Thermodynamic equilibrium phases of TP347H steel with different contents of Cr and Ni

doi:10.13251/j.issn.0254-6051.2016.10.022

HTM

Previous Articles Next Articles

Thermodynamic equilibrium phases of TP347H steel with different contents of Cr and Ni

1. Electric Power Research Institute of Guangdong Power Grid Co., Ltd. 2. School of Power and Engineering, Wuhan University

Online:2016-10-25 Published:2016-11-09

Abstract

CLC Number:

TG113.1

Wang Wei1, Wang Zhiwu2, Li Wensheng1, Tian Jing2, Zhong Wanli1, Song Tao2, Lin Jiedong1. Thermodynamic equilibrium phases of TP347H steel with different contents of Cr and Ni[J]. HTM, doi: 10.13251/j.issn.0254-6051.2016.10.022.

[1]	Zhao Ping. Cause analysis for cracking of high temperature superheater tubes in supercritical circulating fluidized bed boiler [J]. Heat Treatment of Metals, 2021, 46(6): 225-230.
[2]	Ren Yuebin1, Wang Wei2, Ping Shaobo3. Failure analysis of T23/TP347H dissimilar steel welded tube joint for high temperature reheater [J]. HTM, 2016, 41(3): 199-203.
[3]	Li Zhenliang, Wang Jia’an, Xiao Minyan. Failure analysis of SA-213TP347H steel reheater tube [J]. HTM, 2015, 40(8): 191-194.
[4]	Song Tao, Wang Zhiwu. Analysis on thermodynamic equilibrium phases of T91 steel with different contents of V and Nb [J]. HTM, 2014, 39(11): 59-63.

Thermodynamic equilibrium phases of TP347H steel with different contents of Cr and Ni

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 4

Recommended Articles

Metrics

Comments