Effect of heating temperature on depth of decarburization layer of 45 steel in air atmosphere

doi:10.13251/j.issn.0254-6051.2024.04.035

Abstract

Abstract: Effect of different heating temperatures (700-1300 ℃ for 1 h, heating up along with the furnace and air cooling) under air atmosphere on decarburization depth of 45 steel surface was studied, and the mechanism of decarburization was analyzed. The results show that as the temperature increases, the depth of the decarburization layer on 45 steel surface is increased. When heated at 700 ℃, no decarburization occurs on the 45 steel surface. When heated at 750~800 ℃, it is mainly dominated by completely decarburized structure. When heated in the range of 850~900 ℃, there is a coexistence of completely decarburized structure and partially decarburized structure. When heated at 950 ℃ and above, it is primarily composed of partially decarburized structure.

Key words: complete decarbonization, partial decarburization, temperature

CLC Number:

TG156.6

Xu Cheng, Yang Yu, Wang Runqi, Tong Xinru, Ren Junwei. Effect of heating temperature on depth of decarburization layer of 45 steel in air atmosphere[J]. Heat Treatment of Metals, 2024, 49(4): 219-222.

References

[1]熊涛, 赵刚, 徐耀文, 等. 弹簧钢50CrV4加热气氛对表面脱碳的影响[J]. 热加工工艺, 2017, 47(4): 54-58.
Xiong Tao, Zhao Gang, Xu Yaowen, et al. Effect of heating atmosphere on surface decarburization of 50CrV4 spring steel[J]. Hot Working Technology, 2017, 47(4): 54-58.
[2]于学森, 沈奎, 江卓俊, 等. 弹簧钢60Si2MnA表面脱碳规律研究[J]. 热加工工艺, 2017, 46(24): 224-231.
Yu Xuesen, Shen Kui, Jiang Zhuojun, et al. Study on surface decarburization law of spring steel 60Si2MnA[J]. Hot Working Technology, 2017, 46(24): 224-231.
[3]王慧军, 涛雅, 陈林, 等. U76CrRE钢轨热处理过程组织控制及性能[J]. 金属热处理, 2022, 47(5): 161-165.
Wang Huijun, Tao Ya, Chen Lin, et al. Microstructure control and properties of U76CrRE steel rail during heat treatment[J]. Heat Treatment of Metals, 2022, 47(5): 161-165.
[4]胡磊, 王雷, 麻晗. 高碳钢盘条的表面氧化与脱碳行为[J]. 钢铁研究学报, 2016, 28(3): 67-73.
Hu Lei, Wang Lei, Ma Han. Behaviors of oxidation and decarburization on surfaces of high carbon steel wire rods[J]. Journal of Iron and Steel Research, 2016, 28(3): 67-73.
[5]催忠圻, 覃耀春. 金属学与热处理[M]. 北京: 机械工业出版社, 2016.
[6]赵宪明, 张坤, 杨洋. 42CrMo钢表面脱碳行为研究[J]. 钢铁研究学报, 2019, 31(2): 196-201.
Zhao Xianming, Zhang Kun, Yang Yang. Investigation of surface decarburization behavior in 42CrMo steel[J]. Journal of Iron and Steel Research, 2019, 31(2): 196-201.
[7]赵小龙, 王雍期, 唐兴昌, 等. 钢坯在加热过程中的氧化机理及其研究综述[J]. 轧钢, 2019, 36(6): 66-68.
Zhao Xiaolong, Wang Yongqi, Tang Xingchang, et al. Review on the oxidation mechanism and its research of steel billet in heating process[J]. Steel Rolling, 2019, 36(6): 66-68.

[1]	Guo He, Cui Gongjun, Han Wenpeng, Liu Yanping, Kou Ziming. Preparation and high-temperature tribological properties of self-lubricating CoCrW matrix composites reinforced by SrSO₄ [J]. Heat Treatment of Metals, 2024, 49(4): 18-25.
[2]	Guo Dayong, Gao Hang, Pan Yang, Yang Yingqiang, Wang Bingxi, Gong Wenhe. Effect of high temperature deformation on pearlite colony size in high carbon steel wire rods for fine wires [J]. Heat Treatment of Metals, 2024, 49(4): 146-149.
[3]	Jia Xiaobin, Qin Ruiting, Tu Mingjin, Li Yuanyuan, Hu Yongping, Zhou Zhongcheng. Grain size control of extruded 316H austenitic stainless steel large-diameter pipes [J]. Heat Treatment of Metals, 2024, 49(4): 168-174.
[4]	Ma Zhifeng, Wang Hailong, Zhao Weiyi, Fu Yilei, Lu Zheng. Effects of quenching water temperature and cryogenic treatment on microstructure and mechanical properties of ultra-high strength Al-Zn-Mg-Cu alloy [J]. Heat Treatment of Metals, 2024, 49(4): 195-200.
[5]	Xu Kaitai, Liu Qisheng, You Kaisi, Liu Zhaoyu, Zhang Junjia. Effect of low temperature cold rolling and aging on microstructure and properties of Cu-Ni-Co-Si alloy [J]. Heat Treatment of Metals, 2024, 49(3): 1-6.
[6]	Li Xiaoliang, Cheng Xiaoying, Wang Zhaofeng, Ren Yuwen, Zeng Fanyu. Effect of tempering temperature on hydrogen embrittlement sensitivity of a low-alloy high-strength steel with Nb and V [J]. Heat Treatment of Metals, 2024, 49(3): 7-14.
[7]	Zhao Xinlei, Yuan Xiaofei, Qiao Junwei. Effect of solution temperature on microstructure and mechanical properties of K424 alloy [J]. Heat Treatment of Metals, 2024, 49(3): 15-21.
[8]	Zhang Yu, Yu Jinrui, Yu Xinhong, Feng Yisheng, Zhang Yunshan, Zhao Ertuan. Effect of austempering temperature on microstructure and properties of 50CrVA steel [J]. Heat Treatment of Metals, 2024, 49(3): 28-32.
[9]	Wei Hui, Lin Yuan, Wang Hongxia, Wang Shijia, Li Xu, Zhang Wenkang, Wang Yide. Effect mechanism of intermediate annealing temperature on microstructure and texture of 3.5%Si non-oriented silicon steel during secondary cold rolling [J]. Heat Treatment of Metals, 2024, 49(3): 37-43.
[10]	You Wenhao, Chen Xia, Chen Bin. Effect of normalizing process on microstructure and magnetic properties of grain-oriented silicon steel [J]. Heat Treatment of Metals, 2024, 49(3): 50-55.
[11]	Liu Zaiwang, Guo Min, Teng Huaxiang, Yang Libin, Liang Xuan, Liu Guanghui, Liu Shunming. Influence of annealing temperature on formability and recrystallization texture of an extra-deep drawing steel for enameling [J]. Heat Treatment of Metals, 2024, 49(3): 91-97.
[12]	Wang Jiaojiao, Zhao Linlin, Gao Yunzhe, Shi Shuai, Wu Xiaolong, Zhao Yanqing, Zhou Yuqing, Gong Junjie. Effect of tempering temperature on microstructure and properties of an oil casing steel used for deep wells [J]. Heat Treatment of Metals, 2024, 49(3): 112-115.
[13]	Liu Pengfei, Guan Lin, Liu Jian, Chen Yu, Liu Hongliang. Effect of annealing process on structure and properties of a low cost 980 MPa cold-rolled dual-phase steel [J]. Heat Treatment of Metals, 2024, 49(3): 122-127.
[14]	Jiang Chang, Lu Hengchang, Wei Xicheng, Dong Han. Microstructure and fatigue properties of SCM435 steel for engines [J]. Heat Treatment of Metals, 2024, 49(3): 159-163.
[15]	Dong Jiaxin, Luo Yun, Jiang Wenchun, Gu Wenbin, Dong Pijian. Control and parameter optimization in electromagnetic induction heating temperature uniformity of large thick-walled cylinder [J]. Heat Treatment of Metals, 2024, 49(3): 275-278.