Influence of second tempering on fatigue cycle number of mining link made of 23MnNiCrMo54 steel

doi:10.13251/j.issn.0254-6051.2023.04.022

Abstract

Abstract: Due to technical transformation of the equipment, the quenching medium of the the 23MnNiCrMo54 steel mining link was replaced, and the fatigue life of the mining link after quenching and tempering according to the original process could not meet the technical requirements of the drawing standards. Through adding a second second tempering after the first, it is found that the fatigue cycle number of the mining link significantly increases and reaches the technical requirements of the drawing standard. The phenomenon that second tempering improves the fatigue life of the mining link parts is verified and confirmed, and no abnormality is found in observation of microstructure and inclusions of the mining link under different tempering conditions. When using the scanning electron microscope to observe and analyze the carbide distribution, alloy element distribution and carbide morphology of the tempered specimen, the results show that the carbides after the the first tempering at 420 ℃ and double tempering at 380 ℃+420 ℃ have different morphologies and structures. The carbide boundary after the first tempering is clear, and the number of carbides is small. The carbide boundary after the second tempering is fuzzy, and the amount of carbides is large. The carbide morphology under the second tempering state corresponds to a higher fatigue life.

Key words: mining link, 23MnNiCrMo54 steel, tempering, carbide, fatigue cycle number

CLC Number:

TG156

Liu Jinde, Lu Junling, Wang Liang, Ma Tao, Ma Chunliang, Sun Yongpeng. Influence of second tempering on fatigue cycle number of mining link made of 23MnNiCrMo54 steel[J]. Heat Treatment of Metals, 2023, 48(4): 137-142.

References

[1]王维喜, 马瑞勇, 武兴旺, 等. 矿用高强度圆环链及其热处理的研究进展[J]. 金属热处理, 2009, 34(8): 102-105.
Wang Weixi, Ma Ruiyong, Wu Xingwang, et al. Research progress of high-tensile round link chains for mining and its heat treatment[J]. Heat Treatment of Metals, 2009, 34(8): 102-105.
[2]封秀敏, 23MnNiMoCr54圆环链用钢组织及性能研究[D]. 天津:河北工业大学, 2004.
[3]闫俊萍, 刘宗昌, 李强, 等. 23MnNiCrMo煤机链条钢TTT曲线的研究[J]. 金属热处理, 2001, 26(6): 33-34.
Yan Junping, Liu Zongchang, Li Qiang, et al. Study on TTT diagram of 23MnNiCrMo block chain steel in coal mine machine[J]. Heat Treatment of Metals, 2001, 26(6): 33-34.
[4]杜显玲. 高级链条钢23MnNiMoCr54热处理工艺研究[J]. 中国科技纵横, 2015(8): 93.
Du Xianling. Study on heat treatment process of high grade chain steel 23MnNiMoCr54[J]. China Science and Technology Overview, 2015(8): 93.
[5]齐海东, 王晶, 陈中军, 等. 温度对马氏体和铁素体晶格常数影响规律[J]. 物理学报, 2022, 71(9): 366-373.
Qi Haidong, Wang Jing, Chen Zhongjun, et al. Influence of temperature on lattice constants of martensite and ferrite[J]. Acta Physica Sinica, 2022, 71(9): 366-373.
[6]冯宝萍, 仇亚军, 王传恩, 等. 碳化物对GCr15轴承钢接触疲劳寿命的影响[J]. 轴承, 2003(10): 30-32.
Feng Baoping, Qiu Yajun, Wang Chuanen, et al. Effect of carbide on contact fatigue life of GCr15 bearing steel [J]. Bearing, 2003(10): 30-32.
[7]董绍明, 胡建文, 梁子玉. 锯片基材75Cr1钢的热处理工艺及其组织性能[J]. 金属热处理, 2021, 46(9): 193-198.
Dong Shaoming, Hu Jianwen, Liang Ziyu. Heat treatment process of 75Cr1 steel for saw blade substrate and its microstructure and mechanical properties[J]. Heat Treatment of Metals, 2021, 46(9): 193-198.

[1]	Wang Bohui, Xu Taixu, Lu Ming, He Zhijun. Carbide evolution of GCr15SiMo bearing steel during spheroidizing annealing process [J]. Heat Treatment of Metals, 2023, 48(4): 60-66.
[2]	Zou Hang, Liu Man, Tian Junyu, Xu Guang. Microstructure and properties of ultra-high strength low carbon bainitic steel under rapid tempering process condition [J]. Heat Treatment of Metals, 2023, 48(4): 67-73.
[3]	Xie Gangsheng, Xing Shuqing, Shen Lijuan, Ma Yonglin, Liu Yongzhen, Chen Zhongyi. Effect of pulsed magnetic field on precipitation of carbides during spheroidizing annealing of GCr15 steel [J]. Heat Treatment of Metals, 2023, 48(4): 118-122.
[4]	Wang Zhaofeng, Cheng Xiaoying, Li Xiaoliang, Peng Hao, Cai Zhenxiang. Effect of tempering temperature on hydrogen embrittlement sensitivity of a high strength low alloy steel containing V and Nb [J]. Heat Treatment of Metals, 2023, 48(3): 12-18.
[5]	Wang Kaikai, Ma Longteng, Luo Ping, Liu Meiyan, Lu Shiping, Di Guobiao, Wang Yanfeng, Ma Changwen. Effect of tempering temperature on microstructure and properties of bainitic wear-resistant steel [J]. Heat Treatment of Metals, 2023, 48(3): 84-90.
[6]	Zhao Jinzhu, Xie Zhifeng, Wei Hong. A heat treatment process for improving carbide morphology of wear resistant high manganese steel [J]. Heat Treatment of Metals, 2023, 48(3): 139-142.
[7]	Chang Yaodong, Qi Huiping, Jia Yanlong, Li Yongtang, Wu Yonghong. Heat treatment process and microstructure and properties of Q345/40Cr bimetal ring [J]. Heat Treatment of Metals, 2023, 48(3): 195-202.
[8]	Cui Yi, Zhang Caidong, Yu Feng, Zhang Yunfei, Zhang Zhiwang, Cao Wenquan, Zhao Yingli, Cui Shaopu. Influence of large carbides on rotating bending fatigue of GCr4Mo4V steel [J]. Heat Treatment of Metals, 2023, 48(2): 50-55.
[9]	Yang Liu, Xie Yixin, Ju Yulin, Wei Qi, Cao Fuyang, Luo Rui, Yuan Zhizhong, Cheng Xiaonong. Effect of austempering on high temperature frictional wear property of Dievar hot working die steel [J]. Heat Treatment of Metals, 2023, 48(2): 85-93.
[10]	Yang Denggui, Zhu Xiaoshuo, Fu Yudong, Alinuer·Maimaiti. Intensive quenching and tempering of 40Cr steel [J]. Heat Treatment of Metals, 2023, 48(2): 117-123.
[11]	Hao Xiaoge, Zhao Leijie, Wang Yanhui, Ma Penghui, Zhang Zi, Yue Yun, Xiong Peng. Microstructure and properties of bainitic alloy steels with different carbon contents after austempering [J]. Heat Treatment of Metals, 2023, 48(1): 46-51.
[12]	Zhao Shuai, Li Qingchun, An Haoying, Chen Shuying, Chang Guowei. Formation of reversed austenite and its effect on properties of Cr13Ni4Mo steel [J]. Heat Treatment of Metals, 2023, 48(1): 95-99.
[13]	Yuan Yasha, Wang Yuchang, Wang Wenyan, Shi Ruxing, Yuan Sha, Zhang Yudong. Effect of tempering temperature on microstructure and mechanical properties of 55NiCrMoV7 hot working die steel [J]. Heat Treatment of Metals, 2023, 48(1): 133-138.
[14]	Li Hongjuan, Xiang Chenggong, Wu Qiong, Wang Zhengcai. Effect of quenching and tempering process on microstructure and austenite grain growth of 42CrMo steel [J]. Heat Treatment of Metals, 2023, 48(1): 181-185.
[15]	Sun Yongzhen, Cheng Juqiang, Zhao Xiaohan. Effect of tempering temperature on microstructure and properties of 40CrMoVNbTi steel [J]. Heat Treatment of Metals, 2023, 48(1): 193-197.