[J]. China Metal Bulletin, 2020(9): 107-108.
[5]赵全卿, 王志明, 刘生, 等. 提高07MnNiMoDR 钢板性能合格率的工艺实践[J]. 宽厚板, 2014, 20(2): 18-19, 23.
Zhao Quanqing, Wang Zhiming, Liu Sheng, et al. Technological practice to improve qualification rate of mechanical properties of 07MnNiMoDR steel plate[J]. Wide and Heavy Plate, 2014, 20(2): 18-19, 23.
[6]Dhua S K, Sen S K. Effect of direct quenching on the microstructure and mechanical properties of the lean-chemistry HSLA-100 steel plates[J]. Materials Science and Engineering A, 2011, 528(21): 6356-6365.
[7]陈晓泉. 容器钢低温韧度偏低的原因分析[J]. 理化检验(物理分册), 2015, 51(7): 466-469.
Chen Xiaoquan. Cause analysis on the lower low-temperature toughness of container steel[J]. Physical Testing and Chemical Analysis (Part A: Physical Testing), 2015, 51(7): 466-469.
[8]陈永利. 低温压力容器用07MnNiMoVDR钢轧制及调质工艺研究[D]. 沈阳: 东北大学, 2009.
Chen Yongli. Research on low-temperature pressure vessel steel 07MnNIMoVDR rolled and quenched and tempered technology[D]. Shenyang: Northeastern University, 2009.
[9]张海军, 高雅, 刘利香, 等. 压力容器用07MnNiMoDR钢板的低温冲击韧性研究[J]. 河南冶金, 2014, 22(1): 16-18.
Zhang Haijun, Gao Ya, Liu Lixiang, et al. Research on the low temperature toughness of 07MnNiMoDR steel plate for pressure vessel[J]. Henan Metallurgy, 2014, 22(1): 16-18.
[10]熊涛, 徐光, 洪君. 高参数球形储罐用钢07MnNiMoDR的研制[J]. 热加工工艺, 2014, 43(16): 27-30.
Xiong Tao, Xu Guang, Hong Jun. Development of 07MnNiMoDR steel plate used high parameter spherical tank[J]. Hot Working Technology, 2014, 43(16): 27-30.
[11]Morito S, Yoshida H, Maki T, et al. Effect of block size on the strength of lath martensite in low carbon steels[J]. Materials Science and Engineering A, 2005, 438: 237-240.
[12]李杰, 赵国昌, 张海军, 等. 薄规格调质型07MnNiMoDR钢板的热处理方法: CN111041163A[P]. 2020-04-2.
Li Jie, Zhao Guochang, Zhang Haijun, et al. Heat treatment method of thin gauge quenched and tempered 07MnNiMoDR steel plate: CN111041163A[P]. 2020-04-2.
[13]Shi K, Hou H, Chen J B, et al. Effect of bainitic packet size distribution on impact toughness and its scattering in the ductile-brittle transition temperature region of Q&T Mn-Ni-Mo bainitic steels[J]. Steel Research International, 2016, 87(2): 165-172.
[14]Li Wang, Yong Liu, Wei Zhang, et al. Numerical simulation for processing windows of TiAl alloys during hot forging[J]. American Scientific Publishers, 2012, 9(9): 1485-1490.
[15]陈益哲. GH2907合金热加工工艺窗口的表征与验证[D]. 西安: 西安建筑科技大学, 2019.
Chen Yizhe. Characterization and verification of the hot working processing windows of GH2907 superalloy[D]. Xi'an: Xi'an University of Architecture and Technology, 2009.
[16]高彩茹, 霍喜伟, 宋玉卿, 等. 500 MPa级门架型钢的奥氏体晶粒长大行为[J]. 金属热处理, 2020, 45(1): 139-142.
Gao Cairu, Huo Xiwei, Song Yuqing, et al. Austenite grain growth behavior of 500 MPa grade gantry steel[J]. Heat Treatment of Metals, 2020, 45(1): 139-142.
[17]崔忠圻, 谭耀春. 金属学与热处理[M]. 北京: 机械工业出版社, 2007.
Cui Zhongqi, Tan Yaochun. Metallography and Heat Treatment[M]. Beijing: China Machine Press, 2007.
[18]曹辉. 07MnNiMoVDR压力容器用钢生产工艺与组织性能[D]. 沈阳: 东北大学, 2012.
Cao Hui. Manfacturing process, microstructures and mechanical properties of pressure vessel steel 07MnNiMoVDR[D]. Shenyang: Northeastern University, 2012.
[19]杨浩, 杨汉, 曲锦波. 热处理工艺对690 MPa级低屈强比高强钢组织性能的影响[J]. 材料热处理学报, 2013, 34(5): 137-142.
Yang Hao, Yang Hao, Qu Jinbo. Effect of heat treatment on microstructure and mechanical properties of a 690 MPa grade high strength steel with low yield ratio[J]. Transactions of Materials and Heat Treatment, 2013, 34(5): 137-142.
[20]王冬雪, 蔡庆伍. 回火温度对不同冷速淬火Q690钢组织及力学性能的影响[J]. 金属热处理, 2014, 39(4): 72-75.
Wang Dongxue, Cai Qingwu. Effect of temperature on microstructure and mechanical properties of Q690 steel quenched under different cooling rates[J]. Heat Treatment of Metals, 2014, 39(4): 72-75.